Development of Mg-18wt.%Ni-Hydrogen-Storage Alloy by Mechanical Alloying (기계적인 합금화에 의한 Mg-18wt.%Ni 수소저장합금의 개발)

  • Song, Myoung-Youp;Ahn, Dong-Su;Kwon, Ik-Hyun;Ahn, Hyo-Jun
    • Korean Journal of Materials Research
    • /
    • v.10 no.1
    • /
    • pp.15-20
    • /
    • 2000
  • The hydrogen-storage properties of a mechanically-alloyed Mg-18wt.%Ni mixture were investigated. Among the mixtures mechanically alloyed for 1h, 3h, and 6h, the mixture mechanically alloyed for 6h(MA 6h sample) shows the best properties of activation, hydriding, and dehydriding. The $Mg_2Ni$ phase forms in the mechanically-alloyed Mg-18wt.%Ni mixture along with hydriding-dehydriding cycling. The MA 6h sample is relatively easily activated and has higher hydriding rate than the pure Mg, the Mg-10wt.%Ni alloy, and a little lower hydriding rate than the $Mg_2Ni$alloy. The MA 6h sample lower dehydriding rate than the $Mg_2$Ni alloy but higher dehydriding rate than the pure Mg and the Mg-25wt.%Ni alloy. The MA 6h sample has larger hydrogen-storage capacity than the pure Mg and the other alloys.

  • PDF

Development of MgH2-Ni Hydrogen Storage Alloy Requiring No Activation Process via Reactive Mechanical Grinding

  • Song, Myoung Youp;Kwak, Young Jun;Lee, Seong Ho;Park, Hye Ryoung
    • Korean Journal of Metals and Materials
    • /
    • v.50 no.12
    • /
    • pp.949-953
    • /
    • 2012
  • $MgH_2$ was employed as a starting material instead of Mg in this work. A sample with a composition of 94 wt% $MgH_2-6$ wt% Ni (called $MgH_2-6Ni$) was prepared by reactive mechanical grinding. The hydriding and dehydriding properties were then examined. An $MgH_2-Ni$ hydrogen storage alloy that does not require an activation process was developed. The alloy was prepared in a planetary ball mill by grinding for 4 h at a ball disc revolution speed of 250 rpm under a hydrogen pressure of about 12 bar. The sample absorbed 3.74 wt% H for 5 min, 4.07 wt% H for 10 min, and 4.41 wt% H for 60 min at 573 K under 12 bar $H_2$, and desorbed 0.93 wt% H for 10 min, 1.99 wt% H for 30 min, and 3.16 wt% H for 60 min at 573 K under 1.0 bar $H_2$. $MgH_2-6Ni$ after reactive mechanical grinding contained ${\beta}-MgH_2$ (a room temperature form of $MgH_2$), Ni, ${\gamma}-MgH_2$ (a high pressure form of $MgH_2$), and a very small amount of MgO. Reactive mechanical grinding of Mg with Ni is considered to facilitate nucleation, and to reduce the particle size of Mg. $Mg_2Ni$ formed during reactive mechanical grinding also increases the hydriding and dehydriding rates of the sample.

Hydrogen Storage Properties of Pure MgH2

  • Kwak, Young Jun;Lee, Seong Ho;Park, Hye Ryoung;Song, Myoung Youp
    • Korean Journal of Materials Research
    • /
    • v.23 no.5
    • /
    • pp.266-270
    • /
    • 2013
  • The hydrogen storage properties of pure $MgH_2$ were studied and compared with those of pure Mg. At the first cycle, pure $MgH_2$ absorbed hydrogen very slowly at 573 K under 12 bar $H_2$. The activation of pure $MgH_2$ was completed after three hydriding-dehydriding cycles. At the $4^{th}$ cycle, the pure $MgH_2$ absorbed 1.55 wt% H for 5 min, 2.04 wt% H for 10 min, and 3.59 wt% H for 60 min, showing that the activated $MgH_2$ had a much higher initial hydriding rate and much larger $H_a$ (60 min), quantity of hydrogen absorbed for 60 min, than did activated pure Mg. The activated pure Mg, whose activation was completed after four hydriding-dehydriding cycles, absorbed 0.80 wt% H for 5 min, 1.25 wt% H for 10 min, and 2.34 wt% H for 60 min. The particle sizes of the $MgH_2$ were much smaller than those of the pure Mg before and after hydriding-dehydriding cycling. The pure Mg had larger hydrogen quantities absorbed at 573K under 12 bar $H_2$ for 60 min, $H_a$ (60 min), than did the pure $MgH_2$ from the number of cycles n = 1 to n = 3; however, the pure $MgH_2$ had larger $H_a$ (60 min) than did the pure Mg from n = 4 to n = 6.

