ln this paper, the $Sr_{l-x}Ca_xTiO_3(0\leqx\leq0.2)-based$ grain boundary layer ceramics were fabricated to measure dielectric properties with the sintering temperature and the thermal treatment time. The sintering temperature and time were $1420~15206{\circ}C$, 4hours, and the thermal treatment temperature and time of the specimen were $l150^{\circ}C$, 1, 2, 3hours, respectively. The structural and the dielectric properties were investigated by SEM, X-ray, HP4194A and K6517. The average grain size was increased with increasing the sintering temperature, but it decreased up to 15mo1% with increasing content of Ca. X-ray diffraction analysis results showed that all specimens were the cubic structure, and the main peaks were moved to right and the lattice constant were decreased with increasing content of Ca. The appropriate thermal treatment time and temperature of CuO to obtain dielectric properties of $\varepsilon_r>50000,\; tan \delta<0.05\; and \;\DeltaC<\pm10%$ were 2hrs and $l150^{\circ}C$, respectively.

The mechanical and electrical properties of the hot-pressed and pressureless annealed SiC-39vo1.%TiB$_2$electroconductive ceramic composites were investigated as functions of the liquid additives of $Al_2O_3+Y_2O_3$ and the sintering temperature. The result of phase analysis for the SiC-39vo1.%TiB$_2$ composites by XRD revealed $\alpha -SiC(6H),\; TiB_2,\; and YAG(Al_5Y_3O_{12})$ crystal phase. The relative density of SiC-39vo1.% $TiB_2$ composites was increased with increased $Al_2O_3+Y_2O_3$ contents. The fracture toughness showed the highest value of $7.8 MPa.m_{1/2}$ for composites added with 12 wt% $Al_2O_3+Y_2O_3$additives at $1750^{\circk}C$. The electrical resistivity of the SiC-39vo1.%$TiB_2$composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $25S^{\circ}C \;to\; 700^{\circ}C$.

$(Ba_{0.6}Sr_{0.4}Ca_x)TiO_3 + yAl_2O_3$ wt% (x=0.10, 0.15, 0.20, y=0~3.0) ceramics were fabricated by the mixed-oxide method, and their structural and dielectric properties were investigated with variation of composition ratio and $Al_2O_3$ doping content. As results of the X-ray diffraction and microstructure analysis, all BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with an increase of $Al_2O_3$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing $Al_2O_3$doping content. The dielectric loss is minimum at BSCT doped with 1.5wt% $Al_2O_3$content. The tunability was decreased with increasing an Ca content and the BSCT(50/40/10) specimen doped with 2.0wt% $Al_2O_3$content showed the maximum value of 4.2%.

In this paper, the low power (1.5 W) solenoid-type magnetic thin-film transformers utilizing a $Ni_{81}Fe_{19)$ core material were designed and fabricated for 5 MHz-drive DC-DC converter application. The $20\mum$ thick copper films were used as the coils. The transformers fabricated in this work have the sizes of $3.08 mm\times25.5 mm\; and\; 6.15 mm\times12.75 mm.$ The optimum design of solenoid-type magnetic thin film transformers was performed utilizing the conventional equations, a Maxwell computer simulator (Ansoft HFSS V7.0 for PC), and parameters obtained from the magnetic properties of NiFe magnetic core materials. frequency characteristics of inductance, dc resistance (R), coupling factor (k) and gain of developed transformers were measured using HP4194A impedance and gain-phase analyzer. The fabricated transformers with the size of $6.15 mm\time12.75 mm$ exhibit the inductance of $0.83 \muH$, the dc resistance of $2.3\Omega$$\Omega$, the k of 0.91 and the gain of -1 dB at 5 MHz, which show the comparable results to those reported in the recent literatures. The measured high-frequency characteristics for the fabricated transformers agreed well with those obtained by theoretical calculations .

In this paper, we described the export system to monitor and diagnose 765KV power apparatus. To develop this expert system, we studied the knowledge bases and data bases for 765KV transformer and GIS. In order to make the reliable inference of knowledge base and the good MMI(Man Machine Interface), the data bases were consisted of the tables of power apparatus information, limit level value, measured input data, inference result and diagnosis result. The knowledge base had various rules to infer the conditions of transformer and GIS. We applied both the forward chaining and backward chaining methods to these rules of system for good inferences. This paper describes the applied methods for expert system. Also, this developed system was tested with dissolved gas analyzing result and the result was shown.

In this paper, we described the new IEC method with fuzzy theory for detecting abnormal causes within transformer. The proposed technique presented the solution of limitation in case of lying nearly boundary conditions and not having codes for measured gas values in IEC code. Also, we proved the confidence of diagnosed results in the use of the gases values in real fault transformers.

In this paper, using $500\mum-thickness\; (100)\; silicon\; wafer,\; flat\; 65\mum-thickness$ silicon mirror plates were fabricated through dry etching and wet etching, and $45\mum-depth$ grooved driving electrodes were fabricated through UV-LIGA process. Four shapes of the driving electrode were fabricated: twenty four grooves of the $50\mum-width$, twelve grooves of the $100\mum-width$, six grooves of the $200\mum-width$, and no grooves on the driving electrode. Fabricated mirror plate size and spring size are $2400\times2400\times65\mum3\; and \;500\times10\times65\mum3,$ respectively. Mirror plate parts and driving electrodes were assembled into the scanning mirrors. Measured natural resonance frequencies were about 600Hz which have error within $\pm 2%$ to calculated value. Due to the squeeze effect in the narrow gap between the mirror plate and the driving electrode, measured resonance frequencies were reduced as raising the amplitude of the mirror plate. In a case of driving electrode without grooves, the resonance frequency was reduced largely, compared with a case of driving electrode with grooves. According to the experimental results, squeeze effect was smaller in the driving electrode with smaller-width and many grooves. Therefore, the driving electrode with smaller-width and many grooves was effective in low voltage and high speed operation.

This paper presents theoretical and experimental study on the quality-factor of the laterally oscillated electrostatic microactuator, driven by a lateral repulsive-force generated by the asymmetry of planar electric field. The quality-factor of the repulsive-force microactuator using a creeping flow model of the ambient air is evaluated. By filling the simulation results of damping force, we evaluate the dimensionless damping force, $\alpha$, thereby obtaining an analytical damping force, F, in the form of $F=\mu\; \alphaUL,\; where\; \mu,$ U and L denote the air viscosity, the velocity and the characteristic length of the movable electrodes. The measured quality-factor increases from 12 to 13 for the DC bias voltage increased from 60V to 140v. The theoretical quality-factor estimated from the creeping flow model increases from 14.9 to 18.7. Characteristics of quality-factor of the repulsive-force microactuator have been discussed and compared with those of the conventional attractive-force microactuator.