• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.658-662
• /
• 2000

The microstructure, adhesion strength and conductivity of electroplated Sn-Cu Films on Alloy42 lead Frame were measured for comparison. In the case of electroplated 90Sn10Cu, 99Sn1Cu, Cu$\sub$10/Sn$_3$Phase was formed and Ni$_3$Sn$_2$Phase was formed after 200$^{\circ}C$, 30min annealing. In the case of electroplated 99Sn1Cu, Cu$\sub$10/Sn, Ni$_3$Sn phases were formed and Ni$_3$Sn$_4$, Ni$_3$Sn$_4$phases were formed after 200$^{\circ}C$, 30min annealing. 90Sn10Cu film was measured better uniformity, adhesion strength and conductivity than 99Sn1Cu.

• Tribology and Lubricants
• /
• v.37 no.3
• /
• pp.83-90
• /
• 2021

In this study, an ultrasonic nanocrystal surface modification (UNSM) was used to improve the mechanical properties, scratch resistance and tribological performance of Cu-based bimetals, which are usually used to manufacture sliding bearings and bushings for internal combustion engines (ICEs). Two different Cu-based bimetals, namely CuPb10Sn10 and CuSn10Bi7, were sintered onto a low carbon steel substrate. The mechanical properties and dry tribological performance using a tensile tester and micro-tribo tester were evaluated, respectively. The scratch resistance was assessed using a micro-scratch tester at an incremental load. The tensile test results showed that the yield strength (YS) and ultimate tensile strength (UTS) of both Cu-based bimetals increased after UNSM. Furthermore, the scratch and tribological tests results revealed that the scratch resistance and tribological performance of both Cu-based bimetals were improved by the application of UNSM. These improvements were mainly attributed to the eliminated pores, increased hardness and reduced roughness after UNSM. CuSn10Bi7 demonstrated better mechanical properties, scratch resistance and tribological performance than CuPb10Sn10. It was found that the presence of Bi in CuSn10Bi7 formed a Cu₁₁Bi₇ intermetallic phase, which is harder than Cu₃Sn. Hence, CuSn10Bi7 demonstrated higher strength and wear resistance than CuPb10Sn10. In addition, a CuSn10Bi7 formed both SnO₂ and Bi₂O₃ that prevented adhesion and improved the tribological performance. It can be expected that under dry tribological conditions, ICEs can utilize UNSM bearings and bushings made of CuSn10Bi7 instead of CuPb10Sn10 under oil-lubricated conditions.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.317-321
• /
• 2012

In this study, Cu-5Ni-10Sn(wt%) spinodal alloy was manufactured by gas atomization spray forming, and the microstructural features and mechanical properties of Cu-5Ni-10Sn alloy have been investigated during homogenization, cold working and age-hardening. The spray formed Cu-5Ni-10Sn alloy consisted of an equiaxed microstructure with a mixture of solid solution ${\alpha}$-(CuNiSn) grains and lamellar-structure grains. Homogenization at $800^{\circ}C$ and subsequent rapid quenching formed a uniform solid solution ${\alpha}$-(CuNiSn) phase. Direct aging at $350^{\circ}C$ from the homogenized Cu-5Ni-10Sn alloy promoted the precipitation of finely distributed ${\gamma}$' or ${\gamma}-(Cu,Ni)_3Sn$ phase throughout the matrix, resulting in a significant increase in microhardness and tensile strength. Cold working prior to aging was effective in strengthening Cu-5Ni-10Sn alloy, which gave rise to a maximum tensile strength of 1165 MPa. Subsequent aging treatment slightly reduced the tensile strength to 1000-1100 MPa due to annealing effects.