The Significance of Gonadotropin Ratio in In Vitro Fertilization of Human Oocytes (성선 자극호르몬의 비율이 인간난자의 체외수정에 미치는 영향에 관한 연구)

  • Moon, Shin-Yong
    • Clinical and Experimental Reproductive Medicine
    • /
    • v.15 no.2
    • /
    • pp.135-147
    • /
    • 1988
  • To compare the stimulation effect of the ratio in follicle stimulating hormone and luteinizing hormone in induction of multiple follicular growth, the serum $E_2$ level, the diameter of follicle, number of aspirated follicles and cleavage rate of in vitro fertilized preovulatory oocytes as well as the pregnancy rate were evaluated. Forty one patients with irreparable tubal disease were stimulated by hMG(n=24) or FSH/hMG(n=17) for the purpose of in vitro fertilization and embryo transfer. The following results were obtained. 1. Serum estradiol($E_2$) levels on the day of hCG administration were $921.0{\pm}353.3\;pg/ml$ in hMG group and $1272.9{\pm}1060.6\;pg/ml$ in FSH/hMG group. The serum $E_2$ value of hMG group was significantly lower than that of FSH/hMG group. 2. The diameter of leading follicle by ultrasonogram on the day of hCG administration were $16.2{\pm}2.0\;mm$ in hMG group and $16.2{\pm}2.6\;mm$ in FSH/hMG group. No significant difference of follicle diameter between two groups was demonstrated. 3. The number of follicles with diameter above 10 mm by sonogram on the day of hCG injection were $3.91{\pm}2.32$ in hMG group and $6.52{\pm}3.86$ in FSH/hMG group. There was significant difference of number of follicles between two groups, (p< 0.01). 4. The number of oocytes found per patient at aspiration were $2.59{\pm}1.00$ in hMG group and 3. $76{\pm}2.31$ in FSH/hMG group. There was significant difference of number of aspirated oocytes between two groups. (p< 0.05). 5. The detection rate of preovulatory oocyte at aspiration were 68.4%(39/57) in hMG group (n=22) and 77.6%(38/49) in FSH/hMG group (n=13). 6. The cleavage rate of preovulatory oocyte at 44 hours after insemination were 74.4%(29/39) in hMG group(n=22) and 81.6%(31/38) in FSH/hMG group (n=13). When only hMG was used, one pregnancy was established in 15 patients to whom 29 zygotes were transferred. And a full term normal female baby was delivered by elective cesarean section. In the FSH/hMG group, five pregnancies out of 9 transferred patients were confirmed by serum ${\beta}-hCG$. Two pregnancies were spontaneously aborted before the 6th week of pregnancy. One patient aborted her baby at the 18th week of pregnancy because of incompetent internal os of the cervix. Two patients delivered two full term babies by elective cesarean section. From the above findings, paralell with the increase in the ratio of exogenous follicle stimulating hormone to luteinizing hormone, an increase in oocyte recovery was observed as well as an improvements in pregnancy rate. It was concluded that FSH enrichment early in the follicular phase had a beneficial effect in the controlled ovarian hyperstimulation.

  • PDF

Hydrogen Absorption at a Low Temperature by MgH2 after Reactive Mechanical Grinding

  • Song, Myoung Youp;Lee, Seong Ho;Kwak, Young Jun;Park, Hye Ryoung
    • Korean Journal of Materials Research
    • /
    • v.24 no.3
    • /
    • pp.129-134
    • /
    • 2014
  • Pure $MgH_2$ was milled under a hydrogen atmosphere (reactive mechanical grinding, RMG). The hydrogen storage properties of the prepared samples were studied at a relatively low temperature of 423 K and were compared with those of pure Mg. The hydriding rate of the Mg was extremely low (0.0008 wt% H/min at n = 4), and the $MgH_2$ after RMG had higher hydriding rates than that of Mg at 423 K under 12 bar $H_2$. The initial hydriding rate of $MgH_2$ after RMG at 423 K under 12 bar $H_2$ was the highest (0.08 wt% H/min) at n = 2. At n = 2, the $MgH_2$ after RMG absorbed 0.39 wt% H for 5 min, and 1.21 wt% H for 60 min at 423K under 12 bar $H_2$. At 573 K under 12 bar $H_2$, the $MgH_2$ after RMG absorbed 4.86 wt% H for 5 min, and 5.52 wt% H for 60 min at n = 2. At 573 K and 423 K under 1.0 bar $H_2$, the $MgH_2$ after RMG and the Mg did not release hydrogen. The decrease in particle size and creation of defects by reactive mechanical grinding are believed to have led to the increase in the hydriding rate of the $MgH_2$ after RMG at a relatively low temperature of 423 K.

