Abstract
This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.