• Journal of the Korean Magnetics Society
• /
• v.21 no.1
• /
• pp.37-41
• /
• 2011

Fe compounds of scoria samples distributed in Songdang-ri positioning north-eastern area of Jeju island were investigated by means of X-ray diffractometry (XRD) and $^{57}Fe$ M$\ddot{o}$ssbauer spectroscopy. The samples were prepared from six parasite. We found that the samples were composed of a typical olivine, pyroxene, ilmenite, $SiO_2$, anorite and anorthoclase, M$\ddot{o}$ssbauer spectrum of the most scoria samples are shown doublets and sextets of olivine, doublets of pyroxene, ilmenite and silicate minerals. And the valence states of Fe ion of the scoria samples in this area are chiefly 3+ charge state and a little 2+ charge state.

• Journal of Magnetics
• /
• v.19 no.3
• /
• pp.210-214
• /
• 2014

The effects of manganese substitution on the crystallographic and magnetic properties of Li-Zn-Cu ferrite, $Li_{0.5}Zn_{0.2}Cu_{0.4}Mn_xFe_{2.1-x}O_4$ ($0.0{\leq}x{\leq}0.8$), were investigated. Ferrites were synthesized via a conventional ceramic method. We confirmed the formation of crystallized particles using X-ray diffraction, field emission scanning electron microscopy and $M{\ddot{o}}ssbauer$ spectroscopy. All of the samples showed a single phase with a spinel structure, and the lattice constants linearly decreased as the substituted manganese content increased, and the particle size of the samples also somewhat decreased as the doped manganese content increased. All the $M{\ddot{o}}ssbauer$ spectra can be fitted with two Zeeman sextets, which are the typical spinel ferrite spectra of $Fe^{3+}$ with A- and B-sites, and one doublet. The cation distribution was determined from the variation of the $M{\ddot{o}}ssbauer$ parameters and of the absorption area ratio. The magnetic behavior of the samples showed that an increase in manganese content led to a decrease in the saturation magnetization, whereas the coercivity was nearly constant throughout. The maximum saturation magnetization was 73.35 emu/g at x = 0.0 in $Li_{0.5}Zn_{0.2}Cu_{0.4}Mn_xFe_{2.1-x}O_4$.

• Journal of Magnetics
• /
• v.19 no.2
• /
• pp.126-129
• /
• 2014

We report the crystallographic and magnetic properties of $Ni_{0.3}Fe_{0.7}Ga_2S_4$ by means of X-ray diffractometer (XRD), a superconducting quantum interference device (SQUID) magnetometer, and a M$\ddot{o}$ssbauer spectroscopy. In particular, $Ni_{0.3}Fe_{0.7}Ga_2S_4$ was studied by M$\ddot{o}$ssbauer analysis for evidence of spin reorientation. The chalcogenide material $Ni_{0.3}Fe_{0.7}Ga_2S_4$ was fabricated by a direct reaction method. XRD analysis confirmed that $Ni_{0.3}Fe_{0.7}Ga_2S_4$ has a 2-dimension (2-D) triangular lattice structure, with space group P-3m1. The M$\ddot{o}$ssbauer spectra of $Ni_{0.3}Fe_{0.7}Ga_2S_4$ at spectra at various temperatures from 4.2 to 300 K showed that the spectrum at 4.2 K has a severely distorted 8-line shape, as spin liquid. Electric quadrupole splitting, $E_Q$ has anomalous two-points of temperature dependence of $E_Q$ curve as freezing temperature, $T_f=11K$, and N$\acute{e}$el temperature, $T_N=26K$. This suggests that there appears to be a slowly-fluctuating "spin gel" state between $T_f$ and $T_N$, caused by non-paramagnetic spin state below $T_N$. This comes from charge re-distribution due to spin-orientation above $T_f$, and $T_N$, due to the changing $E_Q$ at various temperatures. Isomer shift value ($0.7mm/s{\leq}{\delta}{\leq}0.9mm/s$) shows that the charge states are ferrous ($Fe^{2+}$), for all temperature range. The Debye temperature for the octahedral site was found to be ${\Theta}_D=260K$.

