• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.70-77
• /
• 2010

This study is to investigate experimentally the influence of mixing factors, such as a mortar mix proportion of non-cement mortar, flow, and W/B, on quality characteristics of blast furnace slag powder mortar incorporating dry type recycled fine aggregates. In the characteristics of fresh mortar, the W/B increased according to the increase in the flow due to the increase in water contents, but air contents decreased due to loss of air contrary to the increase in the W/B. In the case of hardened mortar, the compressive strength showed a decrease due to the highly determined W/B inversely according to the increase in the flow through the entire age in which the compressive strength increased proportionally according to the increase in the B/W. Also, the increasing rate of such compressive strength increased more largely due to the latent hydraulic property of the BS according to the passage of the age. The flexural strength at the age of 28 days according to the increase in the B/W represented a similar level in strength values without any increases. The flexural strength for the compressive strength was distributed as a range of 1/2 ~ 1/3 and that showed a higher range than that of conventional concretes.

• The Journal of Engineering Geology
• /
• v.30 no.4
• /
• pp.541-555
• /
• 2020

The grouting method is used for reinforcing and waterproofing the soft ground, increasing the bearing capacity of structures damaged by lowering or subsidence due to rise and vibration, and for ordering. This study attempted to develop a blast furnace slag-based cementless grout material to increase the strength and hardening time of the grout material using reinforcing fibers. In this regard, in this study, it was used in combination with calcium hydroxide, which is an alkali stimulant of the three fine powders of blast furnace slag, and the content of calcium hydroxide was used by substituting 10, 20, and 30% of the fine powder of blast furnace slag. In addition, in order to compare the strength according to the presence or absence of reinforcing fibers, an experiment was performed by adding 0.5% of each fiber. As the content of carbon fibers and aramid fibers increased, the uniaxial compressive strength increased, and it was confirmed that the crosslinking action of the fibers in the grout material increased the uniaxial compressive strength. In addition, it was confirmed that the gel time sharply decreased as the content of the alkali stimulate increased.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.127-136
• /
• 2015

To evaluate the effects of limestone powder and silica fume on the properties of high-strength high-volume ground granulated blast-furnace slag (GGBFS) blended cement concrete, this study investigated the rheology, strength development, hydration and pozzolanic reaction characteristics, porosity and pore size distribution of high-strength mortars with the water-to-binder ratio of 20, 50 to 80% GGBFS, up to 20% limestone powder, and up to 10% silica fume. According to test results, compared with the Portland cement mixture, the high-volume GGBFS mixture had much higher flow due to the low surface friction of GGBFS particles and higher strength in the early age due to the accelerated cement hydration by increase of free water; however, because of too low water-to-binder ratio and cement content, and lack of calcium hydroxide content, the pozzolanic reactio cannot be activated and the long-term strength development was limited. Limestone powder did not affect the flowability, and also accelerate the early cement hydration. However, because its effect on the acceleration of cement hydration is not greater than that of GGBFS, and it does not have hydraulic reactivity unlikely to GGBFS, compressive strength was reduced proportional to the replacement ratio of limestone powder. Also, silica fume and very fine GGBFS lowered flow and strength by absorbing more free water required for cement hydration. Capillary porosities of GGBFS blended mortars were smaller than that of OPC mortar, but the effect of limestone powder on porosity was not noticeable, and silica fume increased porosity due to low degree of hydration. Nevertheless, it is confirmed that the addition of GGBFS and silica fume increases fine pores.

• Journal of Powder Materials
• /
• v.21 no.4
• /
• pp.271-276
• /
• 2014

15Cr-1Mo base oxide dispersion strengthened (ODS) steel which is considered to be as a promising candidate for high- temperature components in nuclear fusion and fission systems because of its excellent high temperature strength, corrosion and radiation resistance was fabricated by using mechanical alloying, hot isostatic pressing and hot rolling. Torsion tests were performed at room temperature, leading to two different shear strain routes in the forward and reverse directions. In this study, microstructure evolution of the ODS steel during simple shearing was investigated. Fine grained microstructure and a cell structure of dislocation with low angle boundaries were characterized with shear strain in the shear deformed region by electron backscattered diffraction (EBSD). Grain refinement with shear strain resulted in an increase in hardness. After the forward-reverse torsion, the hardness value was measured to be higher than that of the forward torsion only with an identical shear strain amount, suggesting that new dislocation cell structures inside the grain were generated, thus resulting in a larger strengthening of the steel.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.11a
• /
• pp.55-56
• /
• 2015

In this research the processing method of Desulfurized Plaster is changed to cyclotomy, 0.3mm sieve analysis and 500℃ heat exposure, and by changing the mix rate of the binding agent to 0~20%, it was applied to mortar that used natural aggregate and blast furnace slag for testing. The test results showed that the sieve analysis and high heat exposure of the flow and air volume increased according to the increase of mixing rate of FGD while the cyclotomy decreased. The setting time accelerated as the mixing rate of FGD increased, and the compression strength increased to its maximum when the mixing rate of FGD was right around 10%, and especially showed a high trend with cyclotomy and sieve analysis.

