• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.6
• /
• pp.575-579
• /
• 2008

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ of by RF magnetron sputtering. Target was ZnO ceramic mixed with 2 wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-3}$, mobilities from 0.194 to $2.3\;cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4\;{\Omega}cm$. p-type sample has density of $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. XPS spectra show that Ols has O-O and Zn-O structures and Al2p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.408-409
• /
• 2007

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ by RF magnetron sputtering. Target was ZnO ceramic mixed with 2wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}\;to\;4.04{\times}10^{18}cm^{-3}$, mobilities from 0.194 to $2.3cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4{\Omega}cm$. P-type sample has density of $5.40cm^{-3}$ which is smaller than theoretically calculated value of $5.67cm^{-3}$. XPS spectra show that O1s has O-O and Zn-O structures and A12p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.14 no.4
• /
• pp.478-483
• /
• 2014

We propose a new method which can extract the information about the electronic traps in the semi-insulating GaN buffer of AlGaN/GaN heterostructure field-effect transistors (HFETs) using a simple test structure. The proposed method has a merit in the easiness of fabricating the test structure. Moreover, the electric fields inside the test structure are very similar to those inside the actual transistor, so that we can extract the information of bulk traps which directly affect the current collapse behaviors of AlGaN/GaN HEFTs. By applying the proposed method to the GaN buffer structures with various unintentionally doped GaN channel thicknesses, we conclude that the incorporated carbon into the GaN back barrier layer is the dominant origin of the bulk trap which affects the current collapse behaviors of AlGaN/GaN HEFTs.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.1
• /
• pp.6-10
• /
• 2009

In this paper, a selective area growth (SAG) of a GaN/AlGaN double heterostructure (DH) has been performed on r-plane sapphire substrate by using the mixed-source hydride vapor phase epitaxy (HVPE) with multi-sliding boat system. The SAG-GaN/AlGaN DH consists of GaN buffer layer, Te-doped AlGaN n-cladding layer, GaN active layer, Mg-doped AlGaN p-cladding layer, and Mg-doped GaN p-capping layer. The electroluminescence (EL) characteristics show an emission peak of wavelength, 439 nm with a full width at half maximum (FWHM) of approximately 0.64 eV at 20 mA. The I-V measurements show that the turn-on voltage of the SAG-GaN/AlGaN DH is 3.4 V at room temperature. We found that the mixed-source HVPE method with a multi-sliding boat system was one of promising growth methods for III-Nitride LEDs.

• Journal of Sensor Science and Technology
• /
• v.23 no.6
• /
• pp.420-424
• /
• 2014

Aluminum-scandium nitride ($Al_{1-x}Sc_xN$) thin films with a TiN buffer layer have been fabricated on SUS430 substrate by RF reactive magnetron sputtering at room temperature under 50% $N_2$/Ar. The effect of Sc-doping on the structure and piezoelectric properties of AlN films has been investigated using SEM, XRD, surface profiler and pressure-voltage measurements. The as-deposited AlN films showed polycrystalline phase, and the Sc-doped AlN film, the peak of AlN (002) plane and the crystallinity became very strong. With Sc-doping, the crystal size of AlN film was grown from ~20 nm to ~100 nm. The output signal voltage of AlN sensor showed a linear behavior between 15~65 mV, and output signal voltage of Sc-doped AlN sensor was increased over 7 times. The pressure-sensing sensitivity of AlN film was calculated about 10.6mV/MPa, and $Al_{0.88}Sc_{0.12}N$ film was calculated about 76 mV/MPa.

• Korean Journal of Materials Research
• /
• v.12 no.6
• /
• pp.431-435
• /
• 2002

The dark current and photocurrent(PC) spectrum of Mg-doped GaN thin film were investigated with various bias voltages and temperatures. At high temperature and small bias, the dark current is dominated by holes thermally activated from an acceptor level Al located at about 0.16 eV above the valence band maximum $(E_v)$, The PC peak originates from the electron transition from deep level A2 located at about 0.34 eV above the $E_v$ to the conduction band minimum $(E_ C)$. However, at a large bias voltage, holes thermally activated from A2 to Al experience the field-in-duces tunneling to form one-dimensional defect band at Al, which determines the dark current. The PC peak associated with the transition from Al to $E_ C$ is also observed at large bias voltages owing to the extended recombination lifetime of holes by the tunneling. In the near infrared region, a strong PC peak at 1.20 eV appears due to the hole transition from deep donor/acceptor level to the valence band.

