• 한국재료학회지
• /
• 제17권9호
• /
• pp.463-468
• /
• 2007

The interdiffusion characteristics of Cu-plug/Capping Layer/NiSi contacts were investigated. Capping layers were deposited on Ni/Si to form thermally-stable NiSi and then were utilized as diffusion barriers between Cu/NiSi contacts. Four different capping layers such as Ti, Ta, TiN, and TaN with varying thickness from 20 to 100 nm were employed. When Cu/NiSi contacts without barrier layers were furnace-annealed at $400^{\circ}C$ for 40 min., Cu diffused to the NiSi layer and formed $Cu_3Si$, and thus the NiSi layer was dissociated. But for Cu/Capping Layers/NiSi, the Cu diffusion was completely suppressed for all cases. But Ni was found to diffuse into the Cu layer to form the Cu-Ni(30at.%) solid solution, regardless of material and thickness of capping layers. The source of Ni was attributed to the unreacted Ni after the silicidation heat-treatment, and the excess Ni generated by the transformation of $Ni_2Si$ to NiSi during long furnace-annealing.

• 한국표면공학회지
• /
• 제34권5호
• /
• pp.475-480
• /
• 2001

Diffusion of Cu into the low-k para-xylene based plasma polymer (pXPP) thin films deposited by plasma-enhanced chemical vapor deposition using the para-xylene precursor was comparatively measured using various methods. Cu layer was deposited on the surfaces of pXPPs treated by $N_2$ plasma generated in a magnetically enhanced inductively coupled plasma reactor. Diffusion characteristics of Cu into pXPPs were measured using Rutherford backscattering spectroscopy (RBS), secondary ion mass spectroscopy (SIMS), cross-sectional transmission electron microscopy (XTEM), and current-voltage (I-V) measurements for the vacuum-annealed Cu/pXPPs for 1 hour at $450^{\circ}C$ and were compared. The results showed a correlation between the I-V measurement and SIMS data are correlated and have a sensitivity enough to evaluate the dielectric properties but the RBS or XTEM measurements are not sufficient to conclude the electrical properties of low-k dielectrics with Cu in the film bulk. The additional results indicate that the pXPP layers are quite resistant to Cu diffusion at the annealing temperature of $450^{\circ}C$ compared to the other previously reported organic low-k materials.

• 마이크로전자및패키징학회지
• /
• 제20권2호
• /
• pp.59-64
• /
• 2013

3차원 적층 패키지를 위한 Cu/Ni/Au/Sn-Ag/Cu 미세 범프의 열처리에 따른 금속간 화합물 성장 거동을 분석하기 위하여 in-situ SEM에서 $135^{\circ}C$, $150^{\circ}C$, $170^{\circ}C$의 온도에서 실시간 열처리 실험을 진행하였다. 실험 결과 금속간 화합물의 성장 거동은 열처리시간이 경과함에 따라 시간의 제곱근에 직선 형태로 증가하였고, 확산에 의한 성장이 지배적인 것을 확인 할 수 있었다. Ni/Au 층의 존재로 인해 Au의 확산으로 복잡한 구조의 금속간 화합물이 생성 된 것을 확인할 수 있다. 활성화 에너지는 $Cu_3Sn$의 경우 0.69eV, $(Cu,Ni,Au)_6Sn_5$경우 0.84 eV로 Ni이 포함된 금속간 화합물이 더 높은 것을 확인 하였으며, 확산 방지층 역할을 하는 Ni층에 의해 금속간 화합물 성장이 억제됨에 따라 신뢰성이 향상 될 것으로 사료된다.

