• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.11
• /
• pp.977-982
• /
• 2005

Al/AlN/n-type 6H-SiC (0001) MIS structures were prepared by AlN layers on vicinal 6H-SiC(0001) substrates with reactive RF magnetron sputtering method. The AlN films were annealed at $900^{\circ}C$, $N_2$ atmosphere lot 1 minutes showed the best result. With XRD analysis, AlN(0002) peak was clearly found. The typical dielectric constant value of the AlN film in the MIS capacitors was obtained as 8.4 from photo C-V. Also, the gate leakage current density of the MlS capacitor was $10^{-10}\;A/cm^2$ order within the electric field of 1.8 MV/cm. Finally, the amount of interface trap densities, $D_{it}$, was evaluated as $5.3\times10^{10}\;eV^{-1}cm^{-2}$ at (Ec-0.85) eV.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.329-334
• /
• 2008

Aluminum oxide films were deposited on n-type GaN substrates by RF magnetron sputtering technique for MIS devices applications using optimized conditions, Well-behaved C - V characteristics were obtained measured in MIS capacitors structures. The calculated interface trap density measured at $300^{\circ}C$ was about $9\times10^{10}/cm^2$ eV in the upper bandgap. The gate leakage current densities of the MIS structures were about $10^{-9}A/cm^2$ and about $10^{-4}A/cm^2$ measured at room temperature and at $300^{\circ}C$ for $a{\pm}1MV/cm$, respectively. These results indicate that the interface property of this structure is enough quality to MIS devices applications.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1463-1465
• /
• 1994

The electrical characteristics of $Al/Ta_2O_5/Si$ metal-oxide-semiconductor (MOS) capacitors were studied. $Ta_2O_5$ films on p-type silicon had been prepared by ionized cluster beam epitaxy technique (ICBE). This $Ta_2O_5$ films have low leakage current, high breakdown strength and low flat band shift. In this research, a single crystalline cpitaxial film of $Ta_2O_5$ has been grown on p-Si wafer using an ICBE technique. The native oxide layer ($SiO_2$) on the silicon substrate was removed below $500^{\circ}C$ by use of an accelerated arsenic ion beam, instead of a high temperature deposition. $Ta_2O_5$ films formed by ICBE technique can be received considerable attention for applications to coupling capacitors, gate dielectrics in MOS devices, and memory storage capacitor insulator because of their high dielectric constants above 20 and low temperature process.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.998-1001
• /
• 2009

A new flexible TFT backplane structure with improved mechanical reliability is proposed. Amorphous indium-gallium-zinc-oxide (a-IGZO) thin film transistors based on this structure have been fabricated on a polyimide substrate, and the resultant mechanical durability has been evaluated in a cyclic bending test. The panel can withstand 10,000 bending cycles at a bending radius of 5 mm without any noticeable TFT degradation. After 10K bending cycles, the change of threshold voltage, mobility, sub-threshold slope, and gate leakage current were only -0.22V, -0.13$cm^2$/V-s, -0.05V/decade, and $-3.05{\times}10^{-13}A$, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.65-66
• /
• 2006

AIGaN/GaN 고전자 이동도 트랜지스터 (High Electron Mobility Transistors, HEMTs)는 와이드 밴드-갭과 높은 항복 전계 및 우수한 채널 특성으로 인해 마이크로파 응용분야와 전력용 반도체에서 각광받고 있다. 최근, 전력 응용분야에서 요구되는 높은 항복 전압과 출력, 우수한 주파수 특성을 획득하기 인해 이중 게이트 AIGaN/GaN HEHTs에 관한 연구가 발표되고 있다. 본 논문에서는 AIGaN/GaN HEMTs에 이중 게이트를 적용하여, 두 개의 게이트와 드레인, 소스의 누설 전류를 각각 측정하여 이중 게이트 AIGaN/GaN HEMTS의 누설 전류 메커니즘을 분석하였다. 또한 제안된 소자의 $SiO_2$ 패시베이션 전 후의 누설 전류 특성을 비교하였다. $SiO_2 $ 패시베이션되지 않은 소자의 누설 전류는 드레인, 소스와 추가 게이트로부터 주 게이트로 흐른 반면, 패시베이션 된 소자 누설 전류는 드레인으로부터 주 게이트 방향의 누설 전류만 존재하였다. $SiO_2$ 패시베이션 된 소자의 누설 전류는 (87.31 nA ) 패시베이션 되지 않은 소자의 누설 전류 ( $8.54{\mu}A$ )에 비해 의게 감소하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.12
• /
• pp.1017-1021
• /
• 2007