A Study on Basic Investigation for Quality Improvement of Raw-Silk A Study on the Dissolving Behavior of Sericin in the Cocoon Shell and Pupa Protein (Bombyx mori L.) (Part III) (생사 품위향상을 위한 기초조사 연구 견층 Sericin과 용체 단백질의 용해거동에 관한 연구(III))

  • 임영우
    • Journal of Sericultural and Entomological Science
    • /
    • v.17 no.2
    • /
    • pp.161-170
    • /
    • 1975
  • This study is to investigate the content of crude protein intruded in the sericin of cocoon shell and pupa by treatment of buffer solution (pH 1 to pH 13) 20 ml per 1 gram for 30 and 60 minutes at 30$^{\circ}C$, 60$^{\circ}C$ and 100${\pm}$2$^{\circ}C$, respectively. The results obtained are summarized as follows. 1. The quantity of total crude protein obtained from cocoon shell and pupa by treatment during 30 minutes at 30$^{\circ}C$ was dissolved as the largest quantity of 11.874 mg/g at pH 1 and l5.93mg/g at pH 13, but dissolved the smallest quantity 1.75g/g at pH 5 as known. and tile quantity of crude protein treated for 60 minutes is 13.437mg/g at pH 1 and 22.50mg/g at pH 13. Also, the smallest quantity is 2. 813mg/g at pH 5 as known. 2. By the treatment during 30 minutes at 60$^{\circ}C$, the dissolved largest quantity was 13.12mg/g at pH 1 and 21.875 mg/g at pH 13, but the smallest quantity is 2.375mg/g at pH 5 as known After treatment for 60 minutes at 60$^{\circ}C$, the dissolved largest quantity was 17.500 mg/g at pH 1 and 31.56mg/g at pH 13, bu the smallest quantity is 3.849 mg/g at pH 5. 3. The dissolved crude protein from the cocoon shell and pupa by treatment for 30 minutes at 100${\pm}$2$^{\circ}C$ was the largest quantity of 147.000mg/g at pH 1 and 398. 125mg/g at pH 13, but the smallest quantity is 75.00mg/g at pH 5 as known. After treatment for 60 minutes at 100${\pm}$2$^{\circ}C$, the largest quantity was 253.76 mg/g at pH 1 and 460.625mg/g at pH 13, but the smallest quantity is 139.375mg/g at pH 5 as known. 4. The dissolved crude protein from the cocoon shell and pupa was not different in quantity by treatment at 30$^{\circ}C$ or 60$^{\circ}C$. But dissolved crude protein was large quantity from cocoon shell more than pupa, as known. 5. The treatment of cocoon shell and pupa during 60 minutes at 100${\pm}$20$^{\circ}C$ was increased to the dissolved largest quantity of crude protein of 19.20% at pH 1 and 22. 18% at pH 13 from the cocoon shell and 6. 12% at pH, an d 23.87% at pH 13 from the pupa. But dissolved crude protein was increased to the larger quantity from pupa more than cocoon shell.

  • PDF

Improvement of Hydrogen Storage Properties of Mg by Addition of NbF5 via Mechanical Milling under H2

  • Kwak, Young Jun;Song, Jiyoung;Mumm, Daniel R.
    • Korean Journal of Materials Research
    • /
    • v.23 no.10
    • /
    • pp.562-567
    • /
    • 2013
  • A 90 wt% Mg-10 wt% $NbF_5$ sample was prepared by mechanical milling under $H_2$ (reactive mechanical grinding). Its hydriding and dehydriding properties were then examined. Activation of the 90 wt% Mg-10 wt% $NbF_5$ sample was not required. At n=1, the sample absorbed 3.11 wt% H for 2.5 min, 3.55 wt% H for 5 min, 3.86 wt% H for 10 min, and 4.23 wt% H for 30 min at 593K under 12 bar $H_2$. At n=1, the sample desorbed 0.17 wt% H for 5 min, 0.74 wt% H for 10 min, 2.03 wt% H for 30 min, and 2.81 wt% H for 60 min at 593K under 1.0 bar $H_2$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ after reactive mechanical grinding showed Mg, ${\beta}-MgH_2$ and small amounts of ${\gamma}-MgH_2$, $NbH_2$, $MgF_2$ and $NbF_3$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ dehydrided at n=3 revealed Mg, ${\beta}-MgH_2$, a small amount of MgO and very small amounts of $MgH_2$ and $NbH_2$. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial hydriding rate and a larger quantity of hydrogen absorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$, which were reported to have quite high hydriding rates and/or dehydriding rates. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial dehydriding rate (after an incubation period) and a larger quantity of hydrogen desorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$.