• Korean Journal of Materials Research
• /
• v.13 no.2
• /
• pp.133-136
• /
• 2003

Sn-2.5Cu alloy layers were deposited on the Alloy 42 lead-frame substrates by the electroplating method, and their microstructures, adhesion strength, and electrical resistivity were measured to evaluate the applicability of Sn-Cu alloy as a surface finishing material of electronic parts. The Sn-2.5Cu layers were electroplated in the granular form, and composed of pure Sn and Cu$_{6}$Sn$_{5}$ intermetallic compound. Surfaces of the electroplated Sn-2.5Cu layers were rather rough and also the thickness variance was large. The adhesion strength of the Sn-2.5Cu electroplated layers was highly comparable to that of the electroplated Cu alloy layer and the electrical conductivity was about 10 times higher than the pure Sn. After the 20$0^{\circ}C$ 30 min. annealing of the electroplated Sn-2.5Cu layers, the surface roughness was reduced, and adhesion strength and conductivity were improved. These results showed the Sn-Cu alloys can be used as an excellent surface finishing material.ial.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.2
• /
• pp.35-39
• /
• 2012

We studied interfacial reaction and bonding characteristics of a flip chip bonding with the viewpoint of formation behavior of intermetallic compounds. For this purpose, Sn-0.7Cu and Sn-3Cu solders were reflowed on the Al/Cu and Al/Ni UBMs. When Sn-0.7Cu was reflowed on the Al/Cu UBM, no intermetallic compounds were formed at the solder/UBM interface. The $Cu_6Sn_5$ intermetallic compounds formed by reflowing Sn-3Cu solder on the Al/Cu UBM were spalled from the interface, resulting in delamination of the solder/UBM interface. On the other hand, the $(Cu,Ni)_6Sn_5$ intermetallic compounds were formed by reflowing of Sn-0.7Cu and Sn-3Cu on the Al/Ni UBM and the interfacial bonding between the Sn-Cu solders and the Al/Ni UBM was kept stable.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.2
• /
• pp.91-97
• /
• 2014

With Pb-free solder joints containing Sn-Ag-Cu-based ternary alloys (Sn-1.0 wt.%Ag-0.5Cu and Sn-4.0Ag-0.5Cu) and Sn-Ag-Cu-In-based quaternary alloys (Sn-1.0Ag-0.5Cu-1.0In, Sn-1.2Ag-0.5Cu-0.4In, Sn-1.2Ag-0.5Cu-0.6In, and Sn-1.2Ag-0.7Cu-0.4In), fracture-mode change, shear strengths, and fracture energies were observed and measured under a high-speed shear test of 500 mm/s. The samples in each composition were prepared with as-reflowed ones or solid-aged ones at $125^{\circ}C$ to 500 h. As a result, it was observed that ductile or quasi-ductile fracture modes occurs in the most of Sn-Ag-Cu-In samples. The happening frequency of a quasi-ductile fracture mode showed that the Sn-Ag-Cu-In joints possessed ductile fracture properties more than that of Sn-3.0Ag-0.5Cu in the high-speed shear condition. Moreover, the Sn-Ag-Cu-In joints presented averagely fracture energies similar to those of Sn-Ag-Cu joints. While maximum values in the fracture energies were measured after the solid aging for 100 h, clear decreases in the fracture energies were observed after the solid aging for 500 h. This result indicated that reliability degradation of the Sn-Ag-Cu-In solder joints might accelerate from about that time.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.3
• /
• pp.45-51
• /
• 2013

Thermal annealing tests were performed in an in-situ scanning electron microscope chamber at $130^{\circ}C$, $150^{\circ}C$, and $170^{\circ}C$ in order to investigate the effects of solder structure on the growth kinetics of intermetallic compound (IMC) in Cu/Sn-3.5Ag microbump. Cu/Sn-3.5Ag($6{\mu}m$) microbump with spreading solder structure showed $Cu_6Sn_5$ and $Cu_3Sn$ phase growths and then IMC phase transition stages with increasing annealing time. By the way, Cu/Sn-3.5Ag($4{\mu}m$) microbump without solder spreading, remaining solder was transformed to $Cu_6Sn_5$ right after bonding and had only a phase transition of $Cu_6Sn_5$ to $Cu_3Sn$ during annealing. Measured activation energies for the growth of the $Cu_3Sn$ phase during the annealing were 0.80 and 0.71eV for Cu/Sn-3.5Ag($6{\mu}m$) and Cu/Sn-3.5Ag($4{\mu}m$), respectively.

