• 한국세라믹학회지
• /
• 제41권9호
• /
• pp.637-641
• /
• 2004

We investigated the effects of SiH$_4$ gas on the surface of Hf-silicate films during the deposition of polycrystalline (poly) Si films and the thermal stability of sputtered Hf-silicate films in poly Si/Hf-silicate structure by using High Resolution Transmission Electron Microscopy (HR-TEM) and X-ray Photoelectron Spectroscopy (XPS). Hf-silicate films were deposited by using DC-mag-netron sputtering with Hf target and Si target and poly Si films were deposited at 600$^{\circ}C$ by using Low Pressure Chemical Vapor Deposition (LPCVD) with SiH$_4$ gas. After poly Si film deposition at 600$^{\circ}C$, Hf silicide layer was observed between poly Si and Hf-silicate films due to the reaction between active SiH$_4$ gas and Hf-silicate films. After annealing at 900$^{\circ}C$, Hf silicide, formed during the deposition of poly Si, changed to Hf-silicate and the phase separation of the silicate was not observed. In addition, the Hf-silicate films remain amorphous phase.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.117-117
• /
• 2007

The physical and electrical properties of nitrided Hf-silicate films, incorporated by NO gas annealing, were investigated by XPS, NEXAFS, TEM and C-V measurement. We confirmed the nitrogen incorporation during NO gas annealing treatment effectively enhances the thermal stability of Hf-silicate. The suppression of phase separation was observed in Hf-silicate films with high nitrogen contents. The negative shift of threshold voltage is caused by the incorporation of nitrogen in the hafnium silicate films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.116-116
• /
• 2007

We investigated the characteristics of the Hafnium silicate (Hf-silicate) film which is grown by ALD (atomic layer deposition). The Hf-silicate films that were annealed by the RTP. The physical and electrical properties of nitrided Hf-silicate films, incorporated by NO gas and $NH_3$ gas annealing, were investigated by XPS, TEM and I-V measurement. We confirmed the nitrogen incorporation during NO gas annealing treatment effectively enhances the thermal stability of Hf-silicate. The tendency of nitnitridation in NO gas and $NH_3$ is different. Leakage current is improved in post NO gas annealing.

• 한국재료학회지
• /
• 제17권5호
• /
• pp.263-267
• /
• 2007

Hafnium oxide $(HfO_2)$ films were deposited on Si(100) substrates by remote plasma-enhanced atomic layer deposition (PEALD) method at $250^{\circ}C$ using TEMAH [tetrakis(ethylmethylamino)hafnium] and $O_2$ plasma. $(HfO_2)$ films showed a relatively low carbon contamination of about 3 at %. As-deposited and annealed $(HfO_2)$ films showed amorphous and randomly oriented polycrystalline structure. respectively. The interfacial layer of $(HfO_2)$ films deposited using remote PEALD was Hf silicate and its thickness increased with increasing annealing temperature. The hysteresis of $(HfO_2)$ films became lower and the flat band voltages shifted towards the positive direction after annealing. Post-annealing process significantly changed the physical, chemical, and electrical properties of $(HfO_2)$ films. $(HfO_2)$ films deposited by remote PEALD using TEMAH and $O_2$ plasma showed generally improved film qualities compare to those of the films deposited by conventional ALD.

• 한국전기전자재료학회논문지
• /
• 제24권5호
• /
• pp.370-373
• /
• 2011

We investigated the effects of low temperature ($500^{\circ}C$) $O_2$ annealing on the characteristics of hafnium silicate ($HfSi_xO_y$) films deposited on a Si substrate by atomic layer deposition (ALD). We found that the post deposition annealing under oxidizing ambient causes the oxidation of residual Hf metal components, resulting in the improvement of electrical characteristics such as flat band voltage shift (${\Delta}V_{fb}$) by hysteresis without oxide capacitance reduction. We suggest that post deposition annealing under oxidizing ambient is necessary to improve the electrical characteristics of $HfSi_xO_y$ films deposited by ALD.

