• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.1
• /
• pp.15-18
• /
• 2012

Transparent conductive indium zinc oxide thin films were prepared by spin-coating a sol-gel solution. Zinc acetate dihydrate [$Zn(CH_3COO)_2{\cdot}2H_2O$] and indium acetate [In$(CH_3COO)_3$] were used as starting precursors, and 2-methoxyethanol with 1-propanol as solvents. Upon annealing in a temperature range from 500 to $1000^{\circ}C$, the thin film crystallizes into polycrystalline $In_2O_3$(ZnO). The lowest electrical resistivity was obtained at an annealing temperature of $700^{\circ}C$ as $2{\Omega}{\cdot}cm$. Average optical transmittances were higher than 80% at all annealing temperatures. These experimental results confirm that the sol-gel spin-coating can be a good simplified practical method for forming transparent electrodes.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.1
• /
• pp.11-14
• /
• 2000

Transparent conducting ITO thin films have been studied and developed for the solar cell substrate or LCD substrate. ITO thin film has been mostly fabricated by high cost sputtering method. In this research, sol-gel method is applied to fabricate ITO thin film at lower cost. The research is focused on the establishment of process condition and development of precursor. Organic sol was made of indium tri-isopropoxide dissolved in ethylene glycol monoethyl ether. The hydrolysis was controled by addition of acetyl acetone. Tin(IV) chloride was added as dopant. Inorganic sol was made of indium acetate dissolve din normal propanol. Spin coating technique was applied to coat ITO on borosilicate glass. The resistivity of ITO thin film was approximately $0.01\Omega{\cdot}cm$ and the transmittance is higher than $90\%$ in a visible range.

• Advances in nano research
• /
• v.2 no.4
• /
• pp.179-186
• /
• 2014

Indium-nitrogen co-doped zinc oxide thin films (INZO) were prepared on glass substrates in the atmosphere by ultrasonic spray pyrolysis. The aqueous solution of zinc acetate, ammonium acetate and different indium sources: indium (III) chloride and indium (III) nitrate were used as the precursors. After film deposition, different anneal temperature treatment as 350, 450, $550^{\circ}C$ were applied. Electrical properties as concentration and mobility were characterized by Hall measurement. The surface morphology and crystalline quality were characterized by SEM and XRD. With the activation energy analysis for both films, the concentration variation of the films at different heat treatment temperature was realized. Donors correspond to zinc related states dominate the conduction mechanism for these INZO films after $550^{\circ}C$ high temperature heat treatment process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.4
• /
• pp.256-261
• /
• 2021

Indium-doped Mg_0.05Zn_0.95O thin films were deposited on glass substrates by a sol-gel method. Three types of indium precursors such as indium chloride, indium acetate, and indium nitrate were used as doping sources. Physical properties of fabricated thin films were analyzed through XRD (x-ray diffraction), UV-vis spectrophotometer, Hall effect measurement, and EDS (energy dispersive x-ray spectroscopy). All In-doped thin films grown in this study exhibited a preferred orientation of (002) with over 80% transmittance. The results showed that the Mg_0.05Zn_0.95O thin film from indium chloride as the indium precursor has higher crystallinity and transmittance with lower resistivity when compared with those from other indium precursors.

• Journal of the Korean Chemical Society
• /
• v.35 no.5
• /
• pp.506-511
• /
• 1991

A sensitive adsorptive stripping voltammetric study was investigated on the complex of indium with morin at a hanging mercury drop electrode in 0.1 M acetate buffer (pH 3.20) solution. The adsorption phenomena were observed by differential-pulse voltammetry. The effects of various analytical conditions were discussed on the reduction peak current of the adsorbed complex on the surface of HMDE. Interferences by other trace metals and surfactant were also discussed. Detection limit was 2.6 nM of indium after 90 second deposition time, and the relative standard deviation (n = 7) at 4TEX>${\mu}g$/l indium was 2.0%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.7
• /
• pp.413-416
• /
• 2017

