The low kinds of $Al_2O_3$ composite ceramics were prepared using a mixture of 85 wt.% $Al_2O_3$ (mean size $0.5\;{\mu}m$), 15 wt.% SiC Powder with $Y_2O_3$, as an additive powder (0, 1, 3 and 5 wt.%). The crack-healing strengths were studied as functions of crack-healing temperature and amount of $Y_2O_3$. The in-situ crack-healing behavior was observed at 1,573 K for 1 h in the air. The heat treated specimen with 3 wt.% of $Y_2O_3$ showed better crack-healing ability than specimen with 1 or 5 wt.% of $Y_2O_3$. In case of specimen with 3 wt.% of $Y_2O_3$, the bending strength of the crack-healed specimen at 1,473 K was recovered to the bending strength of smooth specimen treated at 1573 K. The heat-resistance limit temperature of $Al_2O_3$ composite ceramics was 1,073 K, 1,373 K, 873 K for the specimen with 1, 3, 5 wt.% of $Y_2O_3$.