• Corrosion Science and Technology
• /
• v.22 no.6
• /
• pp.393-398
• /
• 2023

Properties of hafnium nitride (HfN) coatings are affected by deposition conditions, most often by the sputtering technique. Appropriate use of different magnetron sputtering modes allows control of the structural development of the film, thereby enabling adjustment of its properties. This study compared properties of HfN coatings deposited by direct current magnetron sputtering (dcMS), mid-frequency direct current magnetron sputtering (mfMS), and inductively coupled plasma-assisted magnetron sputtering (ICPMS) systems. The microstructure, crystalline, and mechanical properties of these HfN coatings were investigated by field emission electron microscopy, X-ray diffraction, atomic force microscopy, and nanoindentation measurements. HfN coatings deposited using ICPMS showed smooth and highly dense microstructures, whereas those deposited by dcMS showed rough and columnar structures. Crystalline structures of HfN coatings deposited using ICPMS showed a single δ-HfN phase, whereas those deposited using dcMS and mfMS showed a mixed δ-HfN and HfN_0.4 phases. Their performance were increased in the order of dcMS < mfMS < ICPMS, with ICPMS achieving a value of 47.0 GPa, surpassing previously reported results.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.195-199
• /
• 2011

Mo thin films were deposited on soda lime glass at room temperature by using DC magnetron sputtering The electrical and structural properties of the films were investigated by varying DC power and gas pressure as the deposition parameter. As DC power increased, the deposition rate of Mo films was increased and the electrical resistivity was decreased. It was observable that the crystallinity of the films was improved with increasing DC power. As gas pressure decreased, the deposition rate and resistivity of the films were decreased, and long rectangular grains were densely formed. With increasing gas pressure, the grains were transformed to a round shape and the voids on the film surface were increased. It was confirmed that the electrical resistivity of Mo films was increased as the amount of oxygen combined with Mo atoms increased. It was also disclosed that the films have low resistivity as the degree of coupling of oxygen with Mo was reduced due to the enhancement of the crystallinity of the films.

• Journal of the Korean Physical Society
• /
• v.73 no.11
• /
• pp.1712-1715
• /
• 2018

To study the applications for ferroelectric non-volatile memory and ferroelectric memristor, etc., deposition pressure dependent electric the properties of $(Hf,\;Zr)O_2$ thin films by RF sputtering deposition method were investigated. The bottom electrode was TiN thin film to produce stress effect on the formation of orthorhombic phase and top electrode was Pt thin film by DC sputtering deposition. Deposition pressure was varied along with the same other deposition conditions, for example, sputtering power, target to substrate distance, post-annealing temperature, annealing gas, annealing time, etc. The structural and electric properties of the above thin films were investigated. As a result, it is confirmed that the electric properties of the $(Hf,\;Zr)O_2$ thin films depend on the deposition pressure which affects structural properties of the thin films, such as, structural phase, ratio of the constituents, etc.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.55.1-55.1
• /
• 2010

Cost efficient and large area deposition of superior quality $Al_2O_3$ doped zinc oxide (AZO) films is instrumental in many of its applications including solar cell fabrication due to its numerous advantages over ITO films. In this study, AZO films were prepared by a highly efficient rotating cylindrical dc magnetron sputtering system using AZO target, which has a target material utilization above 80%, on glass substrates in argon ambient. A detailed analysis on the electrical, optical and structural characteristics of AZO thin films was carried out for solar cell application. The properties of films were found to critically depend on deposition parameters such as sputtering power, substrate temperature, working pressure, and thickness of the films. A low resistivity of ${\sim}5.5{\times}10-4{\Omega}-cm$ was obtained for films deposited at 2kW, keeping the pressure and substrate temperature constant at 3 mtorr and $230^{\circ}C$ respectively, mainly due to an increase in carrier mobility and large grain size which would reduce the grain boundary scattering. The increase in carrier mobility with power can be attributed to the columnar growth of AZO film with (002) preferred orientation as revealed by XRD analysis. The AZO films showed a high transparency of>87% in the visible wavelength region irrespective of deposition conditions. Our results offers a cost-efficient AZO film deposition method which can fabricate films with significant low resistivity and high transmittance that can find application in thin-film solar cells.

