• Journal of the Korean institute of surface engineering
• /
• v.40 no.4
• /
• pp.170-174
• /
• 2007

High Velocity Oxygen Fuel (HVOF) thermal spray coating of nano size WC-Co powder (nWC-Co) has been studied as one of the most promising candidate for the possible replacement of the traditional hard plating in some area which causes environmental and health problems. nWC-Co powder was coated on Inconel 718 substrates by HVOF technique. The optimal coating process obtained from the best surface properties such as hardness and porosity is the process of oxygen flow rate (FR) 38 FMR, hydrogen FR 57 FMR and feed rate 35 g/min at spray distance 6 inch for both surface temperature $25^{\circ}C\;and\;500^{\circ}C$. In coating process a small portion of hard WC decomposes to less hard $W_2C$, W and C at the temperature higher than its decomposition temperature $1,250^{\circ}C$ resulting in hardness decrease and porosity increase. Friction coefficient increases with increasing coating surface temperature from 0.55-0.64 at $25^{\circ}C$ to 0.65-0.76 at $500^{\circ}C$ due to the increase of adhesion between coating and counter sliding surface. Hardness of nWC-Co is higher or comparable to those of other hard coatings, such as $Al_2O_3,\;Cr,\;Cr_2O_3$ and HVOF Tribaloy 400 (T400). This shows that nWC-Co is recommendable for durability improvement coating on machine components such as high speed spindle.

• Journal of Sericultural and Entomological Science
• /
• v.43 no.1
• /
• pp.41-48
• /
• 2001

The purification, dissolution and powdering of stained waste silk obtained from weaving and dyeing process were studied for the surface modification of textile fabric and plastic materials. The whiteness of stained waste silk could be improved through degumming and bleaching with sodium hydrosulfite. The water-soluble fibroin solution can be obtained by dissoving the degummed waste silk in a boiling solution of 50% calcium chloride for 60 minutes. The salts and heavy metals contained in fibroin solution were removed by electric dialysis, wool fiber filtration and gel filtration chromatography. The fibroin powder was prepared by using a fine grinder after the alkali treatment for weakening the silk fiber. The fine fibroin powder of particle size around 30 ㎛ was obtained with a ultra fine-mill, while it was finer below 10 ㎛ with a ball-mill. The dissolved or powdered silk was applied to the surface of fabric with addition of the binder (a urethane resin). The moisture content of polyester and nylon fabrics treated with the silk solution was improved due to hygroscopic property of silk. The fine fibroin powder mixed with the binder ws coated on the surface of synthetic film by use of the air pressed sprayer. It was revealed that the hygroscopicity as well as the softness of fibroin powder coated film was much improved. Therefore, it is thought that the fine silk fibroin powder is applicable as an coating agent for the surface modification of plastic and synthetic leather.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.242-247
• /
• 2017

In this study, the electroless nickel plating method has been investigated for the coating of Ni nanoparticles onto fine Al powder as promising energetic materials. The adsorption of nickel nanoparticles onto the surface of Al powders has been studied by varying various process parameters, namely, the amounts of reducing agent, complexing agent, and pH-controller. The size of nickel nanoparticles synthesized in the process has been optimized to approximately 200 nm and they have been adsorbed on the Al powder. TGA results clearly show that the temperature at which oxidation of Al mainly occurs is lowered as the amount of Ni nanoparticles on the Al surface increases. Furthermore, the Ni-plated Al powders prepared for all conditions show improved exothermic reaction due to the self-propagating high-temperature synthesis (SHS) between Ni and Al. Therefore, Al powders fully coated by Ni nanoparticles show the highest exothermic reactivity: this demonstrates the efficiency of Ni coating in improving the energetic properties of Al powders.

• Korean Journal of Metals and Materials
• /
• v.47 no.5
• /
• pp.290-296
• /
• 2009

We report on the effects of mixing of powders with various particle sizes on fracture toughness and wear resistance of thermally sprayed WC-10Co-4Cr coating layers fabricated by HVOF (high-velocity oxygen fuel) process. The size and the mixing ratio of powders were changed in order to get high fracture toughness and wear resistance. The mixing of small amount of coarse powders with fine powders resulted in the highest fracture toughness and wear resistance due to the lowest porosity in coating layers.