• Journal of the Korean Magnetics Society
• /
• v.16 no.2
• /
• pp.144-148
• /
• 2006

$CoGa_{0.1}Fe_{1.9}O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, VSM and $M\ddot{o}ssbauer$ spectroscopy. $CoGa_{0.1}Fe_{1.9}O_4$ powder that was annealed at $250^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle is around 10 nm. The hyperfine fields at 4.2 K f3r the A and B patterns were found to be 518 and 486 kOe, respectively. The blocking temperature $(T_B)$ of superparammagnetic $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant of $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle was calculated to be $3.0X10^5\;ergs/cm^3$. $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle was annealed at $250^{\circ}C$ will be used to candidate for biomedicine applications as magnetic carriers.

• Journal of the Korean Magnetics Society
• /
• v.19 no.2
• /
• pp.57-61
• /
• 2009

$MnFe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, and $M{\ddot{o}}ssbauer$ spectroscopy, VSM. $MnFe_2O_4$ powder that was annealed at $250^{\circ}C$ has spinel structure and behaved superparamagnetically at room temperature. $MnFe_2O_4$ annealed at 400 and $500^{\circ}C$ has a typical spinel structure and is ferrimagnetic in nature. The estimated size of superparammagnetic $MnFe_2O_4$ nanoparticle is around 17 nm. The hyperfine fields of the A and B patterns at 4.2 K were found to be 508 and 475 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $MnFe_2O_4$ nanoparticle is about 120 K. The magnetic anisotropy constant and relaxation time constant of $MnFe_2O_4$ nanoparticle were calculated to be $4.9{\times}10^5erg/cm^3$.

• Journal of Magnetics
• /
• v.15 no.1
• /
• pp.25-28
• /
• 2010

This study examined the crystallographic and magnetic properties of vanadium-substituted lithium cobalt titanium ferrite, $Li_{0.7}Co_{0.2}Ti_{0.2}V_{0.2}Fe_{1.7}O_4$. Ferrite was synthesized using a conventional ceramic method. The samples annealed below $1040^{\circ}C$ showed X-ray diffraction peaks for spinel and other phases. However, the sample annealed above $1040^{\circ}C$ showed a single spinel phase. The lattice constant of the sample was $8.351\;{\AA}$, which was relatively unaffected by vanadium-substitution. The average grain size after vanadium-substitution was $13.90\;{\mu}m$, as determined by scanning electron microscopy. The M$\ddot{o}$ssbauer spectrum could be fitted to two Zeeman sextets, which is the typical spinel ferrite spectra of $Fe^{3+}$ with A and B sites, and one doublet. From the absorption area ratio of the M$\ddot{o}$ssbauer spectrum, the cation distribution was found to be ($Co_{0.2}V_{0.2}Fe_{0.6})[Li_{0.7}Ti_{0.2}Fe_{1.1}]O_4$. Vibrating sample magnetometry revealed a saturation magnetization and coercivity of 36.9 emu/g and 88.6 Oe, respectively, which were decreased by vanadium-substitution.

• Journal of Magnetics
• /
• v.21 no.3
• /
• pp.308-314
• /
• 2016

Cobalt-, zinc-, and nickel-zinc-substituted nano-size manganese ferrite powders, $MnFe_2O_4$, $Mn_{0.8}Co_{0.2}Fe_2O_4$, $Mn_{0.8}Zn_{0.2}Fe_2O_4$ and $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$, were fabricated using a sol-gel method, and their crystallographic and magnetic properties were subsequently studied. The $MnFe_2O_4$ ferrite powder annealed at temperatures above 523 K exhibited a spinel structure, and the particle size increased as the annealing temperature increased. All ferrites annealed at 773 K showed a single spinel structure, and the lattice constants and particle size decreased with the substitution of Co, Zn, and Ni-Zn. The $M{\ddot{o}}ssbauer$ spectrum of the $MnFe_2O_4$ ferrite powder annealed at 523 K only showed a doublet due to its superparamagnetic phase, and the $M{\ddot{o}}ssbauer$ spectra of the $MnFe_2O_4$, $Mn_{0.8}Co_{0.2}Fe_2O_4$, and $Mn_{0.8}Zn_{0.2}Fe_2O_4$ ferrite powders annealed at 773 K could be fitted as the superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. However, the $M{\ddot{o}}ssbauer$ spectrum of the $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$ ferrite powder annealed at 773 K consisted of two Zeeman sextets and one quadrupole doublet due to its ferrimagnetic and paramagnetic behavior. The area ratio of the $M{\ddot{o}}ssbauer$ spectra could be used to determine the cation distribution equation, and we also explained the variation in the $M{\ddot{o}}ssbauer$ parameters by using this cation distribution equation, the superexchange interaction and the particle size. Relative to pure $MnFe_2O_4$, the saturation magnetizations and coercivities were larger in $Mn_{0.8}Co_{0.2}Fe_2O_4$ and smaller in $Mn_{0.8}Zn_{0.2}Fe_2O_4$, and $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$. These variations could be explained using the site distribution equations, particle sizes and magnetic moments of the substituted ions.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.142-147
• /
• 2005