• 한국재료학회지
• /
• 제22권4호
• /
• pp.202-206
• /
• 2012

$CoSi_2$ was formed through annealing of atomic layer deposition Co thin films. Co ALD was carried out using bis(N,N'-diisopropylacetamidinato) cobalt ($Co(iPr-AMD)_2$) as a precursor and $NH_3$ as a reactant; this reaction produced a highly conformal Co film with low resistivity ($50\;{\mu}{\Omega}cm$). To prevent oxygen contamination, $ex-situ$ sputtered Ti and $in-situ$ ALD Ru were used as capping layers, and the silicide formation prepared by rapid thermal annealing (RTA) was used for comparison. Ru ALD was carried out with (Dimethylcyclopendienyl)(Ethylcyclopentadienyl) Ruthenium ((DMPD)(EtCp)Ru) and $O_2$ as a precursor and reactant, respectively; the resulting material has good conformality of as much as 90% in structure of high aspect ratio. X-ray diffraction showed that $CoSi_2$ was in a poly-crystalline state and formed at over $800^{\circ}C$ of annealing temperature for both cases. To investigate the as-deposited and annealed sample with each capping layer, high resolution scanning transmission electron microscopy (STEM) was employed with electron energy loss spectroscopy (EELS). After annealing, in the case of the Ti capping layer, $CoSi_2$ about 40 nm thick was formed while the $SiO_x$ interlayer, which is the native oxide, became thinner due to oxygen scavenging property of Ti. Although Si diffusion toward the outside occurred in the Ru capping layer case, and the Ru layer was not as good as the sputtered Ti layer, in terms of the lack of scavenging oxygen, the Ru layer prepared by the ALD process, with high conformality, acted as a capping layer, resulting in the prevention of oxidation and the formation of $CoSi_2$.

• 한국세라믹학회지
• /
• 제42권9호
• /
• pp.624-630
• /
• 2005

To investigate the possibility of the $ZrO_2$ buffer layer as the insulator for the Metal-Ferroelectric-Insulator-semiconductor (MFIS) structure, $ZrO_2$ and $SrBi_2Ta_2O_9$ (SBT) thin films were deposited on the P-type Si(111) wafer by the R.F. magnetron-sputtering method. According to the process with and without the post-annealing of the $ZrO_2$ buffer layer and SBT thin film, the diffusion amount of Sr, Bi, Ta elements show slight difference through the Glow Discharge Spectrometer (GDS) analysis. From X-ray Photoelectron Spectroscopy (XPS) results, we could confirm that the post-annealing process affects the chemical binding condition of the interface between the $ZrO_2$ thin film and the Si substrate. Compared to the MFIS structure without the post-annealing of the $ZrO_2$ buffer layer, memory window value of MFlS structure with post-annealing of the $ZrO_2$ buffer layer were considerably improved. The window memory of the Pt/SBT (260 nm, $800^{\circ}C)/ZrO_2$ (20 nm) structure increases from 0.75 to 2.2 V under the applied voltage of 9 V after post-annealing.

• 한국재료학회지
• /
• 제14권6호
• /
• pp.389-393
• /
• 2004

The silicide layer used as a diffusion barrier in microelectronics is typically required to be below 50 nm-thick and, the same time, the silicides also need to have low contact resistance without agglomeration at high processing temperatures. We fabricated Si(100)/15 nm-Ni/15 nm-Co samples with a thermal evaporator, and annealed the samples for 40 seconds at temperatures ranging from $700^{\circ}C$ to $1100^{\circ}C$ using rapid thermal annealing. We investigated microstructural and compositional changes during annealing using transmission electron microscopy and auger electron spectroscopy. Sheet resistance of the annealed sample stack was measured with a four point probe. The sheet resistance measurements for our proposed Co/Ni composite silicide was below 8 $\Omega$/sq. even after annealing $1100^{\circ}C$, while conventional nickel-monosilicide showed abrupt phase transformation at $700^{\circ}C$. Microstructure and auger depth profiling showed that the silicides in our sample consisted of intermixed phases of $CoNiSi_{x}$ and NiSi. It was noticed that NiSi grew rapidly at the silicon interface with increasing annealing temperature without transforming into $NiSi_2$. Our results imply that Co/Ni composite silicide should have excellent high temperature stability even in post-silicidation processes.

• 한국표면공학회지
• /
• 제36권1호
• /
• pp.14-21
• /
• 2003

Thin films of ZrO$_2$ and TiO$_2$ were deposited on Si(100) substrates using RF magnetron sputtering technique. To study an influence of the sputtering parameters, systematic experiments were carried out in this work. XRD data show that the $ZrO_2$ films were mainly grown in the [111] orientation at the annealing temperature between 800 and $1000^{\circ}C$ while the crystal growth direction was changed to be [012] at above $1000^{\circ}C$. FT-IR spectra show that the oxygen stretching peaks become strong due to $SiO_2$ layer formation between film layers and silicon surface after annealing, and proved that a diffusion caused by either oxygen atoms of $ZrO_2$ layers or air into the interface during annealing. Different crystal growth directions were observed with the various deposition parameters such as annealing temperature, RF power magnitude, and added $O_2$ amounts. The growth rate of $TiO_2$ thin films was increased with RF power magnitude up to 150 watt, and was then decreased due to a sputtering effect. The maximum growth rate observed at 150 watt was 1500 nm/hr. Highly oriented, crack-free, stoichiometric polycrystalline $TiO_2$<110> thin film with Rutile phase was obtained after annealing at $1000^{\circ}C$ for 1 hour.

