Effects of Cr and Ni addition on damping capacity, mechanical property, and corrosion resistance of Fe-17%Mn martensitic alloy have been studied. Martensite start temperature($M_{S}$) of the alloy decreases linearly with increasing Cr and Ni contents up to 15%. The damping capacity decreases gradually from 27 to 22% in specific damping capacity(SDC) with increasing Cr and Ni contents from zero to 10%, and decreases rapidly with further Cr and Ni content in Fe-17%Mn alloy. The tensile strength of the alloy maintains a level of 60 $kgf/mm^{2}$ regardless of Cr content with an elongation of 20 to 25%. But, in case of Fe-17%Mn-x%Ni alloy, the tensile strength decreased rapidly with the Ni content of above 10% because of austenite morphology. Immersion test in 5% NaCl solution leads to the result that the corrosion resistance of the alloy becomes excellent above 10% Cr. From the above results, it is concluded that the optimum Cr content to improve the mechanical property and corrosion resistance of the alloy in 5%NaCl solution with a lesser decrease in damping capacity is about 10%. In the case of 5% $H_{2}SO_{4}$ condition, the Fe-17%Mn-10%Ni is an optimum alloy.

The microstructure and mechanical property of the Ni and Ni-Cr porous metal reinforced AC4C matrix composites fabricated by squeeze casting were investigated. In this study Ni, Ni-Cr porous metals which are estimated to be easy to fabricate by squeeze casting are used as strengtheners for composite materials. As a matrix material, Al-7wt.%Si-0.3wt.%Mg(AC4C) has been used. In case of Ni/AC4C and Ni-Cr/AC4C composite, $750^{\circ}C$ melt temperature and minimum 25MPa squeezing pressure are needed to produce sound composite materials. The observation of interfacial reaction zone at various heat treatment condition shows that atsolutionizing temperature of above $520^{\circ}C$, the interfacial reaction zone increases proportionally with heat treatment time and the reaction products formed by interfacial reactions are mainly composed by $Al_{3}Ni$ and $Al_{3}Ni_{2}$ phases.

The microstructure and mechanical property of the ceramic reinforced AC4C matrix composites processed by squeeze casting were investigated. In this study Kaowool and Saffil fiber which are ceramic reinforcements are used as preform materials. As a matrix material, Al-7wt.%Si-0.3wt.%Mg(AC4C) has been used. In case of Kaowool and Saffil/AC4C composites, 7.5 MPa squeezing pressure and minimum 7.0% binder amount are needed to produce sound composite materials. The tensile strength of Kaowool/ AC4C composite is lower than the matrix metal and this can be explained by the melt unfilling due to formed cluster of Kaowool reinforcements. But the mechanical properties of hardness, wear resistance and thermal expansion are better than the matrix materials due to the strengthening effect of ceramic reinforcements.

This study has been carried out to investigate the microstructure of austempered high carbon cast steel with the variation of silicon and heat treatment conditions. The results show that an lower ausferritic structure is formed at the low austemepring temperature ($250{\sim}300^{\circ}C$) and an upper ausferritic structure is formed at the high austemepring temperature ($350{\sim}400^{\circ}C$). As an austempering temperature increased, the retained austenite volume fraction increased, however hardness decreased. Also, as a silicon content increased, the precipitation of cementite was suppressed, therefore 2nd reaction of autempering transformation was delayed.

The ability and fading behavior of inoculant in ductile cast iron melt and the effect of minor element on them were investigated. The result obtanied on nodularization and the performance of inoculant were more distinct when the melt was treated and held at the high temperature range of $1450{\sim}1500^{\circ}C$ than at the lower one of $1350{\sim}1400^{\circ}C$. The performance of 5.2%Mg-Fe-Si alloy was the best of 4 nodularizers. That of Fe-75%Si(I) alloy was better than other 4 inoculants. The performance of the Fe-75%Si(I) inoculant was deteoriated by the addition of sulfur or bismuth. On the other hand, that was improved by the addition of cerium, even though its extent was not big.