• Journal of the Korean Ceramic Society
• /
• v.54 no.1
• /
• pp.33-37
• /
• 2017

Single phase niobium nitride (NbN) coatings were deposited using asymmetric bipolar pulsed dc sputtering by varying pulse frequency and duty cycle of pulsed plasmas. Crystal structure, microstructure, morphology and mechanical properties were examined using XRD, FE-SEM, AFM and nanoindentation. Upon increasing pulse frequencies and decreasing duty cycles, the coating morphology was changed from a pyramidal-shaped columnar structure to a round-shaped dense structure with finer grains. Asymmetric bipolar pulsed dc sputtered NbN coatings deposited at pulse frequency of 25 kHz is characterized by higher hardness up to 17.4 GPa, elastic modulus up to 193.9 GPa, residual compressive stress and a smaller grain size down to 27.5 nm compared with dc sputtered NbN coatings at pulse frequency of 0 kHz. The results suggest that the asymmetric bipolar pulsed dc sputtering technique is very beneficial to reactive deposition of transition-metal nitrides such as NbN coatings.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.10 no.3
• /
• pp.473-478
• /
• 2006

High quality indium tin oxide (ITO) thin films have been prepared by DC magnetron sputtering technique. By controlling the deposition parameters such as substrate temperature and oxygen flow rate, we were able to minimize the negative ion damage during the deposition. Films pr데ared under such conditions were found to posses an excel]ent electrical resistivity of $1.6\times10^{-4}{\Omega}cm$ and also found to have a optical transmission above 90%. We also observe that, increasing the oxygen now rate above 4 sccm leads to an increase in electrical resistivity of the films while the transmission was found to saturate with the increase in the oxygen gas flow.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.342-349
• /
• 2019

Titanium nitride(TiN) thin films have been deposited on PEN(Polyethylene naphthalate) substrate by reactive RF(13.56 MHz) magnetron sputtering in a 25% N₂/Ar mixed gas atmosphere. The pulsed DC bias voltage of -50V on substrates was applied with a frequency of 350 kHz, and duty ratio of 40%(1.1 ㎲). The effects of pulsed DC substrate bias voltage on the crystallinity, color, electrical properties of TiN_x films have been investigated using XRD, SEM, XPS and measurement of the electrical properties such as electrical conductivity, carrier concentration, mobility. The deposition rates of TiN_x films was decreased with application of the pulsed DC substrate bias voltage. The TiN_x films deposited without and with pulsed bias of -50V to substrate exhibits gray and gold colors, respectively. XPS depth profiling revealed that the introduction of the substrate bias voltage resulted in decreasing oxygen concentration in TiN_x films, and increasing the electrical conductivities, carrier concentration, and mobility to about 10 times, 5 times, and 2 times degree, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.52-53
• /
• 2005

$Y_2O_3$ film was directly deposited on Ni-3at%W substrate using DC reactive sputtering technique. Metallic yttrium was used for DC sputtering target and water vapor was used for oxidizing the deposited metallic Yttrium atoms on the substrate. The window of the water vapor turned out to be broad. The minimum partial pressure of water vapor was determined by sufficient oxidation of the $Y_2O_3$ film, and the maximum partial pressure of water vapor was determined by the non-oxidation of the target surface. As the sputtering power was increased, The deposition rate increased without narrowing the window. The fabricated $Y_2O_3$ films showed good texture qualities and surface morphologies. The YBCO film deposited directly on the $Y_2O_3$ buffered Ni-3at%W substrate showed $T_c$, $I_c$ (77 K, self field), and $J_c$ (77 K, self field) of 89 K, 64 A/cm and 1.l $MA/cm^2$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.244-247
• /
• 1995

Physical, electrical and optical properties of Aluminum(Al) thin films were investigated in order to establish the optimum sputtering parameters in mirror reflection films. Al. thin films deposited on corning glass substrate by DC magnetron sputtering were grown as a variation of the input power, operation pressure and deposition time. The properties of the Al thin films have been discussed by deposition rate, SEM, XRD, sheet resistivity, resistivity and reflectance. Al thin films were obtained at the deposition conditions as follows: operating pressure, 3 mtorr; DC input power desnsitiy, 3W/$\textrm{cm}^2$.

• Journal of the Semiconductor & Display Technology
• /
• v.17 no.4
• /
• pp.32-36
• /
• 2018

For various oxygen($O_2$) to argon(Ar) gas ratio, aluminum-doped zinc oxide(AZO) films were deposited for 3 min at different duty ratio by changing reverse pulse times. As the duty ratio increased, the thickness of the AZO film decreased and the sheet resistance increased. It can be concluded that When sputtering AZO Thin film, oxygen interfered with sputtering. When the reverse time was increased, the thickness of AZO was proportional to the real sputtering time and decreased. From the optical transmittance and sheet resistance, it was possible to obtain a higher figure of merits of AZO at a lower reverse pulse time. Even at the short reversed pulse time, it can be concluded that the accumulated charges on the AZO target are completely cleared. At a lower reverse pulse time, pulsed-DC sputtering of AZO is expected to be used instead of DC sputtering in the deposition of transparent conductive oxide(TCO) films without any degradation in thickness and structural/electrical characteristics.