A Bi$_{4}$Ti$_{3}$O$_{12}$ (BIT) thin film is prepared by sol-gel method using acetate precursors and evaluated whether it could be applied to NVFRAM (Non-Volatile Ferroelectric RAM). The drying and the annealing temperature are 40$0^{\circ}C$ and $650^{\circ}C$, respectively and they are determined from the DT-TG (Differential Thermal-Thermal Gravimetric) analysis. The BIT thin film deposited on Pt/Ta/SiO$_{2}$/Si substrate shows orthorhombic perovskite phase. The grain size and the surface roughness are about 100 nm and 70.2$\AA$, respectively. The dielectric constant and the loss tangent at 10 KHz are 176 and 0.038, respectively, and the leakage current density at 100 ㎸/cm is 4.71 $mutextrm{A}$/$\textrm{cm}^2$. In the results of hysteresis loops measured at $\pm$250 ㎸/cm, the remanent polarization (Pt) and the coercive field (Ec) are 5.92 $\mu$C/$\textrm{cm}^2$ and 86.3 ㎸/cm, respectively. After applying 10$^{9}$ square pulses of $\pm$5V, the remanent polarization of the BIT thin film decreases as much as about 33% from 5.92 $\mu$C/$\textrm{cm}^2$ of initial state to 3.95 $\mu$C/$\textrm{cm}^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제34권6호
• /
• pp.442-448
• /
• 2021

In this work, the (K_1-xAg_x)(Ta_0.8Nb_0.2)O₃ (x=0.1-0.4) ceramics were fabricated using mixed-oxide method, and their structural and electrical properties were measured. All specimens represented a pseudo cubic structure with the lattice constant of 0.3989 nm. When 0.4 mol of Ag was added, second phases induced from metallic Ag and K₂(Ta,Nb)₆O₁₆ phase were observed. Dielectric constant and dielectric loss of K(Ta_0.8Nb_0.2)O₃ specimen doped with 0.3 mol of Ag were 2,737 and 0.446, respectively. The curie temperature was about -5℃, which does not change with Ag addition. The remanent polarization began to decrease sharply around 12~15℃, and the temperature at which the remanent polarization began to decrease as the applied voltage increased shifted to the high temperature side. The electrocaloric effect (ΔT) and electrocaloric efficiency (ΔT/ΔE) of the (K_0.7Ag_0.3)(Ta_0.8Nb_0.2)O₃ ceramics were 0.01024℃ and 0.01825 KmV^-1, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제37권3호
• /
• pp.297-303
• /
• 2024

In this study, KTN heterolayer thin films were fabricated by alternately stacking films of K(Ta_0.70Nb_0.30)O₃ and K(Ta_0.55Nb_0.45)O₃ synthesized using the sol-gel method. The sintering temperature and time were 750℃ and 1 hour, respectively. All specimens exhibited a polycrystalline pseudo-cubic crystal structure, with a lattice constant of approximately 0.398 nm. The average grain size was around 130~150 nm, indicating relatively uniform sizes regardless of the number of coatings. The average thickness of a single-coated film was approximately 70 nm. The phase transition temperature of the KTN heterolayer films was found to be approximately 8~12℃. Moreover, the 6-coated KTN heterolayer film displayed an excellent dielectric constant of about 11,000. As the number of coatings increased, and consequently the film thickness, the remanent polarization increased, while the coercive field decreased. The 6-coated KTN heterolayer film exhibited a remanent polarization and coercive field of 11.4 μC/cm² and 69.3 kV/cm at room temperature, respectively. ΔT showed the highest value at a temperature slightly above the Curie temperature, and for the 6-coated KTN heterolayer film, the ΔT and ΔT/ΔE were approximately 1.93 K and 0.128×10^-6 K·m/V around 40℃, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• 제25권6호
• /
• pp.239-244
• /
• 2015

Lead zirconate titanate (PZT) thick films with thickness of $10{\sim}20{\mu}m$ were fabricated on silicon substrate by aerosol deposition method. As-deposited films on silicon were annealed at the temperatures of $700^{\circ}C$. The electrical properties of films deposited by PZT powders were characterized using impedance analyzer and Sawyer-Tower circuit. The PZT powder was prepared by both conventional solid reaction process and sol-gel process. The remanent polarization, coercive field, and dielectric constant of the $10{\mu}m$ thick film with solid reaction process were $20{\mu}C/cm^2$, 30 kV/cm and 1320, respectively. On the other hand, the PZT films by sol-gel process showed a poor dielectric constant of 635. The reason was probably due to the presence of pores produced from organic residue during annealing.

• Korean Journal of Materials Research
• /
• 제11권11호
• /
• pp.960-964
• /
• 2001

$Bi_{3.99}Ti_{2.97}V_{0.03}O_{12}$ (BTV) thin films with 3 mol% vanadium doping were Prepared on $Pt/Ti/SiO_2/Si$ substrate by sol-gel method. X-ray diffraction analysis indicated that single-phase layered perovskite were obtained and preferred orientation was not observed. Under the annealing temperature at $600^{\circ}C$, the surface morphology of the BTV thin films had fine-rounded particles and then changed plate-like at $650^{\circ}C$ and $700^{\circ}C$. The remanent polarization $(2P_r)$ and coercive field $(2E_c)$ of $700^{\circ}C$ annealed BTV thin film were 25 $\mu$C/cm$^2$ and 116 kV/cm, respectively. In addition, BTV thin film showed little polarization fatigue during $10_9$ switching cycles. These improved ferroelectric properties were attributed to the increased rattling space and reduced oxygen vacancies by substitution $Ti^{4+}$ ion (68 pm) with smaller $V^{5+}$ ion (59 pm). The dielectric constant and loss were measured 130 and 0.03 at 10 kHz, respectively.

• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.219-223
• /
• 2000

The ferroelectric SBT films were deposited on Pt/Ti/SiO$_2$/Si substrates by liquid injection metalorganic chemical vapor deposition (MOCVD) with single-mixture solution of Sr[Ta(OEt)$_5$(dmae)]$_2$and Bi(C$_6$ 6/H$_5$)$_3$. The Sr/Ta and Bi/Ta ratio in SBT films depended on deposition temperature and mol ratio of precursor in the single-mixture solution. At the substrate temperature of 40$0^{\circ}C$, Sr/Ta and Bi/Ta ratio were close to 0.4 and 1 at precursor mol ratio of 0.5~1.0, respectively. As-deposited film was amorphous. However, after annealing at 75$0^{\circ}C$ for 30 min in oxygen atmosphere, the diffraction patterns indicated polycrystalline SBT phase. The remanent polarization (Pr) and coercive field (Ec) of SBT film annealed at 75$0^{\circ}C$ were 4.7$\mu$C/$\textrm{cm}^2$ and 115.7kV/cm at an applied voltage of 5V, respectively. The SBT films annealed at 75$0^{\circ}C$ showed practically no polarization fatigue up to 10$^10$ switching cycles.

• Transactions on Electrical and Electronic Materials
• /
• 제5권6호
• /
• pp.223-226
• /
• 2004

The PZT thin films are one of well-known materials that has been widely studied for ferroelectric random access memory (FRAM). We etched the PZT thin films by $CF_{4}/(Cl_{2}+Ar)$ plasma and investigated improvement in etching damage by $O_{2}$ annealing. The maximum etch rate of the PZT thin films was 157 nrn/min and that the selectivity of the PZT thin films to Pt was 3.1 when $CF_{4}(30{\%})$ was added to a $Cl_{2}(80{\%})/Ar(20{\%})$ gas mixing ratio. To improve the ferroelectric properties of PZT thin films after etching, the samples were annealed for 10 min at various temperatures in $O_{2}$ atmosphere. After $O_{2}$ annealing, the remanent polarization of the asdeposited films was $34.6{\mu}/cm^{2}$ and the sample annealed at 650, 550, and $450^{\circ}C$ was 32.8, 22.3, and $18.6{\mu}/cm^{2}$, respectively. PZT thin films with $O_{2}$ annealing at $450^{\circ}C$ retained $77{\%}$ of their original polarization at 106 cycles. Also as the annealing temperature increased, the fatigue properties improved. And the leakage current was decreased gradually and almost recovered to the as-deposited value after the annealing at $450^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제15권9호
• /
• pp.783-787
• /
• 2002

In recent year, B $i_{4-}$x L $a_{x}$ $Ti_3$ $O_{12(BLT)}$ is one of promising substitute materials for the ferroelectric random access memory(FRAM) applications. But the systematic composition is still insufficient, so this experiment was carried out in ceramic ambient sintering process which has the very excellent ferroelectric property. Samples were prepared by a bulk and the purpose which was estimated with a suitability of thin films applications. The density of B $i_{3.75}$ L $a_{0.25}$ $Ti_3$ $O_{12}$ was high and the XRD pattern showed that the intensity of main peak (117) was increased at the argon ambient sintering. Controlling the quantity of oxygen, crystallization showed a thin, long plate like type, and we obtained the excellent dielectric and polarization properties at the argon atmosphere sintering. Also this sintering process was effective at the bulk sample. Argon ambient sintered sample produced higher permittivity of 154, the remanent polarization(2Pr) of 6.8 uC/$\textrm{cm}^2$ compared with that sintered in air and oxygen ambient. And this sintering process showed a possibility which could be applied to thin films process..

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.296-296
• /
• 2007

Ferroelectric neodymium-substituted $Bi_4Ti_3O_{12}$(BTO) thin films have been successfully deposited on Pt/Ti/$SiO_2$/Si substrate by a sol-gel spin-coating process and the effect of crystallization temperature on their microstructure and ferroelectric properties were studied systematically. $Bi(TMHD)_3$, $Nd(TMHD)_3$, $Ti(O^iPr)_4$ were used as the precursors, which were dissolved in 2-methoxyethanol. The thin films were annealed at various temperatures from 600 to $720^{\circ}C$ in oxygen ambient for 1 hr, which was followed by post-annealed for 1 hr after depositing a Pt electrode to enhance the electrical properties. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze the crystallinity and surface morphology of layered perovskite phase, respectively. The crystallinity of the BNT films was improved and the average grain size increased as the crystallization temperature increased from 600 to $720^{\circ}C$ at an interval of $40^{\circ}C$. The polarization values of the films were a monotonous function of the crystallization temperature. The remanent polarization value of the BNT thin films annealed at $720^{\circ}C$ was $24.82\;{\mu}C/cm^2$ at an applied voltage of 5 V.

• Proceedings of the KIEE Conference
• /
• 대한전기학회 1999년도 하계학술대회 논문집 D
• /
• pp.1771-1773
• /
• 1999

Ferroelectric PZT(10/90)/(90/10)heterolayered thin films were fabricated by the alkoxide-based Sol-Gel method Electric and dielectric properties of PZT(10/90)/(90/10) heterolayered thin films have been investigated, focusing on the effect of PZT/PZT and PZT/electrode interface on the heterolayered films. Dielectric constant increased with increasing the number of coatings. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered thin films deposited on Pt/Ti/$SiO_2$/Si were $7.18{\mu}C/cm$, $68.5kV/cm^2$, respectively. Leakage current, densities were increased with increasing the number of coatings, and the value of the PZT-4 film deposited on the Pt/Ti/$SiO_2$/Si substrate was about $7{\times}10^{-8}A/cm^2$ at 0.05MV/cm.