• Journal of the Korean institute of surface engineering
• /
• v.43 no.2
• /
• pp.80-85
• /
• 2010

The surfaces of WC-Co and SCM415 were etched to form a micro size protrusion for oil based ultra low friction applications using an ion bombardment process in a filtered vacuum arc plasma. WC-Co species showed that a self-patterned surface was available by the ion bombarding process due to the difference of sputtering yield of WC and Co. And the increasing rate of roughness was 0.6 nm/min at -600 V substrate bias voltage. The increasing rate of roughness of SCM415 species was 1.5 nm/min at -800 V, but the selfpatterning effect as shown in WC-Co was not appeared. When the SCM415 species pretreated by electrical discharge machining is etched, the increasing rate of roughness increased from 1.5 nm/min to 40 nm/min at -800 V substrate bias voltage and the uniform surface treatment was available.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.4
• /
• pp.181-185
• /
• 2005

Lithium cobalt oxide thin film cathode, having thickness of $2.9{\mu}m$ with area of $4cm^2$, was deposited on platinum patterned alumina substrate by radio frequency magnetron sputtering. Li/Co molar ratio, which is an important factor for battery performance, was measured as a function of argon working pressure and applied R.F. power. Constant current charge and discharge performances were characterized with high rate discharge and cycling behavior. Using AC impedance analysis, internal resistance of the thin film battery was measured and simulated by proposed equivalent circuit model.

• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.21-25
• /
• 2016

The microstructural properties and electrical characteristics of sputtering films deposited with a Cu-Ga target are analyzed. The Cu-Ga target is prepared using the cold spray process and shows generally uniform composition distributions, as suggested by secondary ion mass spectrometer (SIMS) data. Characteristics of the sputtered Cu-Ga films are investigated at three positions (top, center and bottom) of the Cu-Ga target by X-ray diffraction (XRD), SIMS, 4-point probe and transmission electron microscopy (TEM) analysis methods. The results show that the Cu-Ga films are composed of hexagonal and unknown phases, and they have similar distributions of composition and resistivity at the top, center, and bottom regions of the Cu-Ga target. It demonstrates that these films have uniform properties regardless of the position on the Cu-Ga target. In conclusion, the cold spray process is expected to be a useful method for preparing sputter targets.

• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.1
• /
• pp.29-33
• /
• 2010

Titanium nitride (TiN) films were deposited on the polycarbonate substrate by using radio frequency (RF) magnetron sputtering without intentional substrate heating. After deposition, the films were bombarded with intense electron beam for 20 minutes. The intense electron irradiation impacts on the crystalline, hardness and surface roughness of the TiN films. The films irradiated with an electron beam of 300 eV show the small grains on the surface, while as deposited TiN films did not showany grains on the surface. Also the surface harness evaluated with micro indenter was increased up to 18 Gpa at electron energy of 900 eV after electron beam irradiation. In addition, surface root mean square (RMS) roughness of the films irradiated with intense electron beam affected strongly. The films irradiated by electron beam with 900 eV have the lowest roughness of 1.2 nm in this study.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.6
• /
• pp.310-314
• /
• 2015

We have considered the influence of electron irradiation on the optical and electrical properties of $In_2O_3/Ti$ bi-layered films prepared with RF and DC magnetron sputtering. The $In_2O_3/Ti$ thin films irradiated at 600 eV shows the lowest resistivity of $6.9{\times}10^{-4}{\Omega}cm$. The optical transmittance in a visible wave length region also influenced with the electron irradiation energy. The film that electron irradiated at 600 eV shows 82.9% of optical transmittance in this study. By comparison of figure of merit, it is concluded that the opto-electrical performance of $In_2O_3/Ti$ bi-layered film is improved with electron irradiation.

• Current Photovoltaic Research
• /
• v.4 no.4
• /
• pp.150-154
• /
• 2016

Mg and In co-doped ZnO (MIZO) thin films with transparent conducting characteristics were successfully prepared on glass substrates by RF magnetron sputtering technique. The Influence of different substrate temperature (from RT to $400^{\circ}C$) on the structural, morphological, electrical, and optical properties of MIZO thin films were investigated. The MIZO thin film prepared at the substrate temperature of $350^{\circ}C$ showed the best electrical characteristics in terms of the carrier concentration ($4.24{\times}10^{20}cm^{-3}$), charge carrier mobility ($5.01cm^2V^{-1}S^{-1}$), and a minimum resistivity ($1.24{\times}10^{-4}{\Omega}{\cdot}cm$). The average transmission of MIZO thin films in the visible range was over 80% and the absorption edges of MIZO thin films were very sharp. The bandgap energy of MIZO thin films becomes wider from 3.44 eV to 3.6 eV as the substrate temperature increased from RT to $350^{\circ}C$. However, Band gap energy of MIZO thin film was narrow at substrate temperature of $400^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.404-405
• /
• 2011

