• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.289-293
• /
• 2013

We have studied structural, optical, and electrical properties of the Ga-doped ZnO (GZO) thin films being usable in transparent conducting oxides. The GZO thin films were deposited on the corning 1737 glass plate by the RF magnetron sputtering system. To find optimal properties of GZO for transparent conducting oxides, the Ar gas in sputtering process was varied as 40, 60, 80 and 100 sccm, respectively. As reaction gas decreased, the crystallinity of GZO thin film was increased, the optical bandgap of GZO thin film increased. The transmittance of the film was over 80% in the visible light range regardless of the changes in reaction gas. The measurement of Hall effect characterizes the whole thin film as n-type, and the electrical property was improved with decreasing reaction gas. The structural, optical, and electrical properties of the GZO thin films were affected by Ga dopant content in GZO thin film.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.336.2-336.2
• /
• 2014

Indium Tin Oxide (ITO) thin films are used as the Transparent Conducting Oxide (TCO), such as flat panel display, transparent electrodes, solar cell, touch screen, and various optical devices. ZnO has attracted attention as alternative materials to ITO film due to its resource availability, low cost, and good transmittance at the visible region. Recently, very thin film deposition is important. In order to minimize the damage caused by bending. However, ZnO thin film such as Ga-doped ZnO(GZO) has poor sheet resistance characteristics. To solve this problem, By adding the conductive metal on films can decrease the sheet resistance and increase the mobility of the films. In this study, We analyzed the electrical and optical characteristics of GZO/Ag/GZO (GAG) films by change in Ag and GZO thickness.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.230-230
• /
• 2011

RF magnetron sputtering을 이용하여 Ar 및 $O_2$유량에 따라 GZO 박막을 유리기판 위에 제작하고 구조적, 광학적, 전기적 특성을 조사하였다. 박막 증착 조건의 초기 압력은 $1.0{\times}10^{-6}$ Torr, RF 파워는 25W, 증착온도는 상온으로 고정하였으며 기판은 Corning 1737 유리 기판을 사용하였다. 공정 변수로 Ar 유량을 40 sccm, 60 sccm, 80 sccm, 100 sccm으로 변화시켰으며, $O_2$ 가스비율을 5~20%으로 변화를 주어 실험을 진행하였다. GZO 타겟은 ZnO,Ga 분말을 각각 97:3 wt.%로 소결된 타겟을 사용하였다. 유리기판 위에 증착된 모든 GZO 박막에서 (002) 면의 우선 배향성이 관찰되었고 평균 85% 이상의 투과율을 나타내었다. 산소유량이 포함되지 않고 Ar 유량이 적은 GZO 박막의 결정성은 향상되었고, 광학적 밴드갭은 증가하였다. Hall 측정 결과 산소의 유량이 포함되어 있는 박막에서는 모두 완전한 산화물에 가까운 화학양론적 조성으로 면저항이 $10^6{\Omega}/{\Box}$ 이상인 부도체 특성을 보였으며, 산소가 포함되지 않은 샘플에서는 투명전도막 특성이 확인되었다. 산소가 포함되지 않은 Ar 유량이 60 sccm일 때 전기비저항 $3.25{\times}10^{-3}{\Omega}cm$, 전하의 농도 $9.41{\times}10^{20}\;cm^{-3}$, 이동도 2.04 $cm^2V^{-1}s^{-1}$로 투명전도막으로 적합한 전기적 특성을 얻었다. GZO 박막의 경우 산소가 포함될 경우 결정성이 저하되고, 절연특성을 갖는 것을 확인할 수 있었다.

• Journal of the Semiconductor & Display Technology
• /
• v.15 no.4
• /
• pp.41-45
• /
• 2016

ITO/GZO double layered thin films were prepared on transparent glass substrates. Ga-doped ZnO(GZO) films were deposited by RF magnetron sputtering using an ZnO:Ga (98: 2 wt%) target. The post deposition annealing process was conducted for 30 minutes at different temperature of 100, 200, 300 and $400^{\circ}C$, respectively. As increase annealing temperature, ITO/GZO double layered thin films show the increment of the prefer orientation of ZnO diffraction peak (002) in the XRD patterns. We obtained Ga-doped ZnO thin films with a lowest resistivity of $1.84{\times}10^{-4}{\Omega}-cm$ at $400^{\circ}C$ and transparency above 80% in visible ranges. The figure of merit obtained in this study means that ITO/GZO double layered thin films which annealed at $400^{\circ}C$ have the highest optoelectrical performance in this study.

• Journal of Surface Science and Engineering
• /
• v.47 no.6
• /
• pp.341-346
• /
• 2014

Ga-doped ZnO (GZO) single layer and $SiO_2/GZO$ bi-layered films were deposited on Polycarbonate(PC) substrate by radio frequency magnetron sputtering. Influence of the structural, electrical, and optical properties of the films was considered. We have considered the influence of electron irradiation energy of 450 and 900 eV on the stuctural, electrical and optical properties of $SiO_2/GZO$ thin films. The optical transmittance in a visible wave length region increased with the electron irradiation energy. The electrical resistivity of the films were dependent on the electron's irradiation energy. The $SiO_2/GZO$ films irradiated at 900 eV were showen the lowest resistivity of $7.8{\times}10^{-3}{\Omega}cm$. The film which was irradiated by electron at 900 eV shows 84.3% optical transmittance and also shows lower than contact angle of $58^{\circ}$ in this study.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.24 no.4
• /
• pp.110-115
• /
• 2010

