• 한국세라믹학회지
• /
• 제38권9호
• /
• pp.777-781
• /
• 2001

$LiCoO_{2}$ thin films have received attention as cathodes of thin film microbatteries in these days. In this study, $LiCoO_{2}$ thin films are fabricated by a sol-gel spin coating method followed by a post-annealing process. The thermal decomposition behaviour of precursor is investigated by TG/DTA analysis. The change of crystallinity, microstructure and electrochemical properties of final films as the drying temperature changes are also studied by XRD, SEM and galvanostatic charge/discharge cycling test. The relationship between the discharge capacity and the drying temperature are intensively investigated in this work.

• 폴리머
• /
• 제35권2호
• /
• pp.130-135
• /
• 2011

전자 기기의 빠른 발전에 따른 무선 기기들의 사용은 급격히 늘어나고 있다. 그래서 이런 제품에 자가 발전이 가능한 재료를 적용시키는 사례가 점차 늘고 있다. 여기에 사용되는 재료로서 poly(vinylidene fluoride) (PVDF)가 있는데 PVDF는 piezoelectricity를 낼 수 있는 특별한 결정구조인 ${\beta}$-phase를 가지고 있다. 이 논문에서는 piezoelectricity에 결정적인 영향인 ${\beta}$-phase 함량을 증가시키기 위해 다층 PVDF 필름을 제조하였다. 이 PVDF 필름은 용매인 DMAc에 10%로 용해시킨 깃으로 spin rate는 850 rpm, spin time은 60초이며 건조온도는 $60^{\circ}C$이다. 비교적으로 다층 필름은 단열 층보다 더 높은 ${\beta}$-phase함량을 나타내었다 이 ${\beta}$-phase함량은 4-layer 필름이 되기까지 점차 증가되었으며 최대 함량은 7.72이다.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.314-322
• /
• 1997

극저 유전특성을 갖는 SiO2 에어로겔의 박막화의 층간 절연막으로써의 응용성이 연구되었다. 점도가 10~14cP인 SiO2 폴리머 졸을 이소프로판을 분위기 하에서 1000~7000m으로 p-Si(111) 웨이퍼 상에 스핀코팅한 습윤겔 박막을 25$0^{\circ}C$와 1160 psing 조건에서 초임계건조하여 0.5 g/㎤ 정도의 밀도(78% 기공율) 와 4000~21000$\AA$ 범위의 두께를 갖는 SiO2 에어로겔 박막을 제조하였다. 박막의 두께와 미세구조를 제어할 수 있는 주요 인자는 졸의 농도, 회전속도 및 습윤겔 숙성시간임을 알 수 있었다. SiO2 에어로겔 박막의 유전상수 값은 giga급 이상의 차세대 반도체 소자에 충분히 응용될 수 있을 정도로 낮은 2.0 정도이었다.

• 한국식품과학회지
• /
• 제44권5호
• /
• pp.532-539
• /
• 2012

섬유소 식품의 조사처리 여부 확인에서 전자스핀공명분석법의 개선을 위한 기초자료를 마련하고자, 감마선 조사된 브로콜리와 배추의 전처리 건조방법(FD, OD, ALD, 및 WAD)에 따른 cellulose radical을 분석 비교하였다. 브로콜리 시료에서는 single central signal($g_0$=2.0007)이 나타났으며, 배추 시료에서는 single central signal 외에 $Mn^{2+}$ ion에 의한 sextet signal이 추가로 발견되었다. 조사처리한 채소류에서는 singlet signal을 중심으로 좌우 두 개의 side peak가 나타났으며, 각 side peak의 거리는 5.8-6.1 mT로 조사처리 유래의 cellulose radical임을 확인할 수 있었다. 채소류의 부위별로 ESR spectra를 비교한 결과, 배추는 뿌리와 줄기, 브로콜리는 잎, 줄기 모두 조사처리 여부를 판별하는데 있어 적합하였다. 건조 방법별로는 FD와 OD 처리 시 ESR 강도는 더 높았으나, $Mn^{2+}$ ion과 함께 나타나 명확한 signal을 얻기 어려웠다. 반면, ALD와 WAD 방법의 경우 $Mn^{2+}$ ion이 제거되고, signal ratio도 적합하게 나타나 조사 처리된 채소류의 ESR 판별시, ALD와 WAD 방법이 가장 적합할 것으로 판단되었다.

• Bulletin of the Korean Chemical Society
• /
• 제23권12호
• /
• pp.1724-1728
• /
• 2002

The adsorption of proteins on the surface of glass slides is essential for the construction of protein chips. Here, we report that a Histidine (His)-tagged protein protein has been efficiently adsorbed on glass coated with nickel. A variety of nickel chloride-coated plates were prepared by the spin-coating method and adsorbed to the His-tagged protein. When the protein was adsorbed onto the surface of a variety of nickel chloride-coated glass slides, the efficiency of protein adsorption was dependent upon the coating conditions such as nickel chloride concentration, the spin speed and the drying temperature. The slides appropriate for protein adsorption were obtained when the slides were coated with 11%(w/w) of $NiCl_2$ at the spin speed of 4000 rpm for 20 sec and then dried at higher than 40°C. The physical properties of their nickel chloride thin layer were characterized by scanning electron microscopy. x-ray diffraction and atomic force microscopy, finding that the nickel chloride particles were around 10 nm in diameter and uniformly crystallized at 101 faces. These results show that nickel chloride-coated slides prepared by the spin-coating method are utilizable for the construction of Histagged protein chips.