Cu(InGa)$Se_2$ (CIGS) 박막 태양전지의 저가 및 대면적화를 위한 양산화 공정인 two-step process (sputter/selenization) 공정에서는 sputtering으로 형성한 metal precursor stack을 $H_2$ Se gas를 이용하여 selenization하는 공정을 주로 이용한다. 하지만 이러한 selenization 공정은 유독한 $H_2$ Se gas를 이용해야 한다는 점과 긴 시간 동안 열처리를 해야 하는 단점을 가지고 있다. 이에 metal precursor stack 위에 Se 막을 우선 증착하고, Rapid Thermal Process (RTP)를 이용하여 selenization하는 방법이 현재 많은 관심을 끌고 있다. 본 논문에서는 sputtering 이후 RTP를 이용한 CIGS 흡수층 제작에 대한 선행연구의 일환으로 co-evaporator 장비를 이용하여 다양한 구조의 precursor를 제작하고 RTP 조건에 따른 selenization 효과를 연구하였다. Co-evaporator를 이용하여 CIGS, CIG/Se, CuGa/In/Se, In/CuGa/Se 4가지 구조의 precursor stack을 Mo coated soda lime glass 위에 제작하였다. 이때 amorphous 상태의 precursor stack을 만들기 위하여 기판에 열은 가하여 주지 않았으며, 각각의 stack 구조에서 가지고 있는 Cu, In, Ga, Se의 총량을 동일하게 유지하기 위하여 각 stack의 증착 시간을 동일하게 유지하였다. Selenization을 위한 RTP 조건은 550, $600^{\circ}C$ 각각에 대하여 1, 5, 10분으로 split을 진행하였다. Precursor stack의 증착 후 관찰한 XRD 결과는 비정질 상태를 잘 나타내었으며, SEM 결과 CIGS precursor stack을 제외한 나머지 구조의 stack에서는 In 박막의 surface roughness로 인하여 박막의 평탄화가 좋지 않음을 확인하였다. CIGS precursor stack의 경우, RTP 온도와 시간 split와 상관없이 결정화가 잘 이루어졌으나 grain의 성장이 부족하였다. 이에 비하여 CIG/Se, CuGa/In/Se, In/CuGa/Se 구조의 precursor stack의 경우, $550^{\circ}C$ 열처리에서는 InSe의 결정상이 관찰 되었으며 $600^{\circ}C$, 5분 이상 열처리에서 CIGS 결정상이 관찰되었다. 이러한 결과는 Se이 metal 원소들과 함께 있는 CIGS 구조에 비하여 metal precursor stack 위에 Se을 증착한 stack 구조들의 경우는 CIGS 결정을 형성하기 위해 Se이 metal 층들로 확산되어 반응을 하여야 하므로 상대적으로 많은 열에너지가 필요한 것으로 이해할 수 있으며, RTP를 이용한 selenization 공정으로 CIGS 박막 태양전지의 흡수층 형성이 가능함을 확인하였다.

• Korean Journal of Materials Research
• /
• v.21 no.10
• /
• pp.550-555
• /
• 2011

A high-quality CIGS film with a selenization process needs to be developed for low-cost and large-scale production. In this study, we used $Cu_2In_3$, CuGa and $Cu_2Se$ sputter targets for the deposition of a precursor. The precursor deposited by sputtering was selenized in Se vapor. The precursor layer deposited by the co-sputtering of $Cu_2In_3$, CuGa and $Cu_2Se$ showed a uniform distribution of Cu, In, Ga, and Se throughout the layer with Cu, In, CuIn, CuGa and $Cu_2Se$ phases. After selenization at $550^{\circ}C$ for 30 min, the CIGS film showed a double-layer microstructure with a large-grained top layer and a small-grained bottom layer. In the AES depth profile, In was found to have accumulated near the surface while Cu had accumulated in the middle of the CIGS film. By adding a Cu-In-Ga interlayer between the co-sputtered precursor layer and the Mo film and adding a thin $Cu_2Se$ layer onto the co-sputtered precursor layer, large CIGS grains throughout the film were produced. However, the Cu accumulated in the middle of CIGS film in this case as well. By supplying In, Ga and Se to the CIGS film, a uniform distribution of Cu, In, Ga and Se was achieved in the middle of the CIGS film.

• Journal of the Korean Vacuum Society
• /
• v.14 no.4
• /
• pp.215-221
• /
• 2005

Thermoelectric bismuth telluride thin films were prepared on $SiO_{2}$/Si substrate with co-sputtering of bismuth and tellurium targets. The effects of deposition temperature on surface morphology, crystallinity and electrical transport properties were investigated. Hexagonal crystallites were clearly visible at the surface of films deposited above $290 ^{\circ}C$. Change of dominant phase from rhombohedral $Bi_2Te_3$ to hexagonal BiTe was confirmed with X-ray diffraction analysis. The deviation from stoichiometric composition at high deposition temperature resulted in the change of structural and electrical characteristics. Seebeck coefficients of all samples have negative value, indicating the prepared $Bi_XTe_Y$ films are n-type thermoelectric. Optimum of Seebeck coefficient and power factor were obtained at the deposition temperature of $225 \^{circ}$C (about -55 $\mu$V/K and $3\times10^{-4}$ W/$k^{2}$m, respectively). Deterioration of thermoelectric properties at higher temperature.

• Journal of information and communication convergence engineering
• /
• v.1 no.3
• /
• pp.129-132
• /
• 2003

In this paper, cobalt (Co)-electrode FBAR devices fabricated on seven-layered Bragg Reflectors are presented along with their resonance characteristics. ZnO films are used as the resonating material in FBAR devices where the Co electrode is 3000${\AA}$ thick. All processes are preformed in an RF magnetron sputtering system. As a result of characterization, the resonance characteristics are observed to depend strongly on the quality of ZnO film and Bragg Reflectors. In addition, the FBAR devices with W/$SiO_2$ reflectors show good resonance characteristics in term of return loss and quality-factor (Q-factor).