• 한국전기전자재료학회논문지
• /
• 제26권1호
• /
• pp.44-48
• /
• 2013

Niobium oxide($Nb_2O_5$) films were deposited on p-type Si wafers at room temperature using in-line pulsed-DC magnetron sputtering system with various frequencies. The different duty ratios were obtained by varying the frequency of pulsed DC power from 100 to 300 kHz at the fixed reverse time of $1.5{\mu}s$. From the thickness of the sputtered $NbO_x$ films, it was possible to obtain much higher deposition rate in case of pulsed-DC sputtering than RF sputtering. However, the similar leakage currents and structural characteristics were obtained from the metal-insulator-semiconductor(MIS) structure fabricated with the $NbO_x$ films and the x-ray photoelectron spectroscopy(XPS) results in spite of the different deposition rates. From the experimental results, the $NbO_x$ films sputtered by pulsed-DC sputtering are expected to be used in the fabrication process instead of RF sputtering.

• 한국전기전자재료학회논문지
• /
• 제36권2호
• /
• pp.170-174
• /
• 2023

Nickel oxide is a nonstoichiometric transparent conductive oxide with p-type conductivity, a wide-band energy gap of 3.4~4.0 eV, and excellent chemical stability, making it a very important candidate as a material for bipolar devices. P-type conductivity in Transparent Conductive Oxides (TCO) is controlled by the oxygen vacancy concentration. During the TCO film deposition process, additional oxygen diffusing into the NiO structure causes the formation of Ni 3p ions and Ni vacancies. This eventually affects the hole concentration of the p-type oxide thin film. In this work, the surface morphology and the electrical characteristics were confirmed in accordance with the annealing atmosphere of the nickel oxide thin film.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.901-904
• /
• 2001

For the c-axis oriented epitaxial YBa$_2$Cu$_3$O$_{7-{\delta}}$ thin film on r-cut sapphire substrate it is necessary to deposit buffer layers. The CeO$_2$buffer layer was deposited on sapphire substrate using RF magnetron sputtering system. We investigated XRD pattern of CeO$_2$thin films at various sputtering conditions such as sputtering gas ratio, sputtering power, target to substrate distance, sputtering pressure and substrate temperature. The optimum condition was 15 mTorr with deposition pressure, 1:1.2 with $O_2$and Ar ratio and 9cm with target to substrate distance. The CeO$_2$(200) peak was notable for a deposition temperature above 75$0^{\circ}C$. The YBa$_2$Cu$_3$O$_{7-{\delta}}$ was deposited on CeO$_2$buffered r-cut sapphire substrate using pulsed laser ablation. The YBa$_2$Cu$_3$O$_{7-{\delta}}$CeO$_2$(200)/A1$_2$O$_3$thin film was exhibited a critical temperature of 89K.xhibited a critical temperature of 89K.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제16권2호
• /
• pp.210-214
• /
• 2016

In this paper, the decrease in the contact resistance of Ni germanide/Ge contact was studied as a function of the thickness of the antimony (Sb) interlayer for high performance Ge MOSFETs. Sb layers with various thickness of 2, 5, 8 and 12 nm were deposited by RF-Magnetron sputter on n-type Ge on Si wafers, followed by in situ deposition of 15nm-thick Ni film. The contact resistance of samples with the Sb interlayer was lower than that of the reference sample without the Sb interlayer. We found that the Sb interlayer can lower the contact resistance of Ni germanide/Ge contact but the reduction of contact resistance becomes saturated as the Sb interlayer thickness increases. The proposed method is useful for high performance n-channel Ge MOSFETs.

• 한국세라믹학회지
• /
• 제46권1호
• /
• pp.10-15
• /
• 2009

We have fabricated silicon-rich silica thin films via RF magnetron sputtering using a SiO target. Thickness evolution and microstructure change of such $SiO_x$ (1$SiO_x$ thin films turned out to be mainly responsible for the increase of refractive index.

