• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.185-192
• /
• 2002

Rigid polyurethane foams (PUFs) were prepared from polymeric 4.4'-diphenyl-methane diisocyanate (PMDI), polyether polyol, 1,4-butane diol, silicone surfactant, and distilled water. The density of the PUF was decreased from 173.7 to 41.7 kg/㎥ with an increase in distilled water from 0.5 to 3.0 php (parts per hundred polyol by weight), respectively, at the 0 php butane diol. The cell size of the PUF increased from 115 to 258 $mu extrm{m}$ with an increase in the amount of distilled water from 0.5 to 3.0 php, respectively, at the 10 php butane diol. It was found that the compressive strength of the PUF increased with the content of distilled water, at the same density. Out of the study for the surfactant effect on the properties of the PUF, it was observed that the cell site of the PUF decreased from 360 to 146 $mu extrm{m}$ with an increase in the amount of the surfactant from 0 to 0.33 php, respectively, but the tell size did not change significantly when the amount of the surfactant exceeded 0.33 php.

• Polymer(Korea)
• /
• v.38 no.4
• /
• pp.441-448
• /
• 2014

Polyurethane/melamine phosphate composite foam (MP-PUF) was prepared from poly(adipate)diol/melamine phosphate composite (f=2), polyether-polyol (f=4.6), and PMDI (f=2.5). The thermal properties of MP-PUF such as morphology, closed-cell content, thermal conductivity, and thermal stabilities were characterized. Water was used as a blowing agent, and the composition of melamine phosphate (MP) was maintained at $1.43{\pm}0.3wt%$ of MP-PUF. As the content of water increased, the thermal conductivity of pure polyurethane foam (PUF) decreased, whereas the thermal conductivity of MP-PUF increased. The thermal stabilities of the PUF and the MP-PUF were maximized at 5 php $H_2O$, and then decreased at the higher $H_2O$ contents. The thermal stabilities of MP-PUF were greatly enhanced due to the synergetic effect of MP and urea, which was generated during the blowing process. The temperature of 50% residual mass of MP-PUF increased to $370{\sim}450^{\circ}C$ and the temperature of 30% residual mass exceeded over $700^{\circ}C$. Compared to the PUF, the temperature of 50% residual mass and 30% residual mass were higher than 25 and $70^{\circ}C$, respectively.

• Journal of Korea Society of Industrial Information Systems
• /
• v.27 no.4
• /
• pp.11-18
• /
• 2022

A physically unclonable function (PUF) is a circuit that generates random numbers by exploiting natural variation. Since it utilizes variations, which cannot be fully controlled, it can be used to generate true random numbers, but environment change may distort the output. In this paper, we propose a PUF with a confidence signal. We designed a PUF that exploits the difference of the time constant of the circuit and verified that different PUFs generate distinct outputs and the same PUF keeps generating similar outputs regardless of the temperature change. Compared to the existing technique, which employs an error correction code, the proposed technique offers the same level of reliability at the 700 times smaller overhead.

• Macromolecular Research
• /
• v.15 no.7
• /
• pp.676-681
• /
• 2007

A process designed to synthesize rigid polyurethane foam (PUF) with insulative properties via the modulation of PUF cell size via the addition of clay and the application of ultrasound was assessed. The blowing agents utilized in this study include water, cyclopentane, and HFC-365mfc, all of which are known to be environmentally-friendly blowing agents. The rigid PUFs were prepared from polymeric 4,4'-diphenylmethane diisocyanate (PMDI) and polyether polyol with a density of $50kg/m^3$. In addition, rigid PUFs/clay nanocomposites were synthesized with clay modified by PMDI with and without the application of ultrasound. The PUF generated using water as a blowing agent evidenced the highest tensile strength. The tensile strength of the PUF/nanocomposites was higher than that of the neat PUF and the strength was even higher with the application of ultrasound. The cell size of the PUF/clay nanocomposites was less than that of the neat PUF, regardless of the type of blowing agent utilized. It appears that the higher tensile strength and lower cell size of the PUF/clay nanocomposites may be attributable to the uniform dispersion of the clay via ultrasonic agitation. The thermal conductivity of the PUF/clay nanocomposites generated with HCFC-141b evidenced the lowest value when PUF/clay nanocomposites were compared with other blowing agents, including HFC-365mfc, cyclopentane, and water. Ultrasound has also proven effective with regard to the reduction of the thermal conductivity of the PUF/clay nanocomposites with any of the blowing agents employed in this study. It has also been suggested that the uniformly dispersed clay particles in the PUF matrix function as diffusion barriers, which prevent the amelioration of the thermal insulation property.

