• Journal of Welding and Joining
• /
• 제14권2호
• /
• pp.71-78
• /
• 1996

In order to rpovide proper SMT design criteria in a systematic way, a mathematical formulation has been developed to predict the configuration of the solder fillet formed between the gullwing type lead and rectangular pad. Effects of SMT design parameters such as the solder volume and pad dimension on the solder profile are investigated using the FEM that calculates the 3D configuration by minimizing the energy due to surface tension and gravity in the equilibrium state. Design criteria of QFP and SOP are illustrated by plotting the acceptable range of the solder volume with respect to the length and width ratios of the pad and lead. The results show that the acceptable design range increases with increase in the pad length and width. The pad length has more significant effects on design criteria compared with the pad width, and Bond number can be utilized to predict the joint quality.

• ETRI Journal
• /
• 제33권4호
• /
• pp.637-640
• /
• 2011

A novel bumping material, which is composed of a resin and Sn3Ag0.5Cu (SAC305) solder power, has been developed for the maskless solder-on-pad technology of the fine-pitch flip-chip bonding. The functions of the resin are carrying solder powder and deoxidizing the oxide layer on the solder power for the bumping on the pad on the substrate. At the same time, it was designed to have minimal chemical reactions within the resin so that the cleaning process after the bumping on the pad can be achieved. With this material, the solder bump array was successfully formed with pitch of 150 ${\mu}m$ in one direction.

• ETRI Journal
• /
• 제35권2호
• /
• pp.340-343
• /
• 2013

A novel bumping process using solder bump maker is developed for the maskless low-volume solder on pad (SoP) technology of fine-pitch flip chip bonding. The process includes two main steps: one is the aggregation of powdered solder on the metal pads on a substrate via an increase in temperature, and the other is the reflow of the deposited powder to form a low-volume SoP. Since the surface tension that exists when the solder is below its melting point is the major driving force of the solder deposit, only a small quantity of powdered solder adjacent to the pads can join the aggregation process to obtain a uniform, low-volume SoP array on the substrate, regardless of the pad configurations. Through this process, an SoP array on an organic substrate with a pitch of $130{\mu}m$ is successfully formed.

• 마이크로전자및패키징학회지
• /
• 제20권4호
• /
• pp.65-68
• /
• 2013

A novel bumping process using solder bump maker (SBM) is developed for fine-pitch flip chip bonding. It features maskless screen printing process. A selective solder bumping mechanism without the mask is based on the material design of SBM. Maskless screen printing process can implement easily a fine-pitch, low-cost, and lead-free solder-on-pad (SoP) technology. Its another advantage is ternary or quaternary lead-free SoP can be formed easily. The process includes two main steps: one is the thermally activated aggregation of solder powder on the metal pads on a substrate and the other is the reflow of the deposited powder on the pads. Only a small quantity of solder powder adjacent to the pads can join the first step, so a quite uniform SoP array on the substrate can be easily obtained regardless of the pad configurations. Through this process, an SoP array on an organic substrate with a pitch of 130 ${\mu}m$ is, successfully, formed.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.181-183
• /
• 2006

This paper studies the mechanical behaviors of Sn-3.5Ag solder joint against substrate(such as Au/Ni/Cu, Au/cu, Ni/Cu and Cu pad) after induction heating, a new soldering method. It was found that the solder bump formation depends on the time and current of the induction heating system. Also the heating value of the solder bump were found to vary with respect to the thermal conductivity of the pads on the substrate. In case of Au/Ni/Cu pad and Au/Cu pad, solder bump's shear strength were high for the heating time of $1.5{\sim}2sec$. For Ni/Cu pad, solder bump's shear strength were found to increase with time increment.

• 마이크로전자및패키징학회지
• /
• 제17권2호
• /
• pp.41-47
• /
• 2010

PCB와 BGA 패드의 형태가 무연솔더 접합부의 기계적 특성에 미치는 영향을 연구하었다. 현재 BGA/PCB 패드의 형태는 NSMD (Non-Solder Mask Defined)와 SMD (Solder Mask Defined) 두 가지 구조로 형성되어 있다. 본 연구에서는 OSP 도금처리한 무연솔더(Sn-3.0Ag-0.5Cu, Sn-1.2Ag-0.5Cu)의 패드 형태를 NSMD, SMD로 달리하여 낙하충격시험, 굽힘충격시험, 고속전단시험을 통한 솔더 접합부의 기계적 특성을 연구하였다. 낙하충격과 굽힘충격시험의 경우 패드 구조에 따른 솔더볼 접합부의 특성수명은 동일한 경향을 나타내었으며, 솔더접합부의 기계적 특성은 SMD가 NSMD보다 우수하였다. 이 이유는 SMD의 경우 낙하충격 시험과 고속 전단시험 모두 IMC에서 파단이 일어난 반면에 NSMD의 경우 낙하충격 시험 후의 파단면은 패턴을 감싸고 있는 랜드 상단 모서리 부분에서 파단이 일어났기 때문인 것으로 판단된다. 전단시험의 경우에는 NSMD 접합부에서 패드 lift현상이 발생하였다. 따라서 BGA/PCB의 패드구조의 조합은 SMD/SMD > SMD/NSMD > NSMD/SMD > NSMD/NSMD 순으로 기계적 특성 수명이 우수하였다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.450-455
• /
• 2002

