• Journal of the Korean Society of Radiology
• /
• v.14 no.4
• /
• pp.391-396
• /
• 2020

In this study, we developed a phosphor film screen that can be applied to radiographs during non-destructive testing using Gd₂O₂S:Tb phosphor compounds. The image uniformity of the fabricated phosphor screen film was analyzed by FE-SEM, RMS and RDS analysis. In addition, the tensile strength, elongation, and modulus of elasticity of the Gd₂O₂S:Tb phosphor screen were evaluated by measuring the stress-strain characteristic curve. As a result, it was evaluated that the RSD value had an excellent image uniformity within 10% of the evaluation criteria. In addition, as a result of evaluation of physical properties, the tensile strength was 1.1760 N/㎟, the tensile strength at break was 1.1515 N/㎟. These results suggest that the Gd₂O₂S:Tb phosphor screen fabricated using the room temperature gel-printing method could be applied to digital radiography detectors for radiography.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.29 no.2
• /
• pp.33-44
• /
• 2011

The inorganic powder EL lamp was made by screen printing technique with a phosphor ink and a dielectric ink. The thickness of a phosphor ink layer and a dielectric ink layer is $35{\mu}m$ and $54{\mu}m$ respectively. A increasing ratio of the luminance of inorganic powder EL lamp to be a 1P1PD-phosphor ink layer in which increased voltage at constant frequency is higher 12% than when increased frequency at constant voltage. It is higher 57% than when increased frequency at constant voltage that the rate of increase of the luminance of inorganic powder EL lamp to be a 2PD-phosphor ink layer in which increased voltage at constant frequency. Finally, when increased voltage at constant frequency, a increasing ratio of the luminance of inorganic powder EL lamp to be a 2PD-phosphor ink layer is higher about 40% than that to be a 1P1PD-phosphor ink layer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.749-753
• /
• 2006

The $ZnGa_2O_4$ phosphor thick films were fabricated using a screen printing method on Si(100) substrates at various sintering temperatures. The XRD patterns show that the $ZnGa_2O_4$ thick films have a (311) main peak and a spinel structure with increasing sintering temperatures. The particle sizes of $ZnGa_2O_4$ phosphor were about 100 nm and the thickness of $ZnGa_2O_4$ thick film was $10{\mu}m$. The CL and PL properties of $ZnGa_2O_4$ showed main peak of 420nm and maximum intensity at the sintering temperature of $900^{\circ}C$. These results indicate that $ZnGa_2O_4$ phosphor thick films hold promise for displays such as plasma display panel and field emission display.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.1
• /
• pp.11-15
• /
• 2011

In this study, $ZnGa_2O_4$ phosphors in its application to field emission displays and electroluminescence were synthesized through the precipitation method and $Mn^{2+}$ ions. A green luminescence activator, $Cr^{3+}$ ions, and a red luminescence activator were separately doped into $ZnGa_2O_4$, which was then screen printed to an indium tin oxide substrate. The thick films of the $ZnGa_2O_4$ were deposited with the various thicknesses using nano-sized powder. The best luminescence characteristics were shown at a thickness of 60 ${\mu}m$. Additionally, green-emission $ZnGa_2O_4:Mn^{2+}$ and red-emission $ZnGa_2O_4:Cr^{3+}$ phosphor thick films, which have superior characteristics, were manufactured through the screen-printing method. These results indicate that $ZnGa_2O_4$ phosphors prepared through the precipitation method have wide application as phosphor of the full color emission.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.454-459
• /
• 2013

Recently, remote phosphors have been reported for application to white LEDs to provide enhanced phosphor efficiency compared with conventional phosphor-based white LEDs. In this study, a remote phosphor was produced by coating via screen printing on a glass substrate with different numbers of phosphor coating. The paste consists of phosphor, lowest softening glass frits, and organic binders. The remote phosphor could be well controlled by varying the phosphor content rated paste. After mounting the remote phosphor on top of a blue LED chip, CCT, CRI, and luminance efficiency were measured and values of 5300 K, 62, and 117 lm/W were respectively obtained in the 80 wt% phosphor with 3 coating layers sintered at $800^{\circ}C$.

