In the present work, the effect of adding Ce on the corrosion behavior of Mg-4Al-2Sn-1Ca alloy was investigated. The studied alloys were fabricated by gravity casting method and a potentiodynamic polarization, A.C. impedance and hydrogen evolution tests were carried out in a 3.5% NaCl solution with pH 7.2 at room temperature to measure the corrosion properties of Mg-4Al-2Sn-1Ca-xCe alloys. The microstructure of the Mg-4Al-2Sn-1Ca alloy was composed of ${\alpha}$-Mg, Mg17Al12, Mg2Sn and CaMgSn phase. Also, a $Al_{11}Ce_3$ phase was newly formed by the addition of Ce. With an increase of the Ce contents, the microstructure became refined and the corrosion resistance improved.

The effect of $Al_2Ca$ on the oxidation resistance and tensile property of Al-5Mg alloys was investigated. According to the TGA (Thermogravimetric analysis) result at $550^{\circ}C$ after 24hrs, the Al-5Mg alloy showed parabolic behavior with weight gain. On the other hand, there was almost no difference in the weight changes of the $Al_2Ca$ added Al-5Mg alloys during the oxidation. It was thought that the improvement of oxidation resistance in $Al_2Ca$ added Al-5Mg alloys might be due to the formation of a protective oxide layer with CaO and MgO on the surface. The microstructures of the alloys showed grain refinement with an increasing $Al_2Ca$ content. From the tensile test, the yield strength of the alloys were improved with an increasing $Al_2Ca$ content. The 0.07 mass%$Al_2Ca$ added Al-5Mg alloy showed similar elongation and increased strength, simultaneously. It was considered that the addition of $Al_2Ca$, which was superior in the oxidation resistance of Al, reduced the formation of Mg oxides and inclusions during the alloying. This, partly led to the improvement of tensile properties.

Pure magnesium and magnesium alloys have been applied to various kinds of industrial fields, especially automotive and electronic parts. These parts are manufactured mainly through a diecasting process. These days, magnesium ingots are used as raw material, and recycled ingots are often used for commercial purposes. But the quality of virgin magnesium and recycled ingots is not secure. Therefore, massive casting defects can occur, and some things manufactured can be damaged by these defects. This study evaluated the inclusions of virgin magnesium and recycled ingot. It also included composition analysis by spectrometer, measuring inclusion contents by SEM & EDS, and performing a brightness test on fractured surfaces. The brightness test is generally very easy and obtains results quickly, so its results have been compared with the results obtained from various test methods. From the test results, we obtained a satisfactory result in evaluating inclusion and oxide. The brightness values are lower as the inclusion contents are higher. When the brightness value is over 47 in AM50A and 44 in AZ91D, the mechanical properties are expected to be good.