• Applied Chemistry for Engineering
• /
• v.19 no.4
• /
• pp.427-431
• /
• 2008

The rigid polyurethane foams (PUF) were prepared using polyols with 90, 110, 130, and 150 isocyanate index. The effect of sea water on the physical properties of PUF with the increase in isocyanate (NCO) index and ageing time was investigated. Tensile strengths and compressive strengths of the PUFs decreased up to 10% and 7% with an increase in ageing time, respectively. Cell morphology of the PUF under sea water was turned out to be the same as that in the ambient condition. It was observed that $T_g$ and tensile modulus of the PUF under sea water increased. The results showed an additional cross-link reaction of non-reacted MDI and the change of NCO peak as observed from FT-IR spectrum.

• Korean Journal of Plant Resources
• /
• v.34 no.4
• /
• pp.377-383
• /
• 2021

In this study, we investigated in vitro immunostimulatory activity of fruit extracts from Pyrus ussuriensis var. hakunensis (Nakai) T.B. Lee (PUF) using mouse macrophage RAW264.7 cells. PUF increased the production of immunostimulatory factors such as NO, iNOS, IL-1β, IL-6 and TNF-α, and phagocytic activity in RAW264.7 cells. The inhibition of TLR2 and TLR4 blocked PUF-mediated production of immunostimulatory factors in RAW264.7 cells. In addition, the inhibition of MAPKs signaling pathway reduced PUF-mediated production of immunostimulatory factors. From these results, PUF may have immunostimulatory activity via TLR2/4-mediated activation of MAPKs signaling pathway. Therefore, PUF expected to be used as a potential immune-enhancing agent.

• KSBB Journal
• /
• v.16 no.1
• /
• pp.24-29
• /
• 2001

Recently hepatocyte-based bioartificial liver (BAL) and hepatocyte transplantation have been actively investigated to treat acute hepatic failure. The BAL acts as a bridge to provide patients with more time until a donor organ becomes available for transplantation or until their own liver can be regenerated. In this study, we manufactured a polyurethane foam (PUF) using 15% NCO-prepolymer with a pore opening that allows it to be used as a hepatocyte immobilizing material. Cubes of PUF (3 mm dim.) were seeded with rat primary hepatocytes at a density of 5.5$\pm$1.1$\times$ $10^6$ cells/$cm^3$ PUF by centrifuging them together. The cell laden PUF cubes were packed into a prototype reactor and perfused with a hormonally defined medium for a week. Hepatocytes in the pores of the PUF formed spheroids that showed stable ammonia removal and urea synthesis activities. The albumin production level was comparable to other BAL systems. The PUF packed hepatocyte bioreactor has the potential to be used as a BAL.

• Journal of Ocean Engineering and Technology
• /
• v.36 no.4
• /
• pp.217-231
• /
• 2022