Hydrogen Generation through the Reaction with Water of MgO, MgCl2 or Ni+Nb2O5 - Added Magnesium Hydrides

  • Hong, Seong-Hyeon;Kim, Hyun-Jin;Song, Myoung Youp
    • Korean Journal of Metals and Materials
    • /
    • v.50 no.2
    • /
    • pp.183-190
    • /
    • 2012
  • Hydrogen was generated by the reaction of metal hydride with water. The variation of hydrogen generation with the kind of powders (milled $MgH_2$, and $MgH_2$ milled with various contents of MgO, $MgCl_2$ or $Ni+Nb_2O_5$) was investigated. $MgH_2$ powder with a hydrogen content of 6.05 wt% from Aldrich Company was used. Hydrogen is generated by the reaction of Mg as well as $MgH_2$ with water, resulting in the formation of byproduct $Mg(OH)_2$. For about 5 min of reaction time, milled $95%MgH_2+5%MgO$ has the highest hydrogen generation rate among milled $MgH_2+x%MgO$ (x=0, 5, 10, 15 and 20) samples. Milled $90%MgH_2+10%MgCl_2$ has the highest hydrogen generation rate among all the samples.

Dietary Effect of Hemicellulose from Soy Fiber on Blood Glucose and Cholesterol Content in Streptozotocin-Induced Diabetic Rats (콩 식이섬유로부터 추출한 헤미셀룰로즈의 식이가 Streptozotocin유도 당뇨 흰쥐의 혈당과 혈청 콜레스테롤 함량에 미치는 영향)

  • 이명예;김미경;신진기;김순동
    • Journal of the Korean Society of Food Science and Nutrition
    • /
    • v.33 no.7
    • /
    • pp.1119-1125
    • /
    • 2004
  • The effect of hemicellulose extracted from soy fiber on the level of blood glucose and serum cholesterol in the streptozotocin-induced diabetic rat were investigated. The experimental plots were divided to cellulose group (control, 0.5% hemicellulose group (H-l) and 1% hemicellulose group (H-2) group. The groups were fed for 6 weeks, then fed for 1 week more after streptozotocin injection. Food intakes, weight gain and food efficiency ratio of H-2 group were higher, while water intakes and liver weight were lower than those of control and H-l group. The content of blood glucose and urine glucose were 212.8 mg/dL, 0.97 mg/dL in the control group, 160.5 mg/dL, 0.53 mg/dL in the H-l group, 141.0 mg/dL, 0.35 mg/dL in the H-2 group, respectively. There was no significantly difference in the content of neutral lipid, while the content of total serum cholesterol was 101.6 mg/dL in the control group, 73.8-78.4 mg/dL in the hemicellulose groups. The content of serum HDL-cholesterol in the all experimental groups showed no significantly difference showing 39.8-44.7 mg/dL. HTR and atherogenic index were 0.44 and 1.27 in the control group, but 0.54 and 0.46-0.85 in the hemicellulose groups, respectively.

Effects of Nutritional Sources on Degradation of Polychlorinated Biphenyls (PCBs) by Pseudomonas sp. P2 (Pseudomonas sp. P2에 의한 Polychlorinated Biphenyls(PCBs) 분해에 대한 영양원의 영향)

  • 최상기;금정호
    • Journal of Environmental Science International
    • /
    • v.5 no.5
    • /
    • pp.611-617
    • /
    • 1996
  • The effects of nutritional sources on growth of Pseudomonas sp. P2 were investigated in medium containing biphentyl as a carbon source. To determine characterization of Pseudomonas sp. P2, the incubation time was determined to 100 h of the log phase in the growth curve. The optimal compositions for the growth of Pseudomonas sp. P2 degrading polychlorinated biphenyls (PCBs) were 1000 mg/L $NH_4NO_3$, 1000mg/L KH_2PO_4$, 100mg/L MgSO_4$.$7H_2O$, 30mg/L $CaCl_2$.$2H_2O$, 200mg/L NaCl, and 10mg/L $FeSO_4$.$7H_2O$. Pseudomonas sp. P2 showed the degradability of 59.3%, 57.6%, 51.4%, and 48.7% at 500mg/L, 1000mg/L, 1500mg/L, and 2000mg/L of the PCBs within insulating oil after 100 h incubation under the optimum conditions, respectively.

  • PDF