• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.54-56
• /
• 2005

Ultrasonic soldering using of Si-wafer to FR-4 PCB atroom temperature was investigated. Sn3.5Ag foil rolled $100{\mu}m$ was used for solder. The UBM of Si-die was Cu/ Ni/ Al from top to bottom and its thickness was $0.4{\mu}m$, $0.4{\mu}m$, $0.3{\mu}m$ respectively. Pad on FR-4 PCB comprised of Au/ Ni/ Cu from top to bottom and its thickness was $0.05{\mu}m$, $5{\mu}m$, $18{\mu}m$ respectively. The ultrasonic soldering time was changed from 0.5sec to 3.0sec and its power 1400W. As experimental result, reliable bond joint by ultrasonic at room temperature was obtained. The shear strength increased with soldering time up to 2.5 sec. That means at 2.5sec, the shear strength showed maximum rate of 65.23N. The strength decreased to 33.90N at 3.0 sec because the cracks generated along the intermetallic compound between Si-wafer and Sn-3.5mass%Ag solder. intermetallic compound produced by ultrasonic between the solder and the Si-die was $(Cu, Ni)_{6}Sn_{5}$ and the intermetallic compound between solder and pad on FR-4 was $(Ni, Cu)_{3}Sn_{4}$.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.236-241
• /
• 2011

Polysilazane and silazane-based precursor films were deposited on stacked TiN/Ti/TEOS/Si-substrate by spin-coating, then annealed at $150{\sim}400^{\circ}C$, integrated further to form the top electrode and pad, and finally characterized. The precursor solutions were composed of 20% perhydro-polysilazane ($SiH_2NH$)n, and 20% hydropolymethyl silazane ($SiHCH_3NH$)n in dibutyl ether. Annealing of the precursor films led to the compositional change of the two chemicals into silicon (di)oxides, which was confirmed by Fourier transform infrared spectroscopy (FTIR) spectra. It is thought that the different results that were obtained originated from the fact that the two precursors, despite having the same synthetic route and annealing conditions, had different chemical properties. Electrical measurement indicated that under 0.6MV/cm, a larger capacitance of $2.776{\times}10^{-11}$ F and a lower leakage current of 0.4 pA were obtained from the polysilazane-based dielectric films, as compared to $9.457{\times}10^{-12}$ F and 2.4 pA from the silazane-based film, thus producing a higher dielectric constant of 5.48 compared to 3.96. FTIR indicated that these superior electrical properties are directly correlated to the amount of Si-O bonds and the improved chemical bonding structures of the spin-on dielectric films, which were derived from a precursor without C. The chemical properties of the precursor films affected both the formation and the electrical properties of the spin-on dielectric film.

• 한국재료학회지
• /
• 제5권8호
• /
• pp.929-935
• /
• 1995

구동 IC를 유리기판 위의 Al패드 전극에 연결하는 LCD(Liquid Crystal Display) 모듈을 실장하는 Chip On Glass (COG) 기술을 개발하기 위하여 기존에 잘 알려진 기술 가운데 실제로 적용 가능성이 가장 유망한 이방성 도전 접착제 (ACA, Anisotropic Conductive Adhesives)를 사용한 공정에 대하여 조사하였다. ACA 공정은 본딩 부분에 ACA 수지를 균일하게 분포시키는 공정과 자외선을 조사하여 수지를 경화하여 칩을 실장하는 공정의 2단계로 진행하였다. 칩에 가해준 하중은 2-15kg이었고 칩의 예열 온도는 12$0^{\circ}C$이었다. 이방성 도전체는 Au 또는 Ni이 표면 피막 재료로 사용된 것을 사웅하였으며 전도성 입자의 갯수가 500, 1000, 2000, 4000개/$\textrm{mm}^2$이며 크기가 5, 7, 12$\mu\textrm{m}$이었다. ACA 처리의 결과 입자 크기가 5$\mu\textrm{m}$이고 입자 밀도는 4000개/$\textrm{mm}^2$일 경우가 대단히 낮은 접촉 저항 및 가장 안정된 본딩 특성을 나타냈었다.

