• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.842-851
• /
• 2009

The long-term reliability of Sn-0.3wt%Ag-0.7wt%Cu solder joints was evaluated and compared with Sn-3.0wt%Ag-0.5wt%Cu under thermal shock conditions. Test vehicles were prepared to use Sn-0.3Ag-0.7Cu and Sn-3.0Ag-0.5Cu solder alloys. To compare the shear strength of the solder joints, 0603, 1005, 1608, 2012, 3216 and 4232 multi-layer ceramic chip capacitors were used. A reflow soldering process was utilized in the preparation of the test vehicles involving a FR-4 material-based printed circuit board (PCB). To compare the shear strength degradation following the thermal shock cycles, a thermal shock test was conducted up to 2,000 cycles at temperatures ranging from $-40^{\circ}C$ to $85^{\circ}C$, with a dwell time of 30 min at each temperature. The shear strength of the solder joints of the chip capacitors was measured at every 500 cycles in each case. The intermetallic compounds (IMCs) of the solder joint interfaces werealso analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results showed that the reliability of Sn-0.3Ag-0.7Cu solder joints was very close to that of Sn-3.0Ag-0.5Cu. Consequently, it was confirmed that Sn-0.3Ag-0.7Cu solder alloy with a low silver content can be replaced with Sn-3.0Ag-0.5Cu.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.2
• /
• pp.63-67
• /
• 2011

We investigated effects of bonding conditions on the peel strength of rigid printed circuit board (RPCB)/ flexible printed circuit board (FPCB) joints bonded using a thermo-compression bond method, The electrodes on the FPCB were coated with Sn by a dipping process. We confirmed that the bonding temperature and bonding time strongly affected the bonding configuration and strength of the joints. Also, the peel strength is affected by dipping conditions; the optimum dipping condition was found to be temperature of $270^{\circ}C$ and time of 1s. The bonding strength linearly increased with increasing bonding temperature and time until $280^{\circ}C$ and 10s. The fracture energy calculated from the F-x (Forcedisplacement) curve during a peel test was the highest at bonding temperature of $280^{\circ}C$.

• Korean Journal of Crystallography
• /
• v.8 no.1
• /
• pp.38-47
• /
• 1997

A new weighing sensor for the automatic diameter control system of the crystal growth is developed in this study. This weighing sensor measures the frequency of the vibrating element which is lineally changing with respect to weight. The signal and the power of this system are transmitted without any physical contact, so that this sensor offers high accuracy and resolution. This system consists of a string, a sinusoidal wave generator, an automatic amplification adjusting circuit, signal transformers and a PCB. 4 kinds of programs are developed for checking DAC, weight calibration and controlling growth process. The measurements of the standard deviation and the resolution show $\pm0.10g$(measured at every second) and $5{\times}10^{-5}$, respectively, This weighing sensor is effective under high pres-sure of 200 atm, high temperature and vacuum condition. The weighing system can control the temperature in the accuracy of $\pm0.025^{\circ}C$ with the 'signal divider'. The optical quality single crystals of $(YGd)_3Sc_2Ga_3O_{12},\;Er-Y_3Sc_2Al_3O_{12},\;and\;Bi_{12}GeO_{20}$ have been grown by Czo-chralski method using this auto-diameter control system.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.6
• /
• pp.568-578
• /
• 2010

In this study, the possibility of biodegradation of polychlorinated biphenyls (PCBs) by various white rot fungi was evaluated, and outstanding white rot fungi for the degradation of PCBs were selected. Seven white rot fungi were used to degrade Aroclor 1254 and 1260, which are widely considered to be toxic and difficult to degrade. And the degradation rates of Aroclors by selected white rot fungi were performed by GC analysis. Through the resistance test of white rot fungi on different concentrations of PCBs, the inhibition of mycelial growth of Cystidodontia isubellina was much less than that of others, and this fungus grew faster than others, relatively. Based on this result, it was considered that C. isubellina was selected as degrading fungus for Aroclors. As a result of biodegradation rate of Aroclors by Cystidodontia isubellina, the degradation rate of Arolor 1254 was reached to 57.57% in 13 days, which showed very high degradation rate. Also the degradation rate of Aroclor 1260 by C. isubellina had a tendency of increasing along with increasing incubation day. Maximal degradation rate of Aroclor 1260 was 49.43% at 13 days. Based on this results, it indicated that in comparison with a previous study, high degradation rate was obtained by C. isubellina.

