CV graphite cast iron has been studied and generally known to have properties close to the average values of those between flake and spheroidal graphite cast iron. However, the thermal diffusivity of CV graphite cast iron is much larger than that of the average value of those between flake and spheroidal graphite cast iron. In this study, an easy production method of CV graphite cast iron with small additions of a Al-Cu which is known as the element of the graphitization was investigated. The effects of hold time and of Al-Cu additions after the treatments with spheroidizer (Fe-Si-Mg alloy) were also investigated. Increasing the additions of a Al-Cu alloy, the holding time to form a CV graphite cast iron was decreasing. Tensile strength and thermal diffusivity (flash method) were measured in order to find the changes of the mechanical properties and the physical properties. Spheroidal, CV, and flake graphite cast iron have tensile strengths 46.44, 38.29, and $27.29\;kg/mm^2$ and thermal diffusivities $3.95{\times}10^{-6,}$ $8.41{\times}10^{-6}$, $8.81{\times}10^{-6}m^2/sec$, respectively at room temperature.

The effect of chromium, aluminium and copper contents on the structures and mechanical properties of cast iron was investigated. 1) Mechanical properties were improved with the formation of ledeburite by chromium addition. The primary carbides dispersed in martensitic matrix contributed to high strength and wear resistance. 2) Small addition of aluminium decreased hardness of the cast iron. 3) The impact values were decreased by the formation of the double carbides but improved by the heat treatment. 4) Small addition of copper up to a certain level increased the hardness. Also impact values were considerably increased.

In this study, the variations of tensile strength and yield strength of Al-20% Si alloy were studied. Copper, magnesium and nickel as alloying elements added from 1% to 3% respectively. The temperature range was from room temperature to $350^{\circ}C$. The refinement of primary silicon crystal was treated with phosphorous addition. The results obtained are as follows: 1. Tensile strnegth and yield strength showed more increased strength in refining treated alloy than that of in nonrefining alloy at elevated temperature. 2. Tensile strength and yield strength were increased with the contents of copper. Tensile strength showed the maximum at $150^{\circ}C$, but yield strength was decreased with increasing temperature. 3. The effect of magnesium addition on tensile strength and yield strength showed the maximum at 1% addition and $150^{\circ}C$. 4. Tensile strength and yield strength showed a slight increase with the content changes of nickel and they were decreased with increasing temperature.