We investigated solution-processed indium-yttrium-oxide (IYO) TFTs using apoly (methyl methacrylate) (PMMA) passivation layer. The IYO semiconductor solution was prepared with 0.1 M indium nitrate hydrate and 0.1 M yttrium acetate dehydrate as precursor solutions. The solution-processed IYO TFTs showed good performance: field-effect mobility of $13.13cm^2/Vs$, a threshold voltage of 8.2 V, a subthreshold slope of 0.93 V/dec, and a current on-to-off ratio of $7.2{\times}10^6$. Moreover, the PMMA passivation layers used to protectthe IYO active layer of the TFTs, did so without deteriorating their performance under ambient conditions; their operational stability and electrical properties also improved by decreasing leakage current.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.7
• /
• pp.432-436
• /
• 2017

IZO transistors with $Al_2O_3$ as gate dielectrics have been investigated. To improve permittivity in an ambient dielectric layer, we grew $Al_2O_3$ by atomic layer deposition directly onto the substrates. Then, we prepared IZO semiconductor solutions with 0.1 M indium nitrate hydrate [$In(NO_3)_3{\cdot}xH_2O$] and 0.1 M zinc acetate dehydrate [$Zn(CH_3COO)_2{\cdot}2H_2O$] as precursor solutions; the IZO solution made with a molar ratio of 7:3 was then prepared. It has been found that these oxide transistors exhibit low operating voltage, good turn-on voltage, and an average field-effect mobility of $0.90cm^2/Vs$ in ambient conditions. Studies of low-voltage driving of IZO transistors with atomic layer-deposited high-k $Al_2O_3$ as gate dielectric provide data of relevance for the potential use of these materials and this technology in transparent display devices and displays.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.7
• /
• pp.437-440
• /
• 2017

We report on amorphous thin-film transistors (TFTs) with indium zinc oxide (IZO) channel layers that were fabricated via a solution process. We prepared the IZO semiconductor solution with 0.1 M indium nitrate hydrate and 0.1 M zinc acetate dehydrate as precursor solutions. The solution- processed IZO TFTs showed good performance: a field-effect mobility of $7.29cm^2/Vs$, a threshold voltage of 4.66 V, a subthreshold slope of 0.48 V/dec, and a current on-to-off ratio of $1.62{\times}10^5$. To investigate the static response of our solution-processed IZO TFTs, simple resistor load-type inverters were fabricated by connecting a $2-M{\Omega}$ resistor. Our IZOTFTbased N-MOS inverter performed well at operating voltage, and therefore, isa good candidate for advanced logic circuits and display backplane.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.8
• /
• pp.484-490
• /
• 2017

We investigated the rewritable operation of a non-volatile memory device composed of Al (top)/$TiO_2$/indium-zinc-oxide (IZO)/Al (bottom). The oxygen-deficient IZO layer of the device was spin-coated with 0.1 M indium nitrate hydrate and 0.1 M zinc acetate dehydrate as precursor solutions, and the $TiO_2$ layer was fabricated by atomic layer deposition. The oxygen vacancies IZO layer of an active component annealed at $400^{\circ}C$ using thermal annealing and it was proven to be in oxygen vacancies and oxygen binding environments with OH species and heavy metal ions investigated by X-ray photoelectron spectroscopy. The device, which operates at low voltages (less than 3.5 V), exhibits non-volatile memory behavior consistent with resistive-switching properties and an ON/OFF ratio of approximately $3.6{\times}10^3$ at 2.5 V.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.516-519
• /
• 2011

Indium tin oxide (ITO) coatings were made using an ITO slurry and an ITO sol. This was achieved by dispersing nanosized ITO powder in a mixed solvent without any dispersant and developing an adhesive ITO sol from indium acetate and tin tetrachloride in a mixture of DMF and n-butanol. Coating was carried out in one step by spin coating an ITO slurry, which was then followed by an ITO sol over it. Here, the sol penetrates into the nano ITO particle layers to make them adhere to each other as well as to a glass substrate. This is then followed by sintering at 500$^{\circ}C$ for 1 h to produce a uniform film consisting of ITO particles of about 50 nm and 10 nm. ITO films were obtained with sheet resistances from 450 to 1500 ohm/${\Box}$ by varying spin speed and concentration. Transmittance is higher than 90% at 550 nm.