Transparent amorphous In-Si-O (ISO)/Ag/In-Si-O (ISO) has been reported for low emissivity (low-e) applications. Effective Si doping into the $In_2O_3$ matrix led to a completely amorphous ISO film as well as a low resistivity and a high optical transmittance. The optical and electrical performances were examined by measuring transmittance with a UV-VIS spectrophotometer and resistivity with a Hall effect measurement. Consequently, low-e glass with ISO/Ag/ISO showed a high transparency in the visible region and low emissivity in the infrared region, indicating that ISO is a promising amorphous transparent electrode for low-e glass.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.1
• /
• pp.13-15
• /
• 2017

Low emissivity glass for high transparency in the visible range and low emissivity in the IR (infrared) range was fabricated and investigated. The multilayers were have been fabricated, and consisted of two outer oxide layers and a middle layer of Ag as a metal layer. Oxide layers were formed by rf sputtering and metal layers were formed using by an evaporator at room temperature. SiInZnO (SIZO) film was used as an oxide layer. The OMO (oxide-metaloxide) structures of SIZO/Ag/SIZO were analyzed by using transmittance, AFM (atomic force microscopye), and XRD (X-ray diffraction). The OMO multilayer structure was designed to investigate the effect of Ag layer thickness on the optical property of the OMO structure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.1
• /
• pp.105-112
• /
• 2018

This paper proposes a method for fabricating heatable glass using the conduction characteristics of metal thin films deposited on the surface of Low-e(Low emissivity) glass. The heating value of Low-e glass depends on the Joule heat caused by Low-e glass sheet resistance. Hence, its prediction and design are possible by measuring the sheet resistance of the material. In this study, silver electrodes were placed at 50 mm intervals on a soft Low-e glass sample with a low emissivity layer of 11 nm. This study measured the sheet resistance using a 4-point probe, predicted the power consumption and heating value of the Low-e glass, and confirmed the heating performance through fabrication and experience. There are two conventional methods for manufacturing heatable glass. One is a method of inserting nichrome heating wire into normal glass, and the other is a method of depositing a conductive transparent thin film on normal glass. The method of inserting nichrome heating wire is excellent in terms of the heating performance, but it damages the transparency of the glass. The method for depositing a conductive transparent thin film is good in terms of transparency, but its practicality is low because of its complicated process. This paper proposes a method for manufacturing heatable glass with the desired heating performance using Low-e glass, which is used mainly to improve the insulation performance of a building. That is by emitting a laser beam to the conductive metal film coated on the entire surface of the Low-e glass. The proposed method is superior in terms of transparency to the conventional method of inserting nichrome heating wire, and the manufacturing process is simpler than the method of depositing a conductive transparent thin film. In addition, the heat characteristics were compared according to the patterning of the surface thin film of the Low-e glass by an emitting laser and the laser output conditions suitable for Low-e glass.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.5
• /
• pp.347-350
• /
• 2013

By inserting a very thin metal layer of Ag between two outer oxide layers of amorphous silicon indium zinc oxide (SIZO), we fabricated a highly transparent SIZO/Ag/SIZO multilayer on a glass substrate. In order to find the optimized thickness of Ag layers, we investigated the variation of optical properties depending on Ag thickness. It was found that the transition of Ag layer from island formation to a continuous film occurred at a critical thickness. Continuity of the Ag film is very important for optical properties in SIZO/Ag/SIZO multilayer. With about 15 nm thick Ag layer, the multilayer showed a high optical transmittance of 80% at 550 nm and low emissivity in IR.

• Korean Journal of Materials Research
• /
• v.23 no.4
• /
• pp.215-218
• /
• 2013

Vanadium dioxide ($VO_2$) is an attractive material for smart window applications where the transmittance of light can be automatically modulated from a transparent state to an opaque state at the critical temperature of ${\sim}68^{\circ}C$. Meanwhile, F : $SnO_2$ (F-doped $SnO_2$, FTO) glass is a transparent conductive oxide material that is widely used in solar-energy-related applications because of its excellent optical and electrical properties. Relatively high transmittance and low emissivity have been obtained for FTO-coated glasses. Tunable transmittance corresponding to ambient temperature and low emissivity can be expected from $VO_2$ films deposited onto FTO glasses. In this study, FTO glasses were applied for the deposition of $VO_2$ thin films by pulsed DC magnetron sputtering. $VO_2$ thin films were also deposited on a Pyrex substrate for comparison. To decrease the phase transition temperature of $VO_2$, tungsten-doped $VO_2$ films were also deposited onto FTO glasses. The visible transmittance of $VO_2$/FTO was higher than that of $VO_2$/pyrex due to the increased crystallinity of the $VO_2$ thin film deposited on FTO and decreased interface reflection. Although the solar transmittance modulation of $VO_2$/FTO was lower than that of $VO_2$/pyrex, room temperature solar transmittance of $VO_2$/FTO was lower than that of $VO_2$/pyrex, which is advantageous for reflecting solar heat energy in summer.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.1
• /
• pp.6-10
• /
• 2007