• 마이크로전자및패키징학회지
• /
• 제19권4호
• /
• pp.57-64
• /
• 2012

표면처리에 따른 Sn-1.2Ag-0.7Cu-0.4In 솔더범프의 접합 강도 평가를 위하여 전단 속도 및 열처리 시간에 따른 볼 전단강도 시험을 실시하였다. 전반적으로, 전단속도가 증가함에 따라 전단강도는 증가하였지만 인성은 감소하는 경향을 나타내었다. 파괴모드 관찰 결과, 전단 속도가 증가함에 따라 파괴모드의 경우, ENIG(electroless nickel immersion gold) 처리는 취성파괴가 대부분 지배적으로 존재하였고, OSP(organic solderability preservative) 처리는 pad open이 주로 발생하였다. 또한, 500 mm/s의 고속전단시험에서는 열처리 시간이 증가함에 따라 표면처리별 전단강도와 인성 값 모두 감소하는 경향을 보였다. ENIG 표면처리가 OSP 표면처리 보다 좋은 접합강도 특성을 보이는 것은 솔더범프 계면의 금속간화합물의 물성 및 두께와 밀접한 연관이 있는 것으로 판단된다.

• 마이크로전자및패키징학회지
• /
• 제29권3호
• /
• pp.25-29
• /
• 2022

최근 전자 패키징 기술의 중요성이 대두되며, 칩들을 평면 외 방향으로 쌓는 이종 집적 기술이 패키징 분야에 적용되고 있다. 이 중 2.5D 집적 기술은 실리콘 관통 전극를 포함한 인터포저를 이용하여 칩들을 적층하는 기술로, 이미 널리 사용되고 있다. 따라서 다양한 열공정을 거치고 기계적 하중을 받는 패키징 공정에서 이 인터포저의 기계적 신뢰성을 확보하는 것이 필요하다. 특히 여러 박막들이 증착되는 인터포저의 구조적 특징을 고려할 때, 소재들의 열팽창계수 차이에 기인하는 열응력은 신뢰성에 큰 영향을 끼칠 수 있다. 이에 본 논문에서는 실리콘 인터포저 위 와이어 본딩을 위한 금속 패드의 열응력에 대한 기계적 신뢰성을 평가하였다. 인터포저를 리플로우 온도로 가열 후 냉각 시 발생하는 금속 패드의 박리 현상을 관측하고, 그 메커니즘을 규명하였다. 또한 높은 냉각 속도와 시편 취급 중 발생하는 결함들이 박리 양상을 촉진시킴을 확인하였다.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2005년도 추계종합학술대회
• /
• pp.913-916
• /
• 2005

This paper describes the design, fabrication and characteristics of a piezoelectric valve using MCA(Multilayer ceramic actuator). The MCA valve, which has the buckling effect, consists of three separate structures; MCA, a valve actuator die and an a seat die. The design of the actuator die was done by FEM modeling and displacement measurement, respectively. The valve seat die with 6 trenches was made, and the actuator die, which is driven to MCA under optimized conditions, was also fabricated. After Si-wafer direct bonding between the seat die and the actuator die, MCA was also anodic bonded to the seat/actuator die structure. PDMS sealing pad was fabricated to minimize a leak-rate. It was also bonded to seat die and SUS package. The MCA valve shows a flow rate of 9.13 sccm at a supplied voltage of 100 V with a 50 % duty cycle, maximum non-linearity was 2.24 % FS and leak rate was $3.03{\times}10^{-8}pa$. $m^3/cm^2$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 반도체 재료 센서 박막재료 전자세라믹스
• /
• pp.129-132
• /
• 2004

