The fatigue behavior of LIPCA was so sensitive to the manufacturing condition, the environmental factors and the change of the test apparatus. Therefore, we could be considering not only the relationship between the stroke range $({\Delta}h)$ and actuating frequency but also the relationship between the stroke range $({\Delta}h)$ and the total effective moment $(M^E)$. Thus, this study proposed the calculation method of the applying $M^E$ when the $({\Delta}h)$ of LIPCA was increased from 1.mm to 20mm. To estimate the relationship between the total effective moment $(M^E)$ and the Bernoulli-Euler bending moment (M) was reviewed. And the residual stress distribution of LIPCA and THUNDER using the CLT was evaluated. In conclusions, converting the $({\Delta}h)$ of LIPCA to the radius of curvature (p) and calculating the $(M^E)$, it was found that the p by the $M^E$ changed similarly as the $({\Delta}h)$. It was found that the $M^E$ was 2.2 times as the M. While CFRP and PZT of LIPCA, which had the superior compressive characteristic, had the compressive residual stress, GFRP was subject to the tensile residual stress. Since this reversed configuration between the compressive residuals stress and the tensile one was made, the requirement of the stroke range $({\Delta}h)$ increase was satisfied.