Ductile cast iron has good ductility and toughness, for the graphite morphology is spheroidal. It has been reported that the strengthening and toughening of the ductile cast iron was resulted from the modification of matrix structure by the heat treatment or the addition of alloying elements. In this study, effects of various special heat treatments (cyclic heat treatment and intermediate heat treatment) and Ni addition on the toughness and strength of the austempered ductile cast iron were studied. The results obtained from this study were as follows : 1. The amount of fine pearlite was increased with the Ni content and the number of cycle in cyclic heat treatment. 2. When the specimens treated and not by special heat treatment at 820 was austempered, in the former the austenite was formed on grain boundary entirely, but in the latter on grain boundary partially. 3. The impact energy was decreased with the Ni content, because the coarisen austenite pools formed with the Ni content was transformed into martensite during quenching. 4. The mechanical properties of austempered ductile cast iron containing 2%Ni treated cyclic heat treatment(5 cycles)was very excellent in handness 99(HRB), impact energy 12(kg-m) maximum fracture load 1500(kg-f).

The microstructures of sintered products of $Fe_2O_3$or $Fe_3O_4$-Oxide added cast iron powder was investigated. And the effects of particle size distribution was investigated too. As the result, the structures of sintered products did not related to the species of Fe-Oxide. Th porosity of sintered products was decreased in size and spherodized with increasing sintering temperature, decreasing Fe-Oxide quantity. Fe-Oxide itself did not hinder sintering of cast iron powder particularly, therefore sintering could be occurred without termination of reduction of it. And the sintered products of finer particle size distribution had finer and more spherodized porosity, and had minimized the deviation of size and shape of porosity.

The major effects of RSP sre 1) extension of solid solubilities, 2) formation of metastable phaeses, 3) microstructural refinement 4) segregationless. The main trust of this study was to investigate the effects of superimposing RSP on the structure and properties of HSLA steels. Powder was made by NGA (Nitrogen Gas Atomization) process, and consolidated by HIP. The high grain-coarsening resistance of NGA-HIP steels was attributed to a fine dispersion of oxide precipitates. The average grain size for the NGA-HIP steels was somewhat finer than that for the conventional HSLA steels, The impact properteis of NGA-HIP steels were improved over those of the conventional HSLA steels.