Cu-cored Sn-Ag solder balls were fabricated by coating pure Sn and Ag on Cu balls. The melting behavior and the solderability of the BGA joint with the Ni/Au coated Cu pad were investigated and were compared with those of the commercial Sn-Ag and Sn-Ag-Cu balls. DSC analyses clarified the melting of Cu-cored solders to start at a rather low temperature, the eutectic temperature of Sn-Ag-Cu. It was ascribed to the diffusion of Cu and Ag into Sn plating during the heating process. After reflow soldering the microstructures of the solder and of the interfacial layer between the solder and the Cu pad were analyzed with SEM and EPMA. By EDX analysis, formation of a eutectic microstructure composing of $\beta$-Sn, Ag$_3$Sn, ad Cu$_{6}$Sn$_{5}$ phases was confirmed in the solder, and the η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer was found to form at the interface between the solder and the Cu pad. By conducting shear tests, it was found that the BGA joint using Cu-cored solder ball could prevent the degradation of joint strength during aging at 423K because of the slower growth me of η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer formed at the solder, pad interface. Furthermore, Cu-cored multi-component Sn-Ag-Bi balls were fabricated by sequentially coating the binary Sn-Ag and Sn-Bi solders on Cu balls. The reflow property of these solder balls was investigated. Melting of these solder balls was clarified to start at the almost same temperature as that of Sn-2Ag-0.75Cu-3Bi solder. A microstructure composing of (Sn), Ag$_3$Sn, Bi and Cu$_{6}$Sn$_{5}$ phases was found to form in the solder ball, and a reaction layer containing primarily η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ was found at the interface with Ni/Au coated Cu pad after reflow soldering. By conducting shear test, it was found that the BGA joints using this Cu-core solder balls hardly degraded their joint shear strength during aging at 423K due to the slower growth rate of the η'-(Au, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer at the solder/pad interface.he solder/pad interface.

• Journal of Welding and Joining
• /
• 제20권1호
• /
• pp.97-102
• /
• 2002

The growth kinetics of intermetallic compound layers formed between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad by solid stateisothermal aging were examined. The interfacial reaction between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad was investigated at 70, 120, 150, $170^{\circ}C$ for various times. The intermetallic compound layer was composed of two phase: $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the solder and $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the copper and on solder/Ni pad the intermetallic compound layer was $Ni_3Sn_4$. Because the values of time exponent(n) have approximately 0.5, the layer growth of the intermetallic compound was mainly controlled by volume diffusion over the temperature range studied. The apparent activation energy for layer growth of total Cu-Sn($Cu_6Sn_5 + Cu_6Sn$), $Cu_6Sn_5$, $Cu_3Sn$ and $Ni_3Sn_4$ intermetallic compound were 64.82kJ/mol, 48.53kJ/mol, 89.06kJ/mol and 71.08kJ/mol, respectively.

• ETRI Journal
• /
• 제35권6호
• /
• pp.1152-1155
• /
• 2013

A cost-effective and simple solder on pad (SoP) process is proposed for a fine-pitch microbump interconnection. A novel solder bump maker (SBM) material is applied to form a 60-${\mu}m$ pitch SoP. SBM, which is composed of ternary Sn3.0Ag0.5Cu (SAC305) solder powder and a polymer resin, is a paste material used to perform a fine-pitch SoP through a screen printing method. By optimizing the volumetric ratio of the resin, deoxidizing agent, and SAC305 solder powder, the oxide layers on the solder powder and Cu pads are successfully removed during the bumping process without additional treatment or equipment. Test vehicles with a daisy chain pattern are fabricated to develop the fine-pitch SoP process and evaluate the fine-pitch interconnection. The fabricated Si chip has 6,724 bumps with a 45-${\mu}m$ diameter and 60-${\mu}m$ pitch. The chip is flip chip bonded with a Si substrate using an underfill material with fluxing features. Using the fluxing underfill material is advantageous since it eliminates the flux cleaning process and capillary flow process of the underfill. The optimized bonding process is validated through an electrical characterization of the daisy chain pattern. This work is the first report on a successful operation of a fine-pitch SoP and microbump interconnection using a screen printing process.

• ETRI Journal
• /
• 제32권2호
• /
• pp.342-344
• /
• 2010

A novel, maskless, low-volume bumping material, called solder bump maker, which is composed of a resin and low-melting-point solder powder, has been developed. The resin features no distinct chemical reactions preventing the rheological coalescence of the solder, a deoxidation of the oxide layer on the solder powder for wetting on the pad at the solder melting point, and no major weight loss caused by out-gassing. With these characteristics, the solder was successfully wetted onto a metal pad and formed a uniform solder bump array with pitches of 120 ${\mu}m$ and 150 ${\mu}m$.