• Korean Journal of Materials Research
• /
• v.10 no.11
• /
• pp.770-777
• /
• 2000

Microstructure and mechanical properties of the $Cu_6Sn_5$-dispersed 63Sn-37Pb solder alloy, for which $Cu_6Sn_5$ powders less than $1{\mu\textrm{m}}$ size were fabricated by mechanical alloying, were characterizde and compared with those of the Cu-dispersed solder alloy. Compared to the $Cu_6Sn_5$-dispersed solder alloy, large amount of $Cu_6Sn_5$ and fast growth of $Cu_6Sn_5$ were observed in the Cu-dispersed alloy. The $Cu_6Sn_5$-dispersed solder alloy exhibited lower yield strength, but higher ultimate tensile strength than those of the Cu-dispersed alloy. With dispersion of 1~9 vol% $Cu_6Sn_5$ and Cu, the yield strength increased from 23 MPa and to 40 MPa, respectively. The ultimate tensile strength increased from 34.7 MPa to 45.3 MPa and to 43.1 MPa with dispersion of 5 vol% $Cu_6Sn_5$ and Cu, respectively.

• Journal of Welding and Joining
• /
• v.25 no.2
• /
• pp.82-88
• /
• 2007

Sn-3.0Ag-0.5Cu lead fee solder was generally utilized in electronics assemblies. But it is insufficient to research about activation energy(Q) that is applying to evaluate the solder joint reliability of environmental friendly electronics assemblies. Therefore this study investigated Q values which are needed to IMC formation and growth of Sn-3.0Ag-0.5Cu/Cu and Sn-40pb/Cu solder joints during aging treatment. We bonded Sn-3.0Ag-0.5Cu and Sn-40Pb solders on FR-4 PCB with Cu pad$(t=80{\mu}m)$. After reflow soldering, to observe the IMC formation and growth of the solder joints, test specimens were aged at 70, 150 and $170^{\circ}C$ for 1, 2, 5, 20, 60, 240, 960, 15840, 28800 and 43200 min, respectively. SEM and EDS were utilized to analysis the IMCS. From these results, we measured the total IMC$(Cu_6Sn_5+Cu_3Sn)$ thickness of Sn-3.0Ag-0.5Cu/Cu and Sn-40Pb/Cu interface, and then obtained Q values for the IMC$(Cu_6Sn_5,\;Cu_3Sn)$ growth of the solder joints.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.180-186
• /
• 2011

Isothermal annealing and electromigration tests were performed at $125^{\circ}C$ and $125^{\circ}C$, $3.6{\times}10_4A/cm^2$ conditions, respectively, in order to compare the growth kinetics of the intermetallic compound (IMC) in the Cu/thin Sn/Cu bump. $Cu_6Sn_5$ and $Cu_3Sn$ formed at the Cu/thin Sn/Cu interfaces where most of the Sn phase transformed into the $Cu_6Sn_5$ phase. Only a few regions of Sn were not consumed and trapped between the transformed regions. The limited supply of Sn atoms and the continued proliferation of Cu atoms enhanced the formation of the $Cu_3Sn$ phase at the Cu pillar/$Cu_6Sn_5$ interface. The IMC thickness increased linearly with the square root of annealing time, and increased linearly with the current stressing time, which means that the current stressing accelerated the interfacial reaction. Abrupt changes in the IMC growth velocities at a specific testing time were closely related to the phase transition from $Cu_6Sn_5$ to $Cu_3Sn$ phases after complete consumption of the remaining Sn phase due to the limited amount of the Sn phase in the Cu/thin Sn/Cu bump, which implies that the relative thickness ratios of Cu and Sn significantly affect Cu-Sn IMC growth kinetics.