This paper describes the design, fabrication and characteristics of a piezoelectric valve using MCA(Multilayer ceramic actuator). The MCA valve, which has the buckling effect, consists of three separate structures; MCA, a valve actuator die and an a seat die. The design of the actuator die was done by FEM modeling and displacement measurement, respectively. The valve seat die with 6 trenches was made, and the actuator die, which is driven to MCA under optimized conditions, was also fabricated. After Si-wafer direct bonding between the seat die and the actuator die, MCA was also anodic bonded to the seat/actuator die structure. PDMS sealing pad was fabricated to minimize a leak-rate. It was also bonded to seat die and SUS package. The MCA valve shows a flow rate of 9.13 sccm at a supplied voltage of 100 V with a 50 % duty cycle, maximum non-linearity was 2.24 % FS and leak rate was $3.03{\times}10^{-8}\;pa{\cdot}m^3/cm^2$. Therefore, the fabricated MCA valve is suitable for a variety of flow control equipment, a medical bio-system, automobile and air transportation industry.

• 한국전기전자재료학회논문지
• /
• 제17권5호
• /
• pp.515-520
• /
• 2004

We report on the development of a Piezoelectric valvc that is designed to have a high reliability for fluid control systems, such as mass flow control, transportation and chemical analysis. The valve was fabricated using a MCA(multilayer ceramic actuator), which has a low consumption power, high resolution and accurate control. The fabricated valve is composed of MCA, a valve actuator die and an seat die. The design of the actuator dic was done by FEM(finite element method) modeling, respectively. And, the valve seat die with 6 trenches was made. and the actuator die, which possible to optimize control to MCA, was fabricated. After Si-wafer direct bonding between the seat die and the actuator die, MCA was also anodic bonded to the scat/actuator die structure. PDMS(poly dimethylsiloxane) sealing pad was fabricated to minimize a leak-rate. It was also bonded to scat die and stainless steel package. The flow rate was 9.13 sccm at a supplied voltage of 100 V with a 50 % duty ratio and non-linearity was 2.24 % FS. From these results, the fabricated MCA valve is suitable for a variety of flow control equipments, a medical bio-system, semiconductor fabrication process, automobile and air transportation industry with low cost, batch recess and mass production.

• Journal of Welding and Joining
• /
• 제31권3호
• /
• pp.84-88
• /
• 2013

These days embedded technology may be the most significant development in the electronics industry. The study focused on the development of active device embedding using flexible printed circuit in view of process and materials. The authors fabricated 30um thickness Si chip without any crack, chipping defects with a dicing before grinding process. In order to embed chips into flexible PCB, the chip pads on a chip are connected to bonding pad on flexible PCB using an ACF film. After packaging, all sample were tested by the O/S test and carried out the reliability test. All samples passed environmental reliability test. In the future, this technology will be applied to the wearable electronics and flexible display in the variety of electronics product.

• 센서학회지
• /
• 제13권3호
• /
• pp.230-235
• /
• 2004

This paper describes the design, fabrication and characteristics of a piezoelectric valve using MCA(Multilayer ceramic actuator). The MCA valve, which has the buckling effect, consists of three separate structures; MCA, a valve actuator die and an a seat die. The design of the actuator die was done by FEM modeling and displacement measurement, respectively. The valve seat die with 6 trenches was made, and the actuator die, which is driven to MCA under optimized conditions, was also fabricated. After Si-wafer direct bonding between the seat die and the actuator die, MCA was also anodic bonded to the seat/actuator die structure. PDMS sealing pad was fabricated to minimize a leak-rate. It was also bonded to seat die and SUS package. The MCA valve shows a flow rate of 9.13 seem at a supplied voltage of 100 V with a 50% duty cycle, maximum non-linearity was 2.24% FS and leak rate was $3.03{\times}10^{-8}pa{\codt}m^{3}/cm^{2}$. Therefore, the fabricated MCA valve is suitable for a variety of flow control equipment, a medical bio-system, automobile and air transportation industry.