• Journal of the Korean Ceramic Society
• /
• v.30 no.10
• /
• pp.829-837
• /
• 1993

Chemically and geometrically homogeneous mixing of Si3N4 powders with sintering additives(YAG, 3Y2O3$.$5Al2O3) was attempted via coprecipitation method. X-ray dot maps for the additive elements(Al and Y) showed that the additives are evenly distributed in the powder mixture prepared by coprecipitation method(CP). TEM observation of the coprecipittion-treated Si3N4 powders revealed that they are covered with extremely fine crystallites of additive. The shift in isoelectric point(IEP) of Si3N4 powders from pH 6.7 to pH 7.9 after coprecipitation mixing gave another evidence for coating of Si3N4 powders with YAG additives. SIMS analysis for composition on the surface and in the matrix of mixed powders showed that the YAG additives are highly enriched on the surface of coprecipitation-treated Si3N4 powders. Especially when a small amount of additive was used, the effect of homogeneous additive distribution on densification was preceptible: After pressureless-sintering of powder compacts containing 5 mol% YAG at 1800$^{\circ}C$ for 0.5h, a sintered density of 96.5% theoretical was obtained from the specimens prepared bycoprecipitation in comparison with 93.8% from the mechanically-mixed one.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.182-187
• /
• 2007

10 mol% $Gd_{2}O_{3}-CeO_{2}$ powder was sintered by microwave in a 2.45 GHz multimode cavity to develop a dense electrolyte layer for intermediate temperature solid oxide fuel cells (IT-SOFCs). Samples were sintered from $1100^{\circ}C$ upto $1500^{\circ}C$ by $50^{\circ}C$ difference and kept for 10 min and 30 min at the maximum temperature respectively. Theoretical density of the sample sintered at $1200^{\circ}C$ for 10 min was 95.4% and increased gradually upto 99% in the sample sintered at $1500^{\circ}C$ for 30 min. All of sintered samples showed very fine microstructures and the maximum average grain size of the sintered sample at $1500^{\circ}C$ for 30 min was $(0.87{\pm}0.42){\mu}m$. Ionic conductvity of the samples were measured by DC 4 probe method.

• Journal of Powder Materials
• /
• v.16 no.4
• /
• pp.275-279
• /
• 2009

The aging characteristics of gas atomized Mg-6 wt.% Al-1 wt.% Zn alloy were investigated and compared to those of cast Mg-6 wt.% Al alloy. The gas atomized Mg-6 wt.% Al-1wt.% Zn alloy powders had spherical morphology between 1 and 100 $\mu m$ in diameter. After compaction under the pressure of 700 MPa at $320^{\circ}C$ for 10 min, the Mg-6 wt.% Al-1 wt.% Zn alloy showed a grain size of approximately 40 $\mu m$ which is smaller than that of the cast Mg-6 wt.% Al alloy, and a relative compact density of approximately 93%. After ageing, the Mg-6 wt.% Al-1 wt.% Zn alloy showed much faster peak hardness than cast Mg-6 wt.% Al alloy. The Mg-6 wt.% Al-1 wt.% Zn alloy showed the new fine precipitations with ageing time, while the cast Mg-6 wt.% Al alloy was almost similar morphology.

• Journal of Powder Materials
• /
• v.15 no.1
• /
• pp.1-5
• /
• 2008

ZnS-$SiO_2$ composite is normally used for sputtering target. In recent years, high sputtering power for higher deposition rate often causes crack formation of the target. Therefore the target material is required that the sintered target material should have high crack resistance, excellent strength and a homogeneous microstructure with high sintered density. In this study, raw ZnS and ZnS-$SiO_2$ powders prepared by a 3-D mixer or high energy ball-milling were successfully densified by spark plasma sintering, the effective densification method of hard-to-sinter materials in a short time. After sintering, the fracture toughness was measured by the indentation fracture (IF) method. Due to the effect of crack deflection by the residual stress occurred by the second phase of fine $SiO_2$, the hardness and fracture toughness reached to 3.031 GPa and $1.014MPa{\cdot}m^{1/2}$, respectively.

• Journal of Powder Materials
• /
• v.5 no.2
• /
• pp.89-97
• /
• 1998

Sintering behavior of nanostructured(NS) W-Cu powders prepared by mechanical alloying (MA) was investigated as a function of sintering temperature. MA NS W-2owt%Cu and W-3owt%Cu composite powders with the crystal size of 20-30 nm were annealed at 90$0^{\circ}C$, and thermal characteristics of those powders were investigated by DSC. Sintering behavior of MA NS W-Cu composite powders was investigated during the solid-state sintering and the Cu-liquid phase sintering. The new nanosintering phenonenon of MA W-Cu powders at solid-state sintering temperature was suggested to explain the W-grain growth in the inside of MA powders. The sintering densification of MA NS W-Cu powders was enhanced at Cu melting temperature by arrangement of MA powders, i.e., the first rearrangement of MA powders was occurred, and then the rearrangement of W-grains in the sintered parts was also took place during liquid-phase sintering, i.e., the second rearrangement was happened. Due to the double rearrangement process of MA NS W-Cu powders, the high sintered density with more than 96%o was obtained and the fine and high homogeneous state of W and Cu phases was achieved by sintering at 1200 $^{\circ}C$.