For low-emissivity application on window glass, coalescence of thin film silver islands is crucial for high transmittance in the visible and high reflectance in the infrared. It is well known that the underlayer affects the growth mode. In this work, the effect of the underlayer on the growth of silver films deposited by filtered cathodic vacuum arc is discussed. While a nominal 0.1 nm niobium underlayer has promoted the coalescence of silver islands, a 0.2 nm layer did not show these features. From a thermodynamic approach, Nb seeding less one monolayer is considered to reduce the surface energy between the silver atoms and $Nb/TiO_2$ surface, resulting the change of its growth from 3D islands to 2D-layer modes. If the seed layer exceeds one monolayer, however, a rougher surface is formed because the surface energy of Nb itself is superior to that of $Nb-TiO_2$. The onset of silver layer on the roughened Nb surface is required more silver.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.321-324
• /
• 2013

In this study, The RF magnetron sputter and evaporator was on glass substrates 30 mm ${\times}$ 30 mm OMO multilayer thin film structure is applied to the low-e. Structural and optical properties, a thin film was produced, the variable was placed into a variable deposition time of the oxide layer. According to the XRD measurement results there is no peak that satisfies the Bragg's law ($2dsin{\theta}=n{\lambda}$) which confirmed that it is an amorphous structure. RMS value of the results of the AFM measurement, has a roughness of less than 2 nm. transmittance measurements results, visible light region an average 80%, IR region 40% showed.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.3
• /
• pp.134-138
• /
• 2015

Ag intermediated $TiO_2$ films were deposited by RF and DC magnetron sputtering and then vacuum annealed at 100, 200 and $300^{\circ}C$ for 30 minutes to investigate the effect of annealing temperature on the structural and optical properties of the films. For all depositions, the thickness of the $TiO_2$ and Ag films were kept constant at 24 and 15 nm by controlling the deposition time. As-deposited $TiO_2/Ag/TiO_2$ trilayer films have a weak crystalline and an optical reflectance in a near infrared wavelength region of 77.8%, while the films annealed at $300^{\circ}C$ show the polycrystalline structure and an increased mean optical reflectance of 80.4%. From the experimental results, it can be concluded that increasing the annealing temperature enhanced the structural and optical properties of the $TiO_2/Ag/TiO_2$ films.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.6
• /
• pp.451-456
• /
• 2023

Transparent conducting films having a three layered structure of ZnO/Cu/ZnO (ZCZ) were deposited onto the glass substrates by using RF and DC magnetron sputtering at room temperature. The emissivity and opto-electrical properties of the films were investigated with a varying thickness(5, 10, 15 nm) of the Cu interlayer. With increasing the Cu thickness to 15 nm, the films showed a enhanced electrical properties. Although ZnO 30/Cu 15/ZnO 30 nm film shows a lower resistivity of 5.2×10^-5 Ωcm, it's visible transmittance is deteriorated by increased optical absorbtion of the films. In addition, X-ray diffraction patterns indicated that the insertion of Cu interlayer improve the grain size of ZnO films, which is favor for the electrical and optical properties of transparent conducting films. From the observed low emissivity of the films, it is concluded that the ZCZ thin films with optimal thickness of Cu interlayer can be applied effectively for the car's window coating materials.

• Korean Journal of Optics and Photonics
• /
• v.13 no.4
• /
• pp.363-369
• /
• 2002

We have designed conductive transparent filters using a low-emissivity coating such as [dielectric|Ag|dielectric] for display applications. The design is the repetition of [$TiO_{2}$|Ti|Ag |$TiO_{2}$] to increase the transmittance in the visible and decrease the transmittance in the near IR. The conductive transparent filters are deposited by a radio frequency(RF) magnetron sputtering system. The optical, structural and electrical properties of the filters were investigated and the optical spectra are compared with simulated spectra. The thickness of the deposited Ag films is above 13 ㎚ to increase the conductivity and that of $TiO_{2}$ films is 24 ㎚ to increase the transmittance in the visible range. Ti blockers are employed to prevent the Ag films from being oxidized by an oxygen gas during the reactive sputtering process. Also, it is shown that the thicker Ti film is necessary as the period increases. Finally, a filter with repetition of the basic structure three times shows the better cut-off near infrared(NIR) and the sheet resistance as low as 2Ω/□ which is enough to shield an unnecessary electromagnetic waves for a display panel.