• Journal of Welding and Joining
• /
• v.25 no.2
• /
• pp.82-88
• /
• 2007

Sn-3.0Ag-0.5Cu lead fee solder was generally utilized in electronics assemblies. But it is insufficient to research about activation energy(Q) that is applying to evaluate the solder joint reliability of environmental friendly electronics assemblies. Therefore this study investigated Q values which are needed to IMC formation and growth of Sn-3.0Ag-0.5Cu/Cu and Sn-40pb/Cu solder joints during aging treatment. We bonded Sn-3.0Ag-0.5Cu and Sn-40Pb solders on FR-4 PCB with Cu pad$(t=80{\mu}m)$. After reflow soldering, to observe the IMC formation and growth of the solder joints, test specimens were aged at 70, 150 and $170^{\circ}C$ for 1, 2, 5, 20, 60, 240, 960, 15840, 28800 and 43200 min, respectively. SEM and EDS were utilized to analysis the IMCS. From these results, we measured the total IMC$(Cu_6Sn_5+Cu_3Sn)$ thickness of Sn-3.0Ag-0.5Cu/Cu and Sn-40Pb/Cu interface, and then obtained Q values for the IMC$(Cu_6Sn_5,\;Cu_3Sn)$ growth of the solder joints.

• Journal of Welding and Joining
• /
• v.34 no.1
• /
• pp.26-34
• /
• 2016

Automotive today has been transforming to an electronic product by adopting a lot of convenience and safety features, suggesting that joining materials and their mechanical reliabilities are getting more important. In this study, a Sn-Cu-Cr-Ca solder composition having a high melting temperature ($>230^{\circ}C$) was fabricated and its joint properties and reliability was investigated with an aim to evaluate the suitability as a joining material for electronics of engine room. Furthermore, mechanical properties change under complex environment were compared with several existing solder compositions. As a result of contact angle measurement, favorable spreadability of 84% was shown and the average shear strength manufactured with corresponding composition solder paste was $1.9kg/mm^2$. Also, thermo-mechanical reliability by thermal shock and vibration test was compared with that of the representative high temperature solder materials such as Sn-3.5Ag, Sn-0.7Cu, and Sn-5.0Sb. In order to fabricate the test module, solder balls were made in joints with ENIG-finished BGA and then the BGA chip was reflowed on the OPS-finished PCB pattern. During the environmental tests, resistance change was continuously monitored and the joint strength was examined after tests. Sn-3.5Ag alloy exhibited the biggest degradation rate in resistance and shear stress and Sn-0.7Cu resulted in a relatively stable reliability against thermo-mechanical stress coming from thermal shock and vibration.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.1 s.34
• /
• pp.9-16
• /
• 2005

This paper presents the development of new anisotropic conductive adhesives with enhanced thermal conductivity for the wide use of adhesive flip chip technology with improved reliability under high current density condition. The continuing downscaling of structural profiles and increase in inter-connection density in flip chip packaging using ACAs has given rise to reliability problem under high current density. In detail, as the bump size is reduced, the current density through bump is also increased. This increased current density also causes new failure mechanism such as interface degradation due to inter-metallic compound formation and adhesive swelling due to high current stressing, especially in high current density interconnection, in which high junction temperature enhances such failure mechanism. Therefore, it is necessary for the ACA to become thermal transfer medium to improve the lifetime of ACA flip chip joint under high current stressing condition. We developed thermally conductive ACA of 0.63 W/m$\cdot$K thermal conductivity using the formulation incorporating $5 {\mu}m$ Ni and $0.2{\mu}m$ SiC-filled epoxy-bated binder system to achieve acceptable viscosity, curing property, and other thermo-mechanical properties such as low CTE and high modulus. The current carrying capability of ACA flip chip joints was improved up to 6.7 A by use of thermally conductive ACA compared to conventional ACA. Electrical reliability of thermally conductive ACA flip chip joint under current stressing condition was also improved showing stable electrical conductivity of flip chip joints. The high current carrying capability and improved electrical reliability of thermally conductive ACA flip chip joint under current stressing test is mainly due to the effective heat dissipation by thermally conductive adhesive around Au stud bumps/ACA/PCB pads structure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.412-412
• /
• 2008

