• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.1057-1059
• /
• 2002

ZnO-Si-ZnO multi-layer thin films have been deposited by pulsed laser deposition (PLD). And then, the films have been annealed at $300^{\circ}C$ in oxygen ambient pressure. Electrical properties of the films were improved slightly than ZnO thin film without Si layer. Also, the optical and structural properties changed by Si layer in ZnO thin film. The optical and structural properties of Si-doped ZnO thin films were characterized by PL(Photoluminescence) and XRD(X-ray diffraction method) respectively. Electrical properties were measured by van der Pauw Hall measurements.

• Journal of Sensor Science and Technology
• /
• v.15 no.1
• /
• pp.65-70
• /
• 2006

Characteristics of thin-film NTC thermal sensors fabricated by micromachining technology were studied as a function of the thickness of membrane. The overall-structure of thermal sensor has a form of Au/Ti/NTC/$SiO_{X}$/(100)Si. NTC film of $Mn_{1.5}CoNi_{0.5}O_{4}$ with 0.5 mm in thickness was deposited on $SiO_{X}$ layer (1.2 mm) by PLD (pulsed laser deposition) and annealed at 873-1073 K in air for 1 hour. Au(200 nm)/Ti(100 nm) electrode was coated on NTC film by dc sputtering. By the results of microstructure, X-ray and NTC analysis, post-annealed NTC films at 973 K for 1 hour showed the best characteristics as NTC thermal sensing film. In order to reduce the thermal mass and thermal time constant of sensor, the sensing element was built-up on a thin membrane with the thickness of 20-65 mm. Sensors with thin sensing membrane showed the good detecting characteristics.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.14 no.5
• /
• pp.666-672
• /
• 2014

We have investigated the gate insulator effects on the electrical performance of p-type tin monoxide (SnO) thin-film transistors (TFTs). Various SnO TFTs are fabricated with different gate insulators of a thermal $SiO_2$, a plasma-enhanced chemical vapor deposition (PECVD) $SiO_x$, a $150^{\circ}C$-deposited PEVCD $SiO_x$, and a $300^{\circ}C$-deposited PECVD $SiO_x$. Among the devices, the one with the $150^{\circ}C$-deposited PEVCD $SiO_x$ exhibits the best electrical performance including a high field-effect mobility ($=4.86cm^2/Vs$), a small subthreshold swing (=0.7 V/decade), and a turn-on voltage around 0 (V). Based on the X-ray diffraction data and the localized-trap-states model, the reduced carrier concentration and the increased carrier mobility due to the small grain size of the SnO thin-film are considered as possible mechanisms, resulting in its high electrical performance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.304.1-304.1
• /
• 2014

Flat-panel displays have been growing as an essential everyday product in the current information/communication ages in the unprecedented speed. The forward-coming applications require light-weightness, higher speed, higher resolution, and lower power consumption, along with the relevant cost. Such specifications demand for a new concept-based materials and applications, unlike Si-based technologies, such as amorphous Si and polycrystalline Si thin film transistors. Since the introduction of the first concept on the oxide-based thin film transistors by Hosono et al., amorphous oxide thin film transistors have been gaining academic/industrial interest, owing to the facile synthesis and reproducible processing despite of a couple of shortcomings. The current work places its main emphasis on the binary oxides composed of ZnO and SnO2. RF sputtering was applied to the fabrication of amorphous oxide thin film devices, in the form of bottom-gated structures involving highly-doped Si wafers as gate materials and thermal oxide (SiO2) as gate dielectrics. The physical/chemical features were characterized using atomic force microscopy for surface morphology, spectroscopic ellipsometry for optical parameters, X-ray diffraction for crystallinity, and X-ray photoelectron spectroscopy for identification of chemical states. The combined characterizations on Zn-Sn-O thin films are discussed in comparison with the device performance based on thin film transistors involving Zn-Sn-O thin films as channel materials, with the aim to optimizing high-performance thin film transistors.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.6
• /
• pp.293-296
• /
• 2006

We studied homeotropic alignment effect for a nematic liquid crystal (NLC) on the $SiO_{x}$ thin film irradiated by the new ion beam method. $SiO_{x}$ thin films were deposited by plasma enhanced chemical vapor deposition (PECVD) and were treated by the DuoPIGatron ion source. A uniform liquid crystal alignment effect was achieved over 2100 eV ion beam energy. Tilt angle were about $90^{\circ}$ and were not affected by various ion beam energy.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.41-47
• /
• 2020

The effect of Co interlayer on the interfacial reliability of SiN_x/Co/Cu thin film structure for advanced Cu interconnects was systematically evaluated by using a double cantilever beam test. The interfacial adhesion energy of the SiN_x/Cu thin film structure was 0.90 J/㎡. This value of the SiN_x/Co/Cu thin film structure increased to 9.59 J/㎡.Measured interfacial adhesion energy of SiN_x/Co/Cu structure was around 10 times higher than SiN_x/Cu structure due to CoSi₂ reaction layer formation at SiN_x/Co interface, which was confirmed by X-ray photoelectron spectroscopy analysis. The interfacial adhesion energy of SiN_x/Co/Cu structure decreased sharply after post-annealing at 200℃ for 24 h due to Co oxidation at SiN_x/Co interface. Therefore, it is required to control the CoO and Co₃O₄ formation during the environmental storage of the SiN_x/Co/Cu thin film to achieve interfacial reliability for advanced Cu interconnections.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1322_1323
• /
• 2009

The $V_{1.85}W_{0.15}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were 38.11, with a dielectric loss of 1%, respectively. Also, the TCR values of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were about -3.45%/K.

• Korean Journal of Crystallography
• /
• v.6 no.2
• /
• pp.134-140
• /
• 1995

SAW properties of SiNx/ZnO bilayer thin film structure were analyzed. ZnO thin films were deposited by rf magnetron sputter using O2 gas as an oxidizer. Structure of ZnO thin films was affected by Ar/O2 ratio. At the gas ratio of Ar/O2=67/33, the standard deviation of X-ray rocking curve of (002) preferred ZnO thin film was 2.17 degree. This value is sufficient to use ZnO thin films as an acoustic element. SAW velocity of glass/SiNx(7000Å)/Al/ZnO(5μm) structure was max. 2.2% faster than that of ZnO/glass.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.256-259
• /
• 2006

The amorphous $SiO_x$ nanowires were synthesized by the vapor phase epitaxy (VPE) method. $SiO_x$ nanowires were formed on silicon wafer of temperatures ranged from $800{\sim}1100^{\circ}C$ and nickel thin film was used as a catalyst for the growth of nanowires. A vapor-liquid-solid (VLS) mechanism is responsible for the catalyst-assisted amorphous $SiO_x$ nanowires synthesis in this experiment. The SEM images showed cotton-like nanostructure of free standing $SiO_x$ nanowires with the length of more than about $10{\mu}m$. The $SiO_x$ nanowires were confirmed amorphous structure by TEM analysis and EDX spectrum reveals that the nanowires consist of Si and O.