• Journal of Magnetics
• /
• v.16 no.4
• /
• pp.332-336
• /
• 2011

We studied the effect on the electronic and magnetic properties of the N defect in clean and Cu-doped wurtzite III-nitrides by using the first-principles calculations. When it is doped two Cu atoms in the nearest neighboring sites, the system of AlN, GaN, or InN with the N vacancy is energetically more favorable than that without the N vacancy site. When the Cu concentration increases, the total magnetic moment of a supercell becomes small. The ferromagnetism of Cu atom is very low due to the weak 3d-3d coupling. It is noticeable that the spin-exchange interaction between the Cu-3d and N defect states is important.

• Journal of the Korean Ceramic Society
• /
• v.27 no.6
• /
• pp.799-807
• /
• 1990

In this study, effects of oxide additives on mechanical properties and microstructure of A1N and A1N polytype ceramics were investigated. Fine A1N powder was synthesized by nitriding alumiuim hydroxide prepared from Al-isopropoxide, at 1350$^{\circ}C$ for 10h in N2 atmosphere. By adding 3w/o Y2O3, 0.56w/o CaO, and 10w/o SiO2 to AlN powder, AlN and AlN polytype ceramics were prepared by hot-pressing under the pressure of 30 MPa at 1800$^{\circ}C$ for 1h. AlN ceramics with no additives formed considerable amount of AlON phase, while AlN ceramics doped with Y2O3 or CaO decreased AlON phase and formed Y-Al or Ca-Al oxide compound. AlN＋10w/o SiO2(＋3w/o Y2O3) composition produced AlON and AlN polytype compound having 21R as a major phase. Room temperature flexural strength of AlN ceramics with no additive was 246MPa, and room temperature flexural strength and critical temperature difference by thermal shock(ΔTc) of AlN ceramics dooped with Y2O3 or CaO were 532MPa/340$^{\circ}C$ and 423MPa/300$^{\circ}C$, respectively. Y2O3 and CaO used as sintering agent played roles of densification and oxygen removal of AlN ceramics, and affected grain growth/grain morphologies of AlN ceramics.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.191-191
• /
• 2003

가시광선영역에서 높은 광학적 투명도를 갖는 n-type 반도체인 ZnO 박막은 넓은 범위에서 응용되고 있다. 현재 ZnO 박막의 특성 향상을 위하여 여러 원소(Al, Ga)의 도핑을 시도하고 있다. 특히 Al-doped ZnO 박막은 sol-gel dip coating에 의해서도 높은 전기전도도와 투과율로 활발히 연구되고 있다 본 논문에서는 여러 도핑농도를 갖는 Al-doped ZnO 박막이 sol-gel dip coating법에 의해 준비되었다. Al-doped ZnO 박막은 zinc acetate [Zn($CH_3$COO$_2$)ㆍ2$H_2O$] powder 와 여러 도핑농도를 갖는 aluminum nitrate (Al(NO$_3$)$_3$ㆍ9$H_2O$) powder를 알코올에 용해하여 $H_2O$, Ethylene glycol, Ethylene diamine 등을 첨가하여 제조하였다 XRD와 SEM (Scanning electron microscope)이 막의 상형성 분석을 위해 이용되었으며, 가시광선 영역 투과율(UV/VIS spectrophotometer)과 표면전기저항(four point probe)이 주요 특성으로 분석되었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.442-443
• /
• 2007

Al-N co-doped ZnO films were fabricated on n-Si (100) and homo-buffer layers in the mixture of oxygen and nitrogen at $450^{\circ}C$ by magnetron sputtering. Target was ZnO ceramic mixed with $2wt%Al_2O_3$. XRD spectra show that as-grown and $600^{\circ}C$ annealed films are prolonged along crystal c-axis. However they are not prolonged in (001) plane vertical to c-axix. The films annealed at $800^{\circ}C$ are not prolonged in any directions. Codoping makes ZnO films unidirectional variation. XPS show that Al content hardly varies and N escapes with increasing annealing temperature from $600^{\circ}C\;to\;800^{\circ}C$. The electric properties of as-grown films were tested by Hall Effect with Van der Pauw configuration show some of them to be p-type conduction.