ENIG(Electroless Nickel Immersion Gold)is a surface treatment method that is used most widely at fine pitch's SMT and BGA packaging process. ENIG has good diffusion barrier of Ni against solder and good wettability due to Au finish. But when the discoloration occurred on the Au finish of ENIG, some key characteristics related to the quality and reliability of PCB such as bondability, solderability and electrical flowing of packaging process could be deteriorated. In this paper, we have performed the water dip test ($88^{\circ}C$ purified water) which accelerates the galvanic corrosion of Ni diffused from the Ni-P layer. That is, the excessive oxidation of the Ni layer could result in non-wetting of the solder because the flux may not be able to remove excessive oxides. Though Au discoloration have been reported to be caused by Ni oxides in many literature, it is still open to verify and discuss The microstructures and chemical compositions have been investigated using FE-SEM, TEM, FIB, EDS and XPS. As a result, authors have found that the Au discoloration in ENIG type is severely caused by the oxidation of the Ni and the mechanism of Au discoloration can be confirmed through the experiment result of water dip test.

• Journal of computational fluids engineering
• /
• v.18 no.1
• /
• pp.63-68
• /
• 2013

The purpose of this study is to investigate the cooling performance of radial heat sink used for high power LED lightings by natural convection cooling with surrounding air. Experimental and numerical analyses are carried out together. Parametric studies are performed to compare the effects of geometric parameters in radial heat sink such as the number of fins, fin height, fin length, and thickness of fin base as well as the surface coatings of radial heat sink. In this study, the cooling of 60 W LED lamp is examined with radiative heat transfer considered as well as natural convection. Numerical results show the optimum condition when the number of fin is 40, heat sink height is 120 mm, fin length is 15 mm, and fin base thickness is 3 mm. The difference in temperature of the LED metal PCB is within $1^{\circ}C$ between numerical analyses and experimental results. Also, the CNT coating on the heat sink surface is found to increase the cooling performance significantly.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.77-77
• /
• 2009

ELV(; End of Life Vehicles)를 비롯한 최근 환경 동향은 자동차 전장 모듈에 대하여 다양한 무연 솔더 적용을 요구하고 있다. 특히 자동차 엔진룸과 트랜스미션은 가동 중 고온 및 진동의 지속적인 영향을 받기 때문에 이와 유사한 환경에서의 신뢰성 연구가 필요한 시점이다. 이에 본 연구에서는 Sn3.5Ag, Sn0.7Cu, Sn5.0Sb 솔더 조성에 대하여 복합환경 조건하에서 접합부 신뢰성을 평가하였다. 복합환경을 구현하기 위하여 $-40{\sim}150^{\circ}C$ 범위의 온도 사이클과 랜덤 진동을 동시에 인가하였으며, 진동 가속도 3G, 진동주파수는 10~1000Hz 로 설정하여 자동차 환경을 충족하였다. 복합시험의 1 cycle 은 20 시간이며, 총 120 시간의 시험 동안 진동의 영향 및 진동과 고온이 동시에 작용하였을 경우의 영향에 대해 비교하였다. 테스트 모듈 제작을 위해 450 um 의 솔더볼이 적용되었으며, 각 조성의 솔더볼을 이용하여 BGA test chip 제작하였고, 제작된 BGA test chip 은 다시 daisy chain PCB 위에 실장 및 리플로우 공정을 통해 접합되었다. 테스트 동안 In-situ 로 저항의 변화를 관찰하여 파단의 유무를 판단하였고 전자주사현미경을 통해 파괴 기전을 평가하였다. 복합시험 시간에 따른 전단강도를 측정하였으며, 각 조성에 대하여 상이한 전단강도 변화를 관찰하였다. 계면 IMC 형상은 전단강도 변화에 영향을 주었으며, 특히 높은 온도가 IMC 성장을 촉진시켜 전단강도 감소에 영향을 주었다. 본 복합환경 시험 조건에서는 Sn0.7Cu 가 가장 안정적이었으며, 파단면을 관찰한 결과 연성파괴 모드가 관찰되었다.