• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.5
• /
• pp.1592-1596
• /
• 2010

According to the increase of the channel length with fixed width/length, characteristic curves of drain current as a function of gate bias voltage of indium gallium zinc oxide (IGZO) thin-film transistors moved to a positive direction of gate voltage, and field-effect mobility decreased. In case of fixed length and width of channel, field-effect mobility was lower and subthreshold slope was larger when drain bias voltage was higher. Due to large work function of IGZO, band bending at the junction region between IGZO channel and source/drain electrodes was expected to be in opposite direction to that between silicon and metal electrodes; this could explain the above results.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.7
• /
• pp.510-514
• /
• 2013

In order to prevent heat loss that occurs through the glass, low-emissivity (Low-E) coating methods with good insulating properties and high transmittance were used. InGaZnO/Ag/InGaZnO (IGZO/Ag/IGZO) multilayer thin films have been deposited on XG glass substrate by RF magnetron sputtering. Depending on the different thickness of Ag in multilayer films, the structural and optical properties of Low-E multilayer films were analyzed. By XRD analysis results, the multilayer thin films were observed to be amorphous structure regardless of Ag thickness. According to the AFM results, surface morphology of the multilayer films was observed and compared. Using UV-VIS spectroscopy, low emissivity property has been observed clearly with the transmittance of higher than 85% at visible range and lower than 30% at IR range.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.5
• /
• pp.208-213
• /
• 2020

In this research, design optimization was investigated using the finite element analysis and the optimal design technique based on the PQRSM algorithm to minimize the thermal deformation of IGZO oxide in a target module in which IGZO oxide and a copper backplate are bonded to each other. In order to apply the optimal design technique in conjunction with finite element analysis, the x-coordinate of lower supports and upper fixed boards used as design valuables, and the optimal design was performed to minimize the thermal displacement of IGZO materials as the objective function. After the optimization process, the thermal displacement within IGZO oxide could be reduced to 42 % comparing with the initial model. The result is thought to be useful in the industry as it can reduce the thermal deformation of target oxides materials only by changing the position of the subsidiary materials during the bonding process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.215.1-215.1
• /
• 2015

본 연구에서는 용액 공정 기반 ZrO2 절연막의 우수한 특성을 확인하기 위해 SiO2 절연막을 가지는 IGZO (Indium-Gallium-Zinc Oxide) 박막 트랜지스터와 비교했다. In:Ga:Zn=1:1:1의 비율의 0.3 M IGZO 용액과 0.2 M ZrO2용액을 사용하였다. ZrO2 박막 트랜지스터는 0.2M ZrO2 용액을 5번 반복 증착하며 140nm 두께의 ZrO2 절연막을 가지는 IGZO 박막 트랜지스터와 비교대상으로 동일한 두께의 SiO2의 절연막을 가지는 IGZO 박막 트랜지스터를 제작하였다. ZrO2 박막 트랜지스터의 문턱전압은 4.3V로 SiO2 박막 트랜지스터의 -6.1V보다 낮았고, 이동도는 $1.2356cm^2/V{\cdot}s$로 $0.0554cm^2/V{\cdot}s$ 보다 약 20배 높았다. 실험 결과를 통해 ZrO2를 절연막으로 사용한 박막 트랜지스터의 특성이 더 향상되었음을 확인하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.43.1-43.1
• /
• 2011

Hydrogenated amorphous Si (a-Si:H), low temperature poly Si (LTPS) 등 기존 thin film transistors (TFTs)에 사용되던 채널 물질을 대체할 재료로써 다양한 연구가 진행되고 있는 amorphous indium-gallium-zinc-oxide (a-IGZO)는 TFT에 적용하였을 때 뛰어난 전기적 특성과 재연성을 나타낼 뿐만 아니라 넓은 밴드갭을 가져 투명소자로도 응용이 가능하다. 본 연구에서는 a-IGZO의 열처리에 따른 소자의 전기적 특성과 조성 분포의 관계를 확인하기 위해 다음과 같이 실험을 진행하였다. Si/SiO2 기판 위에 DC sputter를 이용하여 IGZO를 증착하고 $350^{\circ}C$에서 열처리를 한 후 evaporator로 Al 전극을 형성시켰다. 이 때 전기적 특성의 변화를 비교하기 위해 열처리 한 샘플과 열처리 하지 않은 샘플에 대해 I-V 특성을 측정하였고, 채널 내부의 조성 분포 변화를 transmission electron microscopy (TEM)의 energy dispersive spectrometer (EDS)를 이용하여 관찰하였다. 그 결과 열처리 된 a-IGZO 채널 층의 산소 비율이 감소하였으며 전체적인 조성이 고르게 분포 되었고 전기적 특성은 향상되었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.321-324
• /
• 2013