• 한국전기전자재료학회논문지
• /
• 제26권4호
• /
• pp.321-324
• /
• 2013

In this study, The RF magnetron sputter and evaporator was on glass substrates 30 mm ${\times}$ 30 mm OMO multilayer thin film structure is applied to the low-e. Structural and optical properties, a thin film was produced, the variable was placed into a variable deposition time of the oxide layer. According to the XRD measurement results there is no peak that satisfies the Bragg's law ($2dsin{\theta}=n{\lambda}$) which confirmed that it is an amorphous structure. RMS value of the results of the AFM measurement, has a roughness of less than 2 nm. transmittance measurements results, visible light region an average 80%, IR region 40% showed.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권2호
• /
• pp.1622-1624
• /
• 2007

In order to realize effective p-type doping in ZnO thin films, ZnO films were deposited on P-doped Silayers by RF-magnetron sputter deposition technique and annealed at various temperatures. The result indicated that ZnO film annealed at $700^{\circ}C$ showed p-type conduction with a high carrier concentration in the order of $10^{19}\;cm^{-3}$.

• 한국전기전자재료학회논문지
• /
• 제27권2호
• /
• pp.71-75
• /
• 2014

To observe the optical characteristic of oxide semiconductor depending on the degree of bonding structures, SiOC, ZnO and IGZO were prepared by the RF magnetron sputter system and chemical vapor deposition. Generally, crystal ZnO, amorphous SiOC and IGZO changed the optical characteristics in according to the electro-chemical behavior due to the oxygen vacancy at an interface between different groups. Transmittance of SiOC and IGZO with amorphous structures was higher than that of ZnO with crystal structure, because of lowering the carrier concentration due to the recombination of electron and holes carriers as oxygen vacancies. Besides, the energy gap of amorphous SiOC and IGZO was higher than the energy gap of crystal ZnO. The diffusion mobility of holes is higher than the drift mobility of electrons.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제45회 하계 정기학술대회 초록집
• /
• pp.306-306
• /
• 2013

p-type Si(100)기판위에 Al2O3 박막을 증착하고 Si/SiO2 박막을 연속 증착하여 태양전지를 제작하였다. Si/SiO2 박막을 연속으로 증착하면 양자 구속이 일어나고 이로 인한 유효밴드 갭이 증가하게 되고, tunnel effect와 계면에서의 passivation 효과를 기대할 수 있다. 이런 효과들을 이용하여 고효율 태양전지를 기대 할 수 있다. 본 연구에서는 Remote Plasma Atomic Layer Deposition(RPALD)를 이용하여 Al2O3를 증착하였고 RF-Magnetron Sputter와 e-beam Evaporator 장비를 이용하여 Si/SiO2을 증착하였다. 전극으로는 Ti/Ag와 Al을 이용하였다. Solar simulator 장비를 이용하여 cell의 전기적 특성 평가를 평가하였고(Fig. 1) QE 측정장비를 통해 파장대의 따른 광학적 측정을 하였다(Fig. 2). ellipsometer 장비와 ${\alpha}$-step 장비로 박막과 전극의 두께를 측정하였고 4-point prove 장비를 이용하여 면저항, 저항율을 측정 평가하였다. 또한 I-V, C-V 측정 결과 터널링 현상이 일어나는 것을 확인 하였으며, Si/SiO2 다중 박막을 연속 증착 할수록 cell 효율이 더 좋게 나온다는 것을 확인하였다.

• Current Photovoltaic Research
• /
• 제3권3호
• /
• pp.101-105
• /
• 2015

ZnO is gathering great interest for large square optoelectrical devices of flat panel display (FHD) and solar cell as a transparent conductive oxide (TCO). Herewith, Mg and IIIA (Al, In) co-doped ZnO films were prepared on SLG substrate using RF magnetron sputtering system. The effect of variation of atomic weight % of Mg and ZnO have been investigated. The atomic weight % Al and In are of 3% and kept constant throughout. The numbers of samples were prepared according to their different contents, which are $M_{3%}AZO_{94%}$, $M_{4%}AZO_{93%}-(MAZO)$ and $M_{3%}IZO_{94%}$, $M_{4%}IZO_{93%}-(MIZO)$ respectively. A RF power of 225 W and working pressure of 6 m Torr was used for the deposition at $300^{\circ}C$. All of the two thin film show good uniformity in field emission scanning electron microscopy image. $M_{3%}AZO_{94%}$ thin film shows overall better performance among the all. The film shows the best lowest resistivity, carrier concentration, mobility and Sheet resistance and is found to be are of $8.16{\times}10^{-4}{\Omega}cm$, $4.372{\times}10^{20}/cm^3$, $17.5cm^2/vs$ and $8.9{\Omega}/sq$ respectively. Also $M_{3%}AZO_{94%}$ thin film shows the relatively high optical band gap energy of 3.7 eV with high transmittance more than 80% in visible region required for the better solar cell performance.