• Transactions on Electrical and Electronic Materials
• /
• 제12권3호
• /
• pp.127-130
• /
• 2011

We investigated the effects of $O_2$ annealing (i.e., temperature and time) on the characteristics of hafnium silicate ($HfSi_xO_y$) films deposited on a Si substrate by atomic layer deposition process (ALD). We found that the post deposition annealing under oxidizing ambient causes the oxidation of residual Hf metal components, resulting in the improvement of electrical characteristics (e.g., hysteresis window and leakage current are decreased). In addition, we observed the annealing temperature is more important than the annealing time for post deposition annealing. Based on these observations, we suggest that post deposition annealing under oxidizing ambient is necessary to improve the electrical characteristics of $HfSi_xO_y$ films deposited by ALD. However, the annealing temperature has to be carefully controlled to minimize the regrowth of interfacial oxide, which degrades the value of equivalent oxide thickness.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제36회 동계학술대회 초록집
• /
• pp.181.2-181.2
• /
• 2009

• E2M - 전기 전자와 첨단 소재
• /
• 제16권9호
• /
• pp.63.2-64
• /
• 2003

Epitaxial yttrium-stabilized HfO$_2$ thin films were deposited on p-type (100) Si substrates by pulsed laser deposition at a relatively lower substrate temperature of 550. Transmission electron microscopy observation revealed a fixed orientation relationship between the epitaxial film and Si; that is, (100)Si.(100)HfO$_2$ and [001]Si/[001]HfO$_2$. The film/Si interface is not atomically flat, suggesting possible interfacial reaction and diffusion, X-ray photoelectron spectrum analysis also revealed the interfacial reaction and diffusion evidenced by Hf silicate and Hf-Si bond formation at the interface. The epitaxial growth of the yttrium stabilized HfO$_2$ thin film on bare Si is via a direct growth mechanism without involoving the reaction between Hf atoms and SiO$_2$ layer. High-frequency capacitance-voltage measurement on an as-grown 40-A yttrium-stabilized HfO$_2$ epitaxial film yielded an dielectric constant of about 14 and equivalent oxide thickness to SiO$_2$ of 12 A. The leakage current density is 7.0${\times}$ 10e-2 A/$\textrm{cm}^2$ at 1V gate bias voltage.

• 마이크로전자및패키징학회지
• /
• 제11권2호
• /
• pp.29-35
• /
• 2004

65 nm급 게이트 유전체로의 $HfO_2$의 적용을 위해 hydrogen-terminate된 Si 기판과 ECR $N_2$ plasma를 이용하여 SiNx를 형성한 기판 위에 MOCVD를 이용하여 $HfO_2$를 증착하였다. $450^{\circ}C$에서 증착시킨 박막의 경우 낮은 carbon 불순물을 가지며 비정질 matrix에 국부적인 결정화와 가장 적은 계면층이 형성되었으며 이 계면층은 Hf-silicate임을 알 수 있었다. 또한 $900^{\circ}C$, 30초간 $N_2$분위기에서 RTA 결과 $HfO_2/Si$의 single layer capacitor의 경우 계면층의 증가로 인해 EOT가 열처리전(2.6nm)보다 약 1 nm 증가하였다. 그러나 $HfO_2/SiNx/Si$ stack capacitor의 경우 SiNx 계면층은 열처리후에도 일정하게 유지되었으며 $HfO_2$ 박막의 결정화로 열처리전(2.7nm)보다 0.3nm의 EOT 감소를 나타내었으며 열처리후에도 $4.8{\times}10^{-6}A/cm^2$의 매우 우수한 누설전류 특성을 가짐을 알 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.832-835
• /
• 2001

We report the structural and electrical properties of hafnium oxide (HfO$_2$) films with tungsten silicide (WSi$_2$) metal gate. In this study, HfO$_2$thin films were fabricated by oxidation of sputtered Hf metal films on Si, and WSi$_2$was deposited directly on HfO$_2$by LPCVD. The hysteresis windows in C-V curves of the WSi$_2$HfO$_2$/Si MOS capacitors were negligible (<20 mV), and had no dependence on frequency from 10 kHz to 1 MHz and bias ramp rate from 10 mV to 1 V. In addition, leakage current was very low in the range of 10$^{-9}$ ~10$^{-10}$ A to ~ 1 V, which was due to the formation of interfacial hafnium silicate layer between HfO$_2$and Si. After PMA (post metallization annealing) of the WSi$_2$/HfO$_2$/Si MOS capacitors at 500 $^{\circ}C$ EOT (equivalent oxide thickness) was reduced from 26 to 22 $\AA$ and the leakage current was reduced by approximately one order as compared to that measured before annealing. These results indicate that the effect of fluorine diffusion is negligible and annealing minimizes the etching damage.