The embrittlement of fast neutron-irradiated reactor pressure vessel (RPV) steels was investigated by X-ray diffraction patterns at room temperature and $M\ddot{o}ssbauer$ spectroscopy at room- and liquid nitrogen-temperature. Neutron fluence on the samples were $10^{12},\;10^{13},\;10^{14},\;10^{15},\;10^{16},\;10^{17},\;10^{18}\;n/cm^2$. The X-ray diffraction patterns showed that the structure of the neutron unirradiated sample was bcc type, where as but the neutron irradiated samples with the fluence higher than $10^{17}\;n/{\cal}cm^2$ were so severely damaged, that bcc type structure disappeared. The $M\ddot{o}ssbauer$ spectra of all samples showed superposition of two or more sextets. In this paper all $M\ddot{o}ssbauer$ spectra were fitted by three set of sextet. The isomer shift and quadrupole splitting values were found around zero. At liquid nitrogen temperature, magnetic hyperfine field and absorption area increase rapidly S 1 sextet in the samples of $10^{17}\~10^{18}\;n/{\cal}cm^2$ neutron fluences. And at room temperature, magnetic hyperfine field and absorption increased rapidly at SI sextet in the samples of $10^{17}\~10^{18}\;n/{\cal}cm^2$ neutron fluences. This rapid increase of magnetic hyperfine field and absorption area were inferred to be caused by the change of $^{56}Fe,\;^{55}Mn$ into $^{57}Fe$ due to by neutron irradiation.

• Journal of Magnetics
• /
• v.13 no.3
• /
• pp.110-113
• /
• 2008

In this study, heavy rare earth garnet $Tb_2Bi_1Ga_1Fe_4O_{12}$ powders were fabricated by a sol-gel and vacuum annealing process. The crystal structure was found to be single-phase garnet with a space group of Ia3d. The lattice constant $a_0$ was determined to be 12.465 ${\AA}$. From the analysis of the vibrating sample magnetometer (VSM) hysteresis loop at room temperature, the saturation magnetization and coercivity of the sample are 7.64 emu/g and 229 Oe, respectively. The N$\acute{e}$el temperature($T_N$) was determined to be 525 K. The M$\ddot{o}$ssbauer spectrum of $Tb_2Bi_1Ga_1Fe_4O_{12}$ at room temperature consists of 2 sets of 6 Lorentzians, which is the pattern of single-phase garnet. From the results of the M$\ddot{o}$ssbauer spectrum at room temperature, the absorption area ratios of Fe ions on 24d and 16a sites are 74.7% and 25.3%(approximately 3:1), respectively. These results show that all of the non-magnetic Ga atoms occupy the 16a site by a vacuum annealing process. Absorption area ratios of Fe ions are dependent not only on a sintering condition but also on the temperature of the sample. It can then be interpreted that the Ga ion distribution is dependent on the temperature of the sample. The M$\ddot{o}$ssbauer measurement was carried out in order to investigate the atomic migration in $Tb_2Bi_1Ga_1Fe_4O_{12}$.

• Journal of the Korean Magnetics Society
• /
• v.24 no.5
• /
• pp.135-139
• /
• 2014

Iron-oxide nanopowders were synthesized by a pulsed wire evaporation (PWE) in various ambient gas conditions. SEM measurement indicates that the spherical iron nanoparticles are about 50 nm in diameter. The phase analysis for the produced iron-oxide powders was systematically investigated by using $M\ddot{o}ssbauer$ spectra and the results show that classified phases of $Fe_2O_3$ and $Fe_3O_4$ can be controlled by regulating the oxygen concentration in the mixed gas during the PWE process. A quadrupole line on the center of $M\ddot{o}ssbauer$ spectrum represents the superparamagnetic phase of 12 % from ${\gamma}-Fe_2O_3$ phase.