• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.1
• /
• pp.25-31
• /
• 2010

In this study, we investigated the morphology and thermal stability of interfacial phases in joint between lead free solder(Sn-3.0Ag-0.5Cu) and electroless Ni-W-P under bump metallizations(UBM) with different tungsten contents as a function of thermal aging. Content of phosphorus of each deposits was fixed at 8 wt.%, and content of tungsten was variated each 0, 3, 6 and 9 wt.%. Specimens were prepared by reflowing at $255^{\circ}C$, aging range was $200^{\circ}C$ and up to 2 weeks. After reflow process, in the electroless Ni(W)-P/solder joint, the interfacial intermetallic compound(IMC) was showed both $(Cu,Ni)_6Sn_5$ and $(Ni,Cu)_3Sn_4$. UBM and generated IMC at the interface of lead free solder was proportionally increased with aging time. The thickness of IMC was increased because the generation rate of $Ni(W)_3P$ decreased with increasing contents of W.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.1-5
• /
• 2012

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.63-68
• /
• 2000

This paper introduces the partial melting process for solder application and characterization of its possibility using off-eutectic Pb-Sn alloy. In order to show that the liquid phase in the semi-liquid state maintains the wettability as the single-phase liquid, the wetting balance test are conducted with varying temperatures and compositions. The results are then compared with the surface tension of liquid, both measured and calculated, to examine the correlation. The results from this investigation indicate that the partial melting can yield satisfactory solder joints as long as the liquid phase acquires sufficient chemical activity. At a condition where the partial melting is effective, a direct correlation between the wettability and the surface tension is found to exist. All alloys are found to show a reasonable wettability in semi-liquid state.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.51-57
• /
• 2008

In this paper, wetting and interfacial reaction properties for low Ag containing Sn-Ag-Cu Pb-free solder alloy, i.e., Sn-0.3Ag-0.7Cu were investigated and compared with those of Sn-1.0Ag-0.5Cu and Sn-3.0Ag-0.5Cu. Melting behavior and stress-strain curves of some Sn-xAg-xCu alloys were also measured using a differential scanning calorimeter(DSC) and a tensile test machine, respectively. In order to enhance insufficient wetting properties of Sn-0.3Ag-0.7Cu alloy, the improvement of wetting properties were analyzed by applying fluxes containing higher content of halide or indium adding of 0.2wt.% into the solder alloy. It was concluded that the small addition of indium is more effective for the improvement of wettability in low temperature range of $230{\sim}240^{\circ}C$ than applying flux containing higher content of halide.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.22-30
• /
• 2013

Due to ELV banning, automotive electronics cannot use four kinds of heavy metal element (Pb, Hg, Cd, $Cr^{6+}$) from 2016. Therefore, this study was focused on degradation characteristics of Sn-3.0Ag-0.5Cu Lead-free solder joint with OSP and ENIG finsh under various reliability assessment method, as like to thermal shock test and high temeprature/high humidity test with test duration for cabin electronics. Also, we compared bonding strength degradation to other advanced research results of electronic control unit for engine room because of difference service temperature with mount location in automotive. Whisker growth phenomenon and mitigation method which were essentially consideration items for Pb-free car electronics were examined. Conformal coating is a strong candidate for mitigating whisker growth in automotive electronics. Necessary condition to adapt Pb-free in car electronics was shown.

• Korean Journal of Metals and Materials
• /
• v.47 no.4
• /
• pp.261-266
• /
• 2009

The mechanical and electrical properties of ball grid array (BGA) solder joints were measured, consisting of Sn-3.5Ag, with organic solderability preservative (OSP)-finished Cu pads and Electroless Nickel/Immersion Gold (ENIG) surface finishes. The mechanical properties were measured by die shear test. When ENIG PCB was upper joint and OSP PCB was lower joint, the highest shear force showed at the third reflow. When OSP PCB was upper joint and ENIG PCB was lower joint, the highest shear force showed at the forth reflow. For both joints, after the die shear results reached the highest shear force, shear force decreased as a function of increasing reflow number. Electrical property of the solder joint decreased with the function of increasing reflow number. The scanning electron microscope results show that the IMC thickness at the bonding interface gets thicker while the number of reflow increases.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.105-105
• /
• 2005

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.187-189
• /
• 2003

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.175-177
• /
• 2006

Electrically Conductive Adhesives(ECAs) with solderable particles have been developed as an alternative to Pb-free solders. Our previous study proved that good wettability of solder particle is a prerequisite for the establishment of conduction paths. In this paper, two types of ECAs were formulated and the wetting characteristic low-melting-point Sn-In solder on Cu and Ni/Au pads was investigated. It was found that Sn-In solder in the developed resin material with reduction capability shows good wettability, especially on Cu pad.

• Corrosion Science and Technology
• /
• v.6 no.6
• /
• pp.282-285
• /
• 2007

Smaller size and higher integration of electronic systems make narrower interconnect pitch not only in chip-level but also in package-level. Moreover electronic systems are required to operate in harsher conditions, that is, higher current / voltage, elevated temperature / humidity, and complex chemical contaminants. Under these severe circumstances, electronic components respond to applied voltages by electrochemically ionization of metals and conducting filament forms between anode and cathode across a nonmetallic medium. This phenomenon is called as the electrochemical migration. Many kinds of metal (Cu, Ag, SnPb, Sn etc) using in electronic packages are failed by ECM. Eutectic SnPb which is used in various electronic packaging structures, that is, printed circuit boards, plastic-encapsulated packages, organic display panels, and tape chip carriers, chip-on-films etc. And the material for soldering (eutectic SnPb) using in electronic package easily makes insulation failure by ECM. In real PCB system, not only metals but also many chemical species are included. And these chemical species act as resources of contamination. Model test systems were developed to characterize the migration phenomena without contamination effect. The serpentine-shape pattern was developed for analyzing relationship of applied voltage bias and failure lifetime by the temperature / humidity biased(THB) test.