In this study, The RF magnetron sputter and evaporator was on glass substrates 30 mm ${\times}$ 30 mm OMO multilayer thin film structure is applied to the low-e. Structural and optical properties, a thin film was produced, the variable was placed into a variable deposition time of the oxide layer. According to the XRD measurement results there is no peak that satisfies the Bragg's law ($2dsin{\theta}=n{\lambda}$) which confirmed that it is an amorphous structure. RMS value of the results of the AFM measurement, has a roughness of less than 2 nm. transmittance measurements results, visible light region an average 80%, IR region 40% showed.

• Journal of Information Display
• /
• v.10 no.4
• /
• pp.171-174
• /
• 2009

The optical and electrical properties of the amorphous indium gallium zinc oxide thin-film transistor ($\alpha$-IGZO TFT) were studied. When the $\alpha$-IGZO TFT was illuminated at a wavelength of 660 nm, the off-state drain current slightly increased, while below 550 nm it increased significantly. The $\alpha$-IGZO TFT was found to be extremely sensitive, with deep-level defects at approximately 2.25 eV near the midgap. After UV light illumination, a slight change occurred on the surface of the $\alpha$-IGZO films, such as in terms of the oxygen 1s spectra, resistivity, and carrier concentrations. It is believed that these results will provide information regarding the photo-induced behaviors in the $\alpha$-IGZO films.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.254-255
• /
• 2014

RF magnetron sputtering법으로 증착한 비정질 IGZO 박막과 이를 Active layer로 이용한 TFT의 Transfer 특성에 대한 RF Power의 영향에 대해 연구하였다. Carrier concentration은 Sputtering 공정 중에 산소 분압으로 조절하였다. RF Power가 75에서 150W로 증가할수록 IGZO 박막의 Roughness는 12.2에서 $6.5{\AA}$ 감소하였고 Density는 6.0에서 $6.1g/cm^3$로 증가하였다. 또한, 모든 IGZO 박막은 가시광 영역에서 85% 이상의 투과율을 보였고 Optical band gap은 미세하게 감소하였다. RF Power가 증가할수록 a-IGZO TFT의 Threshold voltage는 0.9에서 7V로 증가하였고, Subthreshold slope은 0.3에서 0.8 V/decade로 증가하였다. 하지만 Mobility는 11에서 $19cm^2/V{\cdot}s$로 증가하였다.

• Journal of the Semiconductor & Display Technology
• /
• v.15 no.3
• /
• pp.57-61
• /
• 2016

We have studied the structural, optical and electrical properties of IGZO thin films. The IGZO thin films were deposited on the silicon wafer by RF magnetron sputtering method. The RF power in sputtering process was varied as 15W, 30W, 45W, 60W, 75W, respectively. All of the thin films transmittance in the visible range was above 85%. XRD analysis showed that amorphous structure of the thin films without any peak. The Hall measurements in the low RF power is the high mobility above $10cm^2/V{\cdot}s$ and the low resistvity are obtained in the IGZO thin films.

• Current Applied Physics
• /
• v.18 no.11
• /
• pp.1447-1450
• /
• 2018

The electron spin resonance (ESR) detects point defect of the In-Ga-Zn oxide (IGZO) like singly ionized oxygen vacancies and excess oxygen, and get spin density as a parameter of defect state. So, we demonstrated the spin density measurement of the IGZO film with various deposition conditions and it has linear relationship. Moreover, we matched the spin density with the total BTS and the threshold voltage ($V_{th}$) distribution of the IGZO thin film transistors. The total BTS ${\Delta}V_{th}$ and the $V_{th}$ distribution were degraded due to the spin density increases. The spin density is the useful indicator to predict $V_{th}$ instability of IGZO TFTs.