Nb-containing austenitic stainless steel is widely used as exhaust frame and diffuser assembly in power plant. However, this steel is known to be difficult to produce by the continuous casting process due to the surface cracks. Therefore, the continuous casting technology was developed for the prevention of the surface cracks on CC slabs. Precipitates and the analysis of heat trasfer in a slab were investigated in order to find out the formation mechanism of surface cracks on cc slabs It was found that surface cracks are occurred due to the NbC precipitates, which are formed along the grain boundaries around $800^{\circ}C$. The secondary cooling pattern has been developed to produce the defect free CC slabs of Nb-containing austenitic stainless steel.

The glass formation behavior was investigated in the melt spun Zr-Ti-Cu-Ni-X (X=B, P and Si) ribbons. The magnitude of supercooled liquid region of Zr-Ti-Cu-Ni alloy increased with an addition of alloying element. The glass transition temperature and the crystallization temperature increased and the magnitude of supercooled liquid region decreased with increasing the content of alloying elements. The largest supercooled liquid region was observed in the Si containing alloy. This is believed to be due to the dense atom packing with the optimum atomic size ratio of constituent elements.

We fabricated test samples containing various shape elements and surface roughness checking points for the jewelry cast master patterns by employing the 3D computer aided design (CAD), selective laser sintering (SLS) rapid prototype (RP) with the DuraForm powders. We varied the alignment angle from $0^{\circ}$ to $10^{\circ}$ at a given layer thickness of 0.08 and 0.1mm, respectively, in RP operation. Dimensions of the shape elements as well as values of surface roughness are characterized by an optical microscope and a contact-scanning profilometer. Surface roughness values of the top and vertical face increased as the alignment angle increased, while the other roughness values and shape elements variation were not depending on the alignment angle. The resolution of the shape realization was enhanced as the layer thickness became smaller. The minimum diameter of the hole, common in jewelry design, was 1.2 mm, and the shrinkage became 12% at the 1.6 mm-diameter hole, Our results implied that we face down the proposed design elements with $0^{\circ}$ alignment angle, and consider the shrinkage effect of each shape element in DuraForm RP jewelry modeling.

The effects of the revolution speed on the mechanical properties and microstructure of Cr-Mo steel during vertical centrifugal casting using investment mold were investigated. The casting yield, tensile strength, hardness and absorbed energy during impact test were increased with increasing revolution speed. The effect of mass variation caused by the change in the revolution speed on the grain size was the most significant.