In commercial Zr-Nb-Cu-Ni-Al amorphous alloys, expensive element, Zr, was substituted to Sn which was cheaper one, and then, glass forming ability, compressive strength and hardness of them were estimated. Even though the Sn was added up to 1.5%, resulting phase was not changed to the crystalline form. It was confirmed by X-ray diffraction and thermal analyses. In the X-ray profiles, there were no peaks for crystalline phases and typical halo pattern for amorphous phase was appeared at the diffraction angle of $35^{\circ}{\sim}45^{\circ}$. Thermal analyses also showed that the Sn modified alloys were corresponded to the amorphous standards where ${\delta}T$(= Tx - Tg) and Trg(= Tg/Tm) affecting to the amorphous forming ability were more than 50K and 0.60 respectively. Compressive strengths were 1.77 GPa, 1.63 GPa, 1.65 GPa and 1.77 GPa for 0%Sn, 0.5%Sn, 1.0%Sn and 1.5%Sn respectively. Hardnesses of the Sn modified alloys were decreased from 752 Hv to 702 Hv in 1.0%Sn and recovered to 746 Hv in 1.5%Sn.

In this study, the extruded Al-6.3Zn-2.4Mg alloys were selected among the 7000 series aluminum alloys sensitive to hydrogen environment in order to examine the effects of both the aging conditions and the length of hydrogen charging period on the mechanical properties of the alloy. The specimens were aged for 24hours at $100^{\circ}C$ (under aging (UA)), $120^{\circ}C$ (peak aging (PA)), and $160^{\circ}C$ (over aging (OA)), respectively. Charging tests were performed at RT for 12, 24, 36 hours under potentiostatic conditions (-2000 mV vs (Ag/AgCl)) for 12, 24 and 36 hours in 1M $H_2SO_4$ and 0.1%$NH_4SCN$ solution. The fracture surface was examined by scanning electron microscopy (SEM). X-ray diffraction (XRD) pattern in peak aged sample was obtained before and after hydrogen charging from extruded Al-6.3Zn-2.4Mg alloys. The decreasing rate of tensile strength and elongation is represented in order of over aging < under aging < peak aging, and it is believed that the hydrogen recharge is more sensitive to elongation than tensile strength. The formation of $AlH_3$ in hydrogen charged Al-6.3Zn-2.4Mg alloys has been confirmed by X-ray diffraction studies.

A Zr-based amorphous alloy specimen was produced by vacuum die casting process. The salt spray test was carried out using the specimens in the as-cast, $Al_2O_3$ and $ZrO_2$ particle blasted state. Using these specimens, the SEM-EDX and XRD analyses, DSC measurement and bending strength test were conducted. After the salt spray test, the specimens were not experienced phase change and thermal characteristics of the alloys were remained unchanged. In the as-cast specimen, corrosion products were not observed. However, in the $Al_2O_3$ particle blasted specimen, pitting corrosion occurred and the detected corrosion products were $ZrCl_2$ and $NaZrO_3$. Due to the salt spray test, bending strength of the $Al_2O_3$ blasted specimens showed about 100 MPa lower strength than the other specimens. The bending fracture surface was vein pattern which was shown typically in the amorphous alloys.