• 한국전기전자재료학회논문지
• /
• 제33권6호
• /
• pp.460-464
• /
• 2020

This study reports the fabrication and application of semitransparent Cu nanoparticle layers. Spin coating and subsequent drying of a Cu colloid solution were performed to deposit Cu nanoparticle layers onto Si and glass substrates. As the spin speed of the spin coating increases, the density of the nanoparticles on the substrate decreases, and the agglomeration of nanoparticles is suppressed. This microstructural variation affects the optical properties of the nanoparticle layers. The transmittance and reflectance of the Cu nanoparticle layers increase with increasing spin speed, which results from the trade-off between the exposed substrate area and surface coverage of the Cu nanoparticles. Since the glass substrates coated with Cu nanoparticle layers are semitransparent and colored, it is anticipated that the application of a Cu nanoparticle-dielectric bilayer structure to transparent solar cells will improve the cell efficiency as well as aesthetic appearance.

• 한국세라믹학회지
• /
• 제34권2호
• /
• pp.188-194
• /
• 1997

TMCS(Trimethylchlorosilane)로 표면개질한 습윤겔을 에탄올에 재분산시켜 코팅용 재분산 실리카 졸을 제조하였고 제조된 졸을 실리콘 기판에 스핀 코팅한 후 상압 하에서 건조(8$0^{\circ}C$) 및 열처리(>25$0^{\circ}C$)하여 열처리온도에 따른 박막의 물성 변화를 관찰하였다. 습윤겔의 재분산시 안정한 재분산 실리카 졸의 제조를 위한 최적 재분산 조건을 습윤겔:에탄올=1g110$m\ell$로 하였고, 이렇게 제조된 재분산 실리카 졸의 농도와 점도는 각각 0.11 M, 2.0-2.2cP였으며 평균 졸 입자크기는 약 30nm정도였다. 1500rpm, 10회 스핀 코팅한 후 8$0^{\circ}C$에서 2시간 건조, 45$0^{\circ}C$에서 2시간 열처리에 의하여 굴절율이 약 1.14, 두께가 400nm정도인 균열이 없는 박막을 얻을 수 있었다.

• 한국재료학회지
• /
• 제10권4호
• /
• pp.264-269
• /
• 2000

$TiO_2$sol(30wt%, anatase)을 이용하여 스핀코팅으로 유리기판에 $TiO_2$박막을 제조하였다. 박막의 두께는 코팅주기의 횟수가 조절하였다. 한 코팅주기는 스핀코팅, 건조, 열처리를 포함한다. 박막의 반응성은 막 위에서의 자외선강도가 0.44와 2.mW/$\textrm{cm}^2$인 조건에서 벤젠기체의 광분해 속도를 통해 조사하였다. 박막의 두께가 증가할수록 표면적으로 증가로 인해 반응성은 증가하였으며, 0.44mW/$\textrm{cm}^2$일 때 4$\mu\textrm{m}$정도 이상의 두께에서 반응성은 더 이상 증가되지 않았다. porous한 $TiO_2$박막은 비교적 넓은 유효표면적을 가지고 있으며, 그것은 비교적 높은 자외선 강도하에서 박막두께에 따라 반응속도를 증가시키는 결과를 낳았다.

• 한국결정성장학회지
• /
• 제18권2호
• /
• pp.72-75
• /
• 2008

Zinc oxide (ZnO) thin films were prepared by a sol-gel method. The structural and electrical properties were investigated by varying drying and annealing temperatures. The thin films were coated (250 nm) by spin-coating method on glass substrates. The optimum drying temperature of ZnO thin films was 300$^{\circ}C$ where the resistivity was the lowest and the preferred c-axis orientation was the highest. The annealing was carried out in air and inert atmospheric conditions. The degree of the preferred c-axis orientation was estimated. The highest preferred c-axis orientation was recorded at 600$^{\circ}C$. The preferred c-axis orientation and grain growth resulted in the mobility enhancement of the ZnO thin films, and the lowest resistivity was 0.62${\Omega}{\cdot}cm$ at 600$^{\circ}C$.

• 한국전기전자재료학회논문지
• /
• 제16권4호
• /
• pp.265-271
• /
• 2003

Ferroelectric lanthanum-substituted Bi$_4$Ti$_3$O$_{12}$(BLT) thin films were fabricated by spin-coating onto a Pt/Ti/SiO$_2$/Si substrate by metalorganic decomposition technique. The grain size in BLT thin films were prepared with controlled by various drying process. The effect of grain size on the crystallization and ferroelectric properties were investigated by x-ray diffraction and field emission scanning electron microscope. The dependence of crystallization and electrical properties are related to the grain size in BLT thin films with different drying temperature. The remanent polarization of BLT thin film increases with the increasing grain size. The value of 2P$_{r}$ and E$_{c}$ of BLT thin film dried at 45$0^{\circ}C$ were 25.9 $\mu$C/$\textrm{cm}^2$ and 85 kV/cm, respectively. The BLT thin film with larger grain size has better fatigue properties. The fatigue properties revealed that small grained film showed more degradation of switching charge than large grained films.lms.s.