• 한국전기전자재료학회논문지
• /
• 제37권5호
• /
• pp.500-506
• /
• 2024

The transparent electrode characteristics of the SnO₂/AgNi/SnO₂ (OMO) multilayer structures prepared by sputtering were investigated according to the annealing temperature. Ni-doped Ag of various compositions was selected as the metal layer and heat treatment was performed at 100~300℃ to evaluate the thermal stability of the metals. The manufactured OMO multilayer structures were heat treated for 6 hours at 400~600℃ in an N₂ atmosphere. The structural, electrical, and optical properties of the OMO structures before and after annealing were evaluated and analyzed using a UV-VIS spectrophotometer, 4-point probe, XPS, FE-SEM, etc. OMO with Ni-doped Ag shows improved performance due to the reduction of structural defects of Ag during annealing, but OMO structure with pure Ag shows degradation characteristics due to Ag diffusion into the oxide layer during high-temperature annealing. The figure of merit (FOM) of SnO₂/Ag/SnO₂ was highest at room temperature and gradually decreased as the heat treatment temperature increased. On the other hand, the FOM value of SnO₂/AgNi/SnO₂ mostly showed its maximum value at high temperature(~550℃). In particular, the FOM value of SnO₂/Ag-Ni (3.2 at%)/SnO₂ was estimated to be approximately 2.38×10^-2 Ω^-1. Compared to transparent electrodes made of other similar materials, the FOM value of the SnO₂/Ag-Ni (3.2 at%)/SnO₂ multilayer structure is competitive and is expected to be used as an alternative transparent conductive electrode in various devices.

• 한국진공학회지
• /
• 제10권2호
• /
• pp.219-224
• /
• 2001

N형 InGaAs에 대한 Pd/Ge/Ti/Pt 오믹 접촉 특성을 조사하였다. $450^{\circ}C$까지의 급속 열처리에 의해 우수한 오믹 특성을 나타내어 $400^{\circ}C$, 10초의 급속 열처리 조건에서 최저 $3.7\times10^{-6}\; \Omega\textrm{cm}^2$ 의 접촉 비저항을 나타내었다. 이는 열처리에 의해 생성된 Pd-Ge계 화합물의 형성 및 Ge의 InGaAs 표면으로의 확산과 관련이 있었다. 그러나 열처리 시간을 연장할 경우 접촉 비저항이 $low-10^5\; \Omega\textrm{cm}^2$로 약간 증가하였다. 고온 열처리 후에도 오믹 재료와 InGaAs의 평활한 계면을 유지하면서 우수한 오믹 특성을 나타내어, 화합물 반도체 소자의 오믹 접촉으로 충분히 응용 가능하다고 판단된다.

• 한국세라믹학회지
• /
• 제34권8호
• /
• pp.908-913
• /
• 1997

Multilayer NbCxC1-x/Y2O3/Ti were sputter-coated on the alumina substrate, starting with a 0.7 ㎛ thick NbCxC1-x layer grown on substrate, followed by 0.7 ㎛ thick Y2O3 layer and 1 ㎛ thick Ti layer. To find out the optimum conditions for thickness uniformity and adhesion, sputtering works have been done with the variation of sputtering power and Ar pressure. After vacuum annealing at 950℃ and 1000℃, the thermal stability of the NbCxC1-x/Y2O3/Ti coated alumina substrates has been investigated by peel off test. The coating scheme didn't cause any debonded layer after an annealing at 950℃ for 3hrs. However, it was peeled off after annealing at 1000℃ for 3hr. It was found that the thermal stability of Al2O3/NbCxC1-x/Y2O3/Ti coating scheme changed with the NbCxC1-x composition.