• Clean Technology
• /
• v.14 no.1
• /
• pp.14-20
• /
• 2008

In this study we have manufactured and characterized the low temperature calcined phosphor paste that can be used as a flat light source for LCD BLU. For the phosphor paste, the low temperature calcined acryl resin was used as the binder. From the result of thermal decomposition measurement, residual carbonaceous materials was found to be less than 0.1 wt% at $400^{\circ}C$. A flat light source device that was made by screen printing using the manufactured paste showed a near 100% luminous efficiency compared to the luminance of the phosphor.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.330-334
• /
• 2013

We developed a package of remote phosphor structure having blue LED chips and phosphors physically separated, and the characteristics were evaluated according to different classifications of phosphor coatings. Remote phosphor was produced by screen printing coating on glass substrate with phosphor content rated paste and heat treatment. After mounting Remote phosphor, which has been classified according to number of coatings, on top of blue LED chips, luminous flux, luminous efficacy, CCT and CRI were measured. The measurement results showed the most suitable characteristics of white LED package as a general light source when the content rate of phosphor in Remote phosphor was 80 wt.% with 3 layers of coatings and thickness over $12{\mu}m$.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.30 no.1
• /
• pp.47-58
• /
• 2012

The inorganic powder EL lamp was made by screen printing technique with a phosphor ink and a dielectric ink. Value of color coordinates X and Y increased under the condition of supplying driving power to the inorganic powder EL lamp and changing voltage with constant frequency. When frequency was changed under the constant voltage, value of color coordinates X and Y were decreased with increasing frequency. However, level of change of color coordinates X was different from color coordinates Y. When voltage was increased under constant frequency, changing degree of color coordinates X and Y shows similarity. But under the constant voltage with changing frequency, color coordinates X and Y were differently changed that degree of change of color coordinates Y showed five times more than that of color coordinates X. As increasing thickness of phosphor ink and dielectric ink, level of voltage and frequency, color coordinates X and Y were slightly changed. According to the thickness of phosphor ink and dielectric ink, and level of voltage and frequency, color coordinate of color light was changed. Frequency was most important element influencing on the change of color coordinate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.1060-1062
• /
• 2002

Spherical and dense BAM phosphor particles were prepared by spray pyrolysis. The key idea of dense BAM particles is to lead gelation in droplets, which was successfully achieved by using the aluminum polycation as the precursor solution for the spray pyrolysis. The BAM phosphor particles prepared by spraying the aluminum polycation solution have completely spherical shape and dense structure. When directly applied to make phosphor film on the glass by the screen-printing method, the prepared spherical BAM phosphor particles showed better packing density and surface morphology than that of commercial one, which has irregular shape and large particle size. It was also found that the thermal degradation in the photoluminescence intensity for dense and spherical BAM particles was less than that of commercial one.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.30 no.3
• /
• pp.30-38
• /
• 2016

In this research, a 6W white LED package with a Glass Remote Phosphor was developed to improve the life of an LED package. The Glass Remote Phosphor was fabricated by the Phosphor in Glass (PiG) method, wherein phosphor YAG:Ce was mixed with glass frit and then heat treated. A paste with 75wt.% of a phosphor substance and 25wt.% glass frit was coated on a glass substrate two times using the screen-printing technique and heat-treated at $800^{\circ}C$ ; this structure gave a luminous efficacy of 136.1lm/W, color rendering index of 74Ra, and color temperature of 5,342K, thus satisfying the requirements as a light source for lighting. Moreover, an IES LM-80 accelerated life test was conducted on the same LED package for 6,000h in order to estimate the L70 lifetime based on IES TM-21. The results showed guaranteed lifetimes of 213,000h at $55^{\circ}C$, 245,000h at $85^{\circ}C$, and 209,000h at $95^{\circ}C$.