Reinforced polyurethane foam (R-PUF), a material for liquefied natural gas cargo containment systems, is expected to have different mechanical properties depending on its stacking position of foaming as the glass fiber reinforcement of R-PUF sinks inside R-PUF under the influence of gravity. In addition, since R-PUF is not a homogeneous material, it is also expected that the coordinate direction within this material has a great correlation with the mechanical properties. So, this study was conducted to confirm this correlation with the one between the mechanical properties and the stacking position. In particular, in this study, R-PUF of 3 different densities (130, 170, and 210 kg/m³) was used, and tensile, compression, and shear tests of this material were performed under 5 temperatures. As a result of the tests, it was confirmed that the strength and modulus of elasticity of the material increased as the temperature decreased. Specifically, the strength and modulus of elasticity in the Z direction, which was the lamination direction, tended to be lower than those in the other directions. Finally, the strength and elastic modulus of different specimens of the material found at the bottom of their lamination compared to the specimens with these properties found at positions other than their lamination bottom were evaluated. Further analysis confirmed that as the temperature decreased, hardening of R-PUF occurred, indicating that the strength and modulus of elasticity increased. On the other hand, as the density of R-PUF increased, a sharp increase in strength and elastic modulus of R-PUF was observed.

• Polymer(Korea)
• /
• v.29 no.5
• /
• pp.457-462
• /
• 2005

Polyurethane foams (PUFs) were prepared from polymeric 4,4'-diphenylmethane diisocyanate (PMDI), mixed polyol with OH value of 480, silicone surfactant, three catalysts, and hydrofluorocarbon(HFC) as blowing agent. Balance (PC-8), gelling (33LV), and trimerization (TMR-2) catalysts were used. The effect of the catalysts on the physical properties of PUF with increase of isocyanate (NCO) index and aging time was investigated. The cell size of the PUF with PC-8 and 33LV slightly increased with an increase in NCO index from 100 to 170 but compressive strength did not change significantly. In case of trimerization catalyst, the compressive strength of PUF increased from 8.75 to 1$10.5 kg_f/cm^2$ and the cell size decreased with an increase in NCO index. The compressive strength of the PUF with 33LV increased from 9.21 to $10.15 kg_f/cm^2$ with an increase in aging time. However, there was no detectable change in the compressive strength of PUF with TMR-2. A possible interpretation of the results includes an additional cross-link reaction of non-reacted MDI and FTIR spectrum illustrated the change of NCO peak.

• Review of KIISC
• /
• v.33 no.6
• /
• pp.37-43
• /
• 2023

현재 사용되고 있는 RSA, ECC 등 비대칭키 암호알고리즘은 앞으로 나올 양자컴퓨터와 양자알고리즘의 빠른 계산 속도로 알고리즘의 비가역성이 깨질 수 있음이 알려졌다. 이는 공개키로부터 비밀키를 계산할 수 있음을 의미한다. 이를 극복하기 위해 미국 국립표준기술연구소 (NIST)는 최근에 양자 내성 암호 (PQC) 알고리즘 선정과 표준화 작업을 진행해 왔으며, 4차 라운드에 진입해 있다. PQC 알고리즘에 필요한 PQC 비밀키는 PQC 알고리즘이 구현된 칩 외부에서 주입하거나 칩 내부에서 자체 생성을 하여 사용하는데, 이 비밀키를 비휘발성 메모리 (NVM) 등에 저장한다. 만약 시스템의 보안 취약성으로 인해 비밀키가 노출된다면 아무리 PQC 알고리즘이 강력해도 전체 시스템이 무너진다. 즉, 알고리즘의 수학적 능력과 무관하게 해당 보안 시스템은 무력화되는 것이다. 본 논문에서는 물리적 복제 방지 기능 (PUF)을 사용하여PQC 비밀키를 안전하게 보호하고, 이를 기반으로 전체 시스템을 보호할 것을 제안한다. PQC 비밀키가 외부에서 주입되면 해당키는 NVM에 저장되기 전에 PUF 키로 암호화 될 수 있다. PUF 값에서 파생되는 PUF 키는 필요할 때 마다 다시 만들어서 사용이 가능하므로 메모리에 저장할 필요가 없으며, 따라서 외부 공격에 PUF 키가 노출 되지 않는다. 반도체 수동소자로 이루어지는 Via PUF 기술은 최악의 환경 변화에도 그 특성이 유지되는 가장 최적의 PUF 기능을 제공한다.