This study aims to investigate the effects of the microstructures and nodule type on the fatigue characteristics of cast iron. Fatigue tests were carried out in tension-tension mode using a servo-hydraulic testing machine with load control mode operating at a frequency of 15 Hz. The tests were conducted at stress ratio R=Kmin/Kmax, of 0.1. Initial crack ${\Dalta}K$ values were highly performed with increase in tensile strength of DCI fatigue specimens. ${\Dalta}K_{th}$ region, fatigue crack propagation was primarily advanced through cell boundary and in periphery of near nodule. Fatigue crack propagation rate of D2 consisted with 2Phase(Ferrite+Pearlite) was slow due to crack closure enhanced by crack deflection and occurred crack branching. The generation of crack branch was occurred due to interaction of crack-nodule. At Threshold and Paris zone, the fractographs of the fatigue fracture surface for DCI show typical striations of a ductile fracture and isolated cleavage planes near graphite. The effect of microstructure on fatigue crack propagation of GC strongly depends on the type of flake. The generation of crack branch occurred due to interaction of crack-nodule. The fractographs of the fatigue fracture surface for GC show cleavage plane along the flake graphite.

Mechanical characteristics of Hi-Cr cast irons containing 16.8%Cr and 3.0%C were studied with various heat treatments. After as-cast Y-block ingots were annealed fully, the ingots were machined into cylinderical specimens with the size of 9mm in diameter and 20mm in length in order to investigate the effect of heat-treatments on mechanical characteristics of high Cr cast irons. All specimens were heat-treated by quenching- tempering, austempering and cyclic heat at the various temperatures(950, 1000, 1050 and $1100^{\circ}C$) respectively. The wear amount was measured for each heat-treated specimens against the counterpart of a hardened SKD11 steel at the following conditions; wearing velocity: 0.7 m/s, load: 100N and sliding distance: 70 km. After as-cast specimens were annealed, fine $M_{3}C$ carbides were formed, which affected the hardness and the wear resistance of Hi-Cr specimens. High hardness and good wear resistance were appeared on the specimens treated at 950 and $1000^{\circ}C$ and the austempered specimens show excellent wear resistance as well as high hardness.

The structures and mechanical property of the unidirectionally solidified Al-Co eutectic alloy were investigated. Al-Co eutectic alloy was unidirectionally solidified with growth rates(R) between I cm/hr and 10 cm/hr in the induction furnace maintaining the thermal gradient (G) at solid-liquid interface, $32^{\circ}C$/cm. The eutectic microstructure was varied with the growth condition(G/R ratio). When the G/R ratio was larger than $8.5{\times}10^{3}^{\circ}C/cm^{2}/sec$, a lamellar structure was formed, But the G/R ratio was smaller than $8.5{\times}10^{3}^{\circ}C/cm^{2}/sec$, a colony structure was formed. It was found that the interlamellar spacing(${\lambda}$) was dependent on the growth rate(R) with the relationship, ${\lambda}^{2}{\cdot}R=constant$. The microhardness of this eutectic alloy increased with increase in the growth rate.

The thermodynamic analysis of deoxidation in molten coppyr by Fe has been made. Equilibrium oxygen solubility saturated with FeO in Cu-Fe-O system has been derived without and with consideration of the solute interaction between Fe and O. The derived relationship of oxygen contents with Fe has been compared with the experimental results done by Kulkarni and the minimum oxygen solubility could be predicted by a simple first order interaction method, Wagner model.

A series of heavy section ductile cast iron ingots with the cube length of 250mm were systematically investigated as functions of casting parameters of sand casting. Abnormal graphite formation was specially observed with the variation of Si content and Bi or Sb addition. Effects of chilling during casting and adaptation of riserless system were also examined, and proved to be effective for the prevention of both shrinkage and abnormal graphite such as chunky one. The formation of chunky graphite was effectively prevented by low Si content despite the promotion of pearlite matrix structure. The ferritic matrix was encouraged to form by high Si content and chunky graphite formation was effectively suppressed by the addition of Bi and Sb. Bi addition, however, was not good enough to control the microstructure owing to the sensitive cooling rate dependent inoculation behavior and relative low ability of nodulization. Sb addition, on the other hand, was proved to be effective for the microstructural control and enhancement of various mechanical properties such as strength, elongation, and impact energy. It may be suggested that optimized casting parameters should be applied to produce heavy section ductile cast iron with reliability.