To implement tera bit level non-volatile memories of low power and fast operation, proving statistical reproductivity and satisfying reliabilities at the nano-scale are a key challenge. We fabricate the charge trapping nano scaled SONOS unit memories and 64 bit flash arrays and evaluate reliability and performance of them. In case of the dielectric stack thickness of 4.5 /9.3 /6.5 nm with the channel width and length of 34 nm and 31nm respectively, the device has about 3.5 V threshold voltage shift with write voltage of $10\;{\mu}s$, 15 V and erase voltage of 10 ms, -15 V. And retention and endurance characteristics are above 10 years and $10^5$ cycle, respectively. The device with LDD(Lightly Doped Drain) process shows reduction of short channel effect and GIDL(Gate Induced Drain Leakage) current. Moreover we investigate three different types of flash memory arrays.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.743-746
• /
• 2000

Metal-ferroelectric-insulator-semiconductor(MFIS) devices using Pt/$LiNbO_3$/Si structure were successfully fabricated. The dielectric constant of the AIN film calculated from the capacitance in the accumulation region in the capacitance-voltage(C-V) curve was about 8.2. The gate leakage current density of MIS devices using a aluminum electrode showed the least value of 1$\times$$1O^{-8}$A/$cm^2$ order at the electric field of 500kV/cm. The dielectric constant of $LiNbO_3$film on AIN/Si structure was about 23 derived from 1MHz capacitance-voltage (C-V) measurement and the resistivity of the film at the field of 500kV/cm was about 5.6$\times$ $1O^{13}$ $\Omega$.cm.

• Journal of IKEEE
• /
• v.23 no.3
• /
• pp.988-993
• /
• 2019

Over the past decades, the semiconductor industry has continuously scaled down the size of semiconductor devices to increase those performance and to integrate them at higher density on the chip. However, facing the reduction of gate control, higher leakage current, and short channel effect, there is a growing interest in next-generation semiconductors which can overcome these problems. In this paper, we discuss digital circuit design techniques using CNTFET(Carbon NanuTube Field Effect Transistor), which are attracting attention as candidates for the next generation of semiconductors. Since the structure of CNTFETs are clearly different from the structure of the structure of conventional MOSFETs, we will discuss how to utilize existing digital circuit methodology when designing digital circuits using the CNTFETs, and then simulate the performance differences between the two devices.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.257-257
• /
• 2010

One of the critical issues for applications of flexible organic thin film transistors (OTFTs) for flexible electronic systems is the electrical stabilities of the OTFT devices, including variation of the current on/off ratio ($I_{on}/I_{off}$), leakage current, threshold voltage, and hysteresis, under repetitive mechanical deformation. In particular, repetitive mechanical deformation accelerates the degradation of device performance at the ambient environment. In this work, electrical stabilities of the pentacene organic thin film transistors (OTFTs) employing multi-stack hybrid encapsulation layers were investigated under mechanical cyclic bending. Flexible bottom-gated pentacene-based OTFTs fabricated on flexible polyimide substrate with poly-4-vinyl phenol (PVP) dielectric as a gate dielectric were encapsulated by the plasma-deposited organic layer and atomic layer deposited inorganic layer. For cyclic bending experiment of flexible OTFTs, the devices were cyclically bent up to $10^5$ times with 5mm bending radius. In the most of the devices after $10^5$ times of bending cycles, the off-current of the OTFT with no encapsulation layers was quickly increased due to increases in the conductivity of the pentacene caused by doping effects from $O_2$ and $H_2O$ in the atmosphere, which leads to decrease in the $I_{on}/I_{off}$ and increase in the hysteresis. With encapsulation layers, however, the electrical stabilities of the OTFTs were improved significantly. In particular, the OTFTs with multi-stack hybrid encapsulation layer showed the best electrical stabilities up to the bending cycles of $10^5$ times compared to the devices with single organic encapsulation layer. Changes in electrical properties of cyclically bent OTFTs with encapsulation layers will be discussed in detail.

• Journal of the Korean Vacuum Society
• /
• v.16 no.5
• /
• pp.359-365
• /
• 2007

In this paper we present a bottom-gate type of zinc oxide (ZnO) and Gallium (Ga) doped zinc oxide (GZO) based thin film transistors (TFTs) through applying a radio frequency (RF) magnetron sputtering method at room temperature. The gate leakage current can be reduced up to several ph by applying $SiO_2$ thermally grown instead of using new gate oxide materials. The root mean square (RMS) values of the ZnO and GZO film surface were measured as 1.07 nm and 1.65 nm, respectively. Also, the transmittances of the ZnO and GZO film were more than 80% and 75%, respectively, and they were changed as their film thickness. The ZnO and GZO film had a wurtzite structure that was arranged well as a (002) orientation. The ZnO TFT had a threshold voltage of 2.5 V, a field effect mobility of $0.027\;cm^2/(V{\cdot}s)$, a on/off ratio of $10^4$, a gate voltage swing of 17 V/decade and it operated in a enhancement mode. In case of the GZO TFT, it operated in a depletion mode with a threshold voltage of -3.4 V, a field effect mobility of $0.023\;cm^2/(V{\cdot}s)$, a on/off ratio of $2{\times}10^4$ and a gate voltage swing of 3.3 V/decade. We successfully demonstrated that the TFTs with the enhancement and depletion mode type can be fabricated by using pure ZnO and 1wt% Ga-doped ZnO.