The effects of solid solution treatment and aging in the properties of Cu-0.32wt%Be-1.35wt%Co alloy was gravity die casted and forged were investigated in order to examine the optimum heat treatment conditions for production of high conductivity mold material. The optimum properties for mold material were obtained under the conditions which were solid solution treated at $930^{\circ}C$ for 1 hour and aged at $430^{\circ}C$ for 2hours.

TiC particulate reinforced magnesium matrix composites were fabricated by melt stirring method. The effect of alloying elements on TiC particulate dispersion into molten magnesium and mechanical properties were investigated. The incorporation time is defined as the time required for dispersion of solid particles into molten metal. The incorporation time of TiC particles into molten pure magnesium was remarkably shorter and the particulated dispersion was more uniform than that of pure aluminum which was reported previously. The incorporation time was, prolonged by the addition of Al, Bi, Ca, Ce, Pb, Sn or Zn. The tensile strength increased and elongation decreased by the addition of Cu or Sn into the matrices and composites. Although, the tensile strength of the matrices and composites increased by alloying with Ca or Ce, the maximum elongation was observed at a content of about 1% for the matrices. By alloying with Zn, the tensile strength increased for the matrices and composites, but the elongation of the matrices increased. The pure magnesium and its alloy matrix composites reinforced with 20vol% TiC have the tensile strength of about 400MPa. This value is compared with the tensile strength of SiC whisker reinforced magnesium matrix composites fabricated by liquid infiltration method at the same volume fraction. There fore, the melt strirring method which has the advantages of simple process is considered to be efficient in fabricating magnesium matrix composites.

Research in heat transfer and solidification commonly involves experimentation and mathematical modeling with associated numerical analysis and computation. Inverse problems in heat transfer are part of this paradigm. During the solidification of metal casting, an interfacial heat transfer resistance exists at the boundary between the casting and the mold, and this heat transfer resistance usually varies with time. In the case of the squeeze casting the contact heat transfer resistance is decreased by pressure and ideal contact is almost accomplished. In the present work, heat transfer coefficient, which is inverse value of the heat transfer resistance, was used for convenience. A numerical technique, Non-Linear Estimation has been adopted for calculation of the casting/mold interfacial heat transfer coefficient during the squeeze casting process. In this method, the measured temperature data from experiment were used. The computational results were applied to the analysis of heat transfer and solidification.

AC4A $Al/Al_2O_3+SiC_p$ hybrid composites were fabricated by the squeeze infiltration technique. Effect of applied pressure, volume fraction of reinforcement($Al_2O_3$ and SiC) and SiC particle size($4.5{\mu}m$, $6.5{\mu}m$ and $9.3{\mu}m$) on the solidification microstructure of the hybrid composites were examined. Mechanical properties were estimated preliminarly by fractographic observation, hardness measurement and wear test. Results show that the microstructure of the hybrid composites were quite satisfactory, namely revealing relatively uniform distribution of reinforcements and refined matrix. Some aggregation of SiC particle caused by particle pushing was observed especially in the hybrid composites containg in fine particle($4.5{\mu}m$). Refined matrix was attributed to applied pressure and increased nucleation sites with addition of reinforcements. Fractured facet also revealed finer for the hybrid composites possibly due to refined matrix. Hardness and wear resistance increased with volume fraction of reinforcements. For hybrid composites with $9.3{\mu}m$ SiC, hardness was somewhat lower and wear resistance higher than other composites.

The structure of austempered ductile cast iron, called ADI, consists of graphite, retained austenite, and bainite. The bainite component of them is considered a useful structure for exriting materials for roll of rolling mill. Therefore, the ADI can be considered applicable to material for rolling contact element. The diverse tests, such as rolling contact friction test, impact test, and X-ray reflection test, were carried out to investigate the possibility of it`s application. The result of this study showed that the expected fact was confirmed. The specimen showed that the best performance had the structure of the low bainite containing the stable retained austenite of about 20%.

SiC fibers were coated with Cu, Ag and Ni metallic thin films by magnetron sputtering in order to improve wetting properties between Al matrix and SiC fiber. The wetting behavior of metal coated SiC fiber by pure Al has been studied at $670^{\circ}C{\sim}900^{\circ}C$ range for $10{\sim}90min$. under vacuum atmosphere. Besides, the effect of coated film thickness on the wettability has been investigated. The wetting behavior and interfacial reaction between Al and SiC fibers were analysed with optical microscope and SEM (scanning electron microscope). The wetting behavior of the as-received SiC fiber with Al melt was not uniform, indicated by the contact angles from less than $90^{\circ} to more Al melt was appeared in the initial stage of reation. It was considered that the metallic thin film played an important role in reducing the interfacial free energy and breaking down the aluminum oxide film by eutectic reaction with Al melt. However the wettability of Ni coated SiC fiber was not improved as much as that of Cu or Ag coated SiC fiber. The improvement of wettability by coating thickness is clearly showed in $1{\mu}m$ coated SiC fiber compared with $0.25{\mu}m$ coated SiC.