Paradigm shift to 3-D chip stacking in electronic packaging has induced a lot of integration challenges due to the reduction in wafer thickness and pitch size. This study presents a hybrid bonding technology by self-alignment effect in order to improve the flip chip bonding accuracy with ultra-thin wafer. Optimization of Cu pillar bump formation and evaluation of various factors on self-alignment effect was performed. As a result, highly-improved bonding accuracy of thin wafer with a $50{\mu}m$ of thickness was achieved without solder bridging or bump misalignment by applying reflow process after thermo-compression bonding process. Reflow process caused the inherently-misaligned micro-bump to be aligned due to the interface tension between Si die and solder bump. Control of solder bump volume with respect to the chip dimension was the critical factor for self-alignment effect. This study indicated that bump design for 3D packaging could be tuned for the improvement of micro-bonding quality.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.3
• /
• pp.31-37
• /
• 2009

Cu-Cu thermo-compression bonding process was successfully developed as functions of the $N_2+H_2$ forming gas annealing conditions before and after bonding step in order to find the low temperature bonding conditions of 3-D integrated technology where the quantitative interfacial adhesion energy was measured by 4-point bending test. While the pre-annealing with $N_2+H_2$ gas below $200^{\circ}C$ is not effective to improve the interfacial adhesion energy at bonding temperature of $300^{\circ}C$, the interfacial adhesion energy increased over 3 times due to post-annealing over $250^{\circ}C$ after bonding at $300^{\circ}C$, which is ascribed to the effective removal of native surface oxide after post-annealing treatment.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2010.10a
• /
• pp.726-729
• /
• 2010

Copper Pillar Tin Bump (CPTB) was investigated for high density chip interconnect technology development, which was prepared by electroplating and electro-less plating methods. Copper pillar tin bumps that have $100{\mu}m$ pitch were introduced with fabrication process using a KM-1250 dry film photoresist (DFR), with copper electroplating for Copper Pillar Bump (CPB) formation firstly, and then tin electro-less plating on it for control oxidation. Electric resistivity and mechanical shear strength measurements were introduced to characterize the oxidation effects and bonding process as a function of thermo-compression. Electrical resistivity increased with increasing oxidation thickness, and shear strength had maximum value with $330^{\circ}C$ and 500 N thermo-compression process. Through the simulation work, it was proved that when the CPTB decreased in its size, it was largely affected by the copper oxidation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.12
• /
• pp.919-923
• /
• 2010

Copper pillar tin bump (CPTB) was developed for high density chip interconnect technology. Copper pillar tin bumps that have $100{\mu}m$ pitch were introduced with fabrication process using a KM -1250 dry film photoresist (DFR), copper electroplating method and Sn electro-less plating method. Mechanical shear strength measurements were introduced to characterize the bonding process as a function of thermo-compression. Shear strength has maximum value with $330^{\circ}C$ and 500 N thenno-compression process. Through the simulation work, it was proved that when the copper pillar tin bump decreased in its size, it was largely affected by the copper oxidation.

• Korean Journal of Materials Research
• /
• v.18 no.4
• /
• pp.204-210
• /
• 2008

$1.5\;{\mu}m$-thick copper films deposited on silicon wafers were successfully bonded at $415^{\circ}C$/25 kN for 40 minutes in a thermo-compression bonding method that did not involve a pre-cleaning or pre-annealing process. The original copper bonding interface disappeared and showed a homogeneous microstructure with few voids at the original bonding interface. Quantitative interfacial adhesion energies were greater than $10.4\;J/m^2$ as measured via a four-point bending test. Post-bonding annealing at a temperature that was less than $300^{\circ}C$ had only a slight effect on the bonding energy, whereas an oxygen environment significantly deteriorated the bonding energy over $400^{\circ}C$. This was most likely due to the fast growth of brittle interfacial oxides. Therefore, the annealing environment and temperature conditions greatly affect the interfacial bonding energy and reliability in Cu-Cu bonded wafer stacks.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.16 no.4
• /
• pp.759-764
• /
• 2012

Copper Pillar Tin Bump (CPTB) was investigated for high density chip interconnect technology development, which was prepared by electroplating and electro-less plating methods. Copper pillar tin bumps that have $100{\mu}m$ pitch were introduced with fabrication process using a KM-1250 dry film photoresist (DFR), with copper electroplating for Copper Pillar Bump (CPB) formation firstly, and then tin electro-less plating on it for control oxidation. Electric resistivity and mechanical shear strength measurements were introduced to characterize the oxidation effects and bonding process as a function of thermo-compression. Electrical resistivity increased with increasing oxidation thickness, and shear strength had maximum value with $330^{\circ}C$ and 500 N at thermo-compression process. Through the simulation work, it was proved that the CPTB decreased in its size of conduction area as time passes, however it was largely affected by the copper oxidation.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.4
• /
• pp.61-66
• /
• 2010

Cu-Cu thermo-compression bonding process was successfully developed as functions of the deposited Cu thickness and $Ar+H_2$ forming gas annealing conditions before and after bonding step in order to find the low temperature bonding conditions of 3-D integrated technology where the interfacial toughness was measured by 4-point bending test. Pre-annealing with $Ar+H_2$ gas at $300^{\circ}C$ is effective to achieve enough interfacial adhesion energy irrespective of Cu film thickness. Successful Cu-Cu bonding process achieved in this study results in delamination at $Ta/SiO_2$ interface rather than Cu/Cu interface.

• Transactions of the KSME C: Technology and Education
• /
• v.3 no.4
• /
• pp.265-271
• /
• 2015

The bonding process should be achieved in vacuum environment to avoid air bubble. In this study, we studied about pressure uniformity that became an issue in thermo compression bonding usually. Uniform press is realized by the method that use air spring and metal form spring. The concept of uniform press using air spring is removed except pressing direction in the press processing so angle between the vector of pressure surface and the pressure axis is parallel automatically. Air spring compensate the errors of machining and assembly. Metal form compensate the thermal deformation and flatness error.