Transparent conducting gallium-doped zinc oxide (GZO) thin films which were deposited on Corning glass substrate using an Gun-type rf magnetron sputtering deposition technology. The GZO thin films were fabricated with an GZO ceramic target (Zn : 97[wt%], $Ga_2O_3$ : 3[wt%]). The GZO thin films were deposited by varying the growth conditions such as the substrate temperature, oxygen pressure. Among the GZO thin films fabricated in this study, the one formed at conditions of the substrate temperature of 200[$^{\circ}C$], Ar flow rate of 50[sccm], $O_2$ flow rate of 5[sccm], rf power of 80[W] and working pressure of 5[mtorr] showed the best properties of an electrical resistivity of $2.536{\times}10^{-4}[{\Omega}{\cdot}cm]$, a carrier concentration of $7.746{\times}10^{20}[cm^{-3}]$, and a carrier mobility of 31.77[$cm^2/V{\cdot}S$], which indicates that it could be used as a transparent electrode for thin film transistor and flat panel display applications.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.248-249
• /
• 2014

본 연구에서는 GZO:Sn에서 Sn의 함유량에 따른 트랜지스터 특성 변화를 알아보았다. 그 결과 GZO:Sn=200W:9W 의 소자에서 가장 좋은 트랜지스터 특성을 얻을 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.182-182
• /
• 2011

태양전지용 TCO로 사용되는 ITO 박막의 고온에서의 전기적 특성을 향상시키기 위하여 고온 안정성을 가지는 GZO/ITO 박막을 증착 하였다. GZO/ITO 박막의 특성은 버퍼 층인 ITO의 두께 및 구조에 의해 영향을 받는 것을 알 수 있었다.

• Journal of the Korean Vacuum Society
• /
• v.16 no.6
• /
• pp.453-457
• /
• 2007

Zinc oxide (ZnO) and Ga doped zinc oxide (GZO) with different thickness in range of 10nm to 100nm are prepared on glass substrate by RF magnetron sputtering at room temperature. The structural and optical properties of the thin films is evaluated. The structural properties of ZnO and GZO are investigated by Tunneling Electron Microscopy (TEM) and scanning electron microscopy (SEM). Optical properties are also investigated by UV-VIS-NIR spectrophotometer (200$\sim$1400nm). The much larger grain size of ZnO compared to GZO decreased the light scattering at the grain boundary and improved the transmittance. The transmittance of ZnO is higher than that of GZO through all of the ranges of wavelengths. In case of over 50nm, we found that the transmittance of ZnO is 20% higher than that of GZO.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.405-406
• /
• 2013

Ga-doped ZnO (GZO)는 $300^{\circ}C$ 이상의 온도에서는 전기적으로 불안정하기 때문에 CIGS, CdTe, DSC와 같은 태양전지의 높은 공정온도 때문에 사용이 제한적이다. ZTO thin film은 Al2O3, SiO2, TiO2, ZnO tihin film과 비교하여 산소 및 수분에 대하여 투과성이 상대적으로 낮은 것으로 알려져 있다. 따라서 GZO single layer에 비하여 ZTO-GZO multi-layer를 구성하여 TCO를 제작하면, 높은 공정온도에서도 사용 가능하다. 실제 제작된 GZO single layer (300 nm)에서 비저항이 $7.69{\times}10^{-4}{\Omega}{\cdot}cm$에서 $500^{\circ}C$에서 열처리 후 $7.76{\times}10^{-2}{\Omega}{\cdot}cm$으로 급격하게 상승한다. ZTO single layer (420 nm)는 as-grown에서는 측정 불가했지만, $400^{\circ}C$에서 열처리 후 $3.52{\times}10^{-1}{\Omega}{\cdot}cm$ $500^{\circ}C$에서 열처리 후 $4.10{\times}10^{-1}{\Omega}{\cdot}cm$으로 열처리에 따른 큰 변화가 없다. 또한 ZTO-GZO multi-layer (720 nm)의 경우 비저항이 $2.11{\times}10^{-3}{\Omega}{\cdot}cm$에서 $500^{\circ}C$에서 열처리 후 $3.67{\times}10^{-3}{\Omega}{\cdot}cm$으로 GZO에 비하여 상대적으로 변화폭이 작다. 또한 ZTO의 두께에 따른 영향을 확인하기 위하여 ZTO를 2 scan, 4 scan, 6 scan 공정 진행 및 $500^{\circ}C$에서 열처리 후 ZTO, ZTO-GZO thin film의 비저항을 측정하였다. ZTO의 경우 $3.34{\times}10^{-1}{\Omega}{\cdot}cm$ (2 scan), $3.62{\times}10^{-1}{\Omega}{\cdot}cm$ (4 scan), $4.1{\times}10^{-1}{\Omega}{\cdot}cm$ (6 scan)으로 큰 차이가 없으며, ZTO-GZO에서도 $3.73{\times}10^{-3}{\Omega}{\cdot}cm$ (2 scan), $3.42{\times}10^{-3}{\Omega}{\cdot}cm$ (4 scan), $3.67{\times}10^{-3}{\Omega}{\cdot}cm$ (6 scan)으로 큰 차이가 없음을 확인하였다. 염료감응 태양전지에 적용하여 기존에 사용되는 FTO대신에 ZTO-GZO를 사용하며, 가격적 측면, 성능적 측면에서 개선 가능할 것으로 생각된다.