• Journal of Welding and Joining
• /
• v.21 no.4
• /
• pp.39-45
• /
• 2003

Nano-TiO$_2$ photocatalytic coatings were deposited on the stainless steel 304(50$\times$70$\times$3mm) by the APS(Atmospheric Plasma Spraying). Photocatlytic reaction was tested in MB(methylene blue) aqueous solution. For applying nano-TiO$_2$ powders by thermal spray, the starting nano-TiO$_2$ powder with 100% anatase crystalline was agglomerated by spray drying. Plasma second gas(H$_2$) flow rate and spraying distance were used as principal process parameters which are known to control heat enthalpy(heat input). The relationship between process parameters and the characteristics of microstructure such as the anatase phase fraction and grain size of the TiO$_2$ coatings were investigated. The photo-decomposition efficiency of TiO$_2$ coatings was evaluated by the kinetics of MB aqueous solution decomposition. It was found that the TiO$_2$ coating with a lower heat input condition had a higher anatase fraction, smaller anatase grain size and a better photo-decomposition efficiency.

• Journal of Korean Society of Water and Wastewater
• /
• v.13 no.3
• /
• pp.101-106
• /
• 1999

This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.

• Applied Chemistry for Engineering
• /
• v.24 no.2
• /
• pp.126-131
• /
• 2013

BGsome coating on the surface of illite powder was attempted to impart skin affinity and improve various characteristics of the powder for makeup cosmetics. BGsome is a type of hydrated liquid crystalline vesicles prepared by the hydration of 1,3-butylene glycol (BG) dissolved lecithin. BGsome droplets were coated through wet process and the coated powders were analyzed by TGA, SEM, and particle size measurements. Effect of BGsome coating on the physical properties, such as flow-ability, dispersibility, spreadability, and adhesion, were examined. The repose angle of BGsome-coated illite was decreased, which means that BGsome coating improves the flowability of the powder. Dispersibility, spreadability, and adhesion of the coated illite were also improved remarkably. The result of adhesion tests showed that the BGsome-coated illite was evenly adhered onto artificial leather surface with almost no lumps. The flowability, dispersibility, spreadability and adhesion of face powders containing the BGsome-coated illite were also improved.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.11
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.15-20
• /
• 2016

Niobium is one of the most important and rarest metals, and is used in the electronic and energy industries. However, it's extremely high melting point and oxygen affinity limits the manufacture of Nb coating materials. Here, a Nb coating material is manufactured using a kinetic spray process followed by hot isotactic pressing to improve its properties. OM (optical microscope), XRD (X-ray diffraction), SEM (scanning electron microscopy), and Vickers hardness and EPMA (electron probe micro analyzer) tests are employed to investigate the macroscopic properties of the manufactured Nb materials. The powder used to manufacture the material has angular-shaped particles with an average particle size of $23.8{\mu}m$. The porosity and hardness of the manufactured Nb material are 0.18% and 221 Hv, respectively. Additional HIP is applied to the manufactured Nb material for 4 h under an Ar atmosphere after which the porosity decreases to 0.08% and the hardness increases to 253 Hv. Phase analysis after the HIP shows the presence of only pure Nb. The study also discusses the possibility of using the manufactured Nb material as a sputtering target.

• Journal of Powder Materials
• /
• v.5 no.1
• /
• pp.28-34
• /
• 1998

Plasma sprayed ceramic coatings are widely used in various industrial fields to improve their properties or to reduce the production cost. The ceramic powders for plasma spray coating have been mainly manufactured by spray drying or fused+crushed process. In this study, chromium oxide which has better mechanical properties than those of the other ceramic was selected and agglomerated chromium oxide powders for plasma spray coating were produced by spray drying process with a various processing condition. The large hollow powders and the harsh surfaced powders are formed at high slurry feed rate more than 163 g/min. and low binder concentration less than 2wt%, respectively. These powders cause the considerable decrease of flowability and apparent density. The powders produced by spray drying process have the spherical shape with the mean size of 45 ${\mu}m$, but these are shown lower apparent density and flowability than the powders produced by fused+crushed powders. The plasma spray coated layers by spray dried powders are shown a different microstructure with that by fused+crushed powders in porosity shape, but their properties such as density, hardness and bond strength are similar.