• Textile Coloration and Finishing
• /
• v.8 no.2
• /
• pp.25-34
• /
• 1996

Diphenyl ethanolamidophosphate(DPEAD) was synthesized for the purpose of developing a new flame retardant for cotton fabric. As the intermediate material was used diphenyl chlorophosphate(DPCP) and it was synthesized by using phosphorus oxychloride and phenol as the starting materials. The final product DPEAP was obtained by the reaction of DPCP and ethanolamine. The flame retardancy of cotton fabrics treated by DPEAP through pad-dry-cure(PDC) process was examined at various conditions. The physical property change of the DPEAP treated cotton fabrics were investigated by examining the drape stiffness, the wrinkle recovery, and the tensile strength. The results are summarized as follows: (1) DPEAP has shown excellent flame retardancy on cotton fabrics in comparison to other flame retardants for cotton fabrics available commercially. (2) The optimal condition for PDC process found was that the curing temperature was 16$0^{\circ}C$, the DPEAP concentration was 10%, the catalyst $({NH_{4})_{2}HPO_{4}$ concentration was 7.0%, and the fixing agent hexamethylol melamine (HMM)/DPEAP weight ratio was 1/8. (3) The wrinkle recovery of the processed fabrics increased with increasing DPEAP concentration. (4) The drape stiffness of the cotton fabrics treated by DPEAP have shown essentially no change until increasing DPEAP concentration to 15 %, however DPEAP concentration exceeds 20% the drape stiffness increased drastically with increasing DPEAP concentration. When DPEAP concentration is kept constant the drape stiffness increased with increasing $({NH_{4})_{2}HPO_{4}$ concentration and HMM/DPEAP weight ratio. (5) The tensile strength of the processed fabrics was lower than that of untreated fabrics, but the tensile strength retention increased with increasing DPEAP concentration.

• Journal of Sericultural and Entomological Science
• /
• v.27 no.2
• /
• pp.28-39
• /
• 1985

The structural and useful characteristics of silk habutae treated with silicone resin by emulsion finishing method were studied. The results were obtained through crease recovery test, water repellency test, scanning micrograph observation, amino acid analysis, X-Ray diffraction analysis, and Fourier Transform Infrared Spectroscopy. The results are summarized as follows; 1) The improvement in crease recovery of silk habutae finished with silicone resin, was observed b soaping treatment and curing conditions. 2) The higher water repellency and stiffness in silk fabrics finished with silicone resin was found by the fabric inspection and the scanning electron microscopic observation. It is suggested that silicone resin impregnated into the void of silk fibroin. 3) The polar side chains of amino acid composition were decreased, when the silicone resin was treated on silk fibroin. 4) Through Amino acid analysis of silicone resin finished fibroin, the different amounts of amino acid composition was indicated due to silk fibroin silicone polymer reaction and the structural difference of its fibroin were also proved by X-ray diffractograms. 5) The functionality of the siloxane compound may be deduced from the silicone finished silk habutae by Fourier Transform Spectroscopy. It was concluded from the above results that the useful characteristics of silk fabric can be improved by silicone resin finishing.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.1-7
• /
• 2017

Concrete behavior in early-age is changing due to hydration reaction with time, and a resistance to chloride attack and strength development are different characterized. In the present work, changing strength and resistance to chloride attack are evaluated with ages from 28 days to 6 months. For the purpose, strength, diffusion coefficient, and passed charge are evaluated for normal concrete with 3 different mix proportions considering 28-day and 6-month curing conditions. With increasing concrete age, the changing ratio of strength falls on the level of 135.3~138.3%, while diffusion coefficient and passed charge shows 41.8%~51.1% and 53.6%~70.0%, respectively. The results of chloride diffusion coefficient and passed charge show relatively similar changing ratios since they are much dependent on the chloride migration velocity in electrical field. The changing ratios in chloride behaviors are evaluated to be much larger than those in compressive strength since the ion transport mechanism is proportional to not porosity but square of porosity.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.6
• /
• pp.308-311
• /
• 2013

The effect of an electric field on the ac electrical treeing in various epoxy/reactive diluent systems was studied in a needle-plate electrode geometry. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and 1,4-butanediol diglycidyl ether (BDGE) or polyglycol (PG) as a reactive diluent was introduced to the DGEBA system, in order to decrease the viscosity of the DGEBA epoxy system. BDGE was acted as a chain extender, and PG acted as a flexibilizer, after the curing reaction. To measure the treeing initiation time and the propagation rate, three constant alternating currents (ac) of 10, 13 and 15 kV/4.2 mm (60 Hz) were applied to the specimen, in a needle-plate electrode arrangement, at $30^{\circ}C$ of insulating oil bath. When 10 kV/4.2 mm (60 Hz) was applied, the treeing initiation time and the propagation rate in the DGEBA system were 356 min and $1.10{\times}10^{-3}$ mm/min, respectively, those in the DGEBA/BDGE system were 150 min and $1.14{\times}10^{-3}$ mm/min, respectively. Those in the DGEBA/PG system were 469 min and $1.05{\times}10^{-3}$ mm/min, respectively. As 15 kV/4.2 mm (60 Hz) was applied, the propagation rate in the DGEBA system was $5.41{\times}10^{-3}$ mm/min, and that in the DGEBA/PG system was $1.42{\times}10^{-3}$ mm/min. These values meant that PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.2
• /
• pp.136-153
• /
• 2020

In this paper, the influence of initial formaldehyde/urea (F/U) molar ratios on the performance of low molar ratio (1.0) urea-formaldehyde (UF) resin adhesives has been investigated. Two initial F/U molar ratios, i.e., the first and second initial molar ratios were used for the alkaline addition reaction. Three levels of the first initial F/U molar ratios (2.0, 3.0, and 4.0) and two levels of the second initial molar ratios (2.0 and 1.7) were employed to prepare a total of six UF resins with an identical final molar ratio (1.0). The basis properties, functional groups, molecular weight, crystallinity, and thermal curing properties of the UF resins were characterized in detail. Higher levels (3.0 and 4.0) of the first initial F/U molar ratio provided the UF resins with better properties (non-volatile solids content, viscosity, gelation time, pH, and specific gravity) than those of the resins prepared with the conventional level F/U molar ratio of 2.0. Statistical analysis suggested that combining the first and second initial molar ratio of 4.0 with 1.7 would result in UF resins with greater adhesion strength and lower formaldehyde emission than those of the resins prepared with other molar ratios. The results showed that higher levels of the first initial molar ratio resulted in a more branched structure, as indicated by GPC, FTIR, DSC, XRD, and greater adhesion strength than those of the other UF resins with an identical final molar ratio of 1.0.

• Journal of Korean Society of Environmental Engineers
• /
• v.29 no.7
• /
• pp.801-809
• /
• 2007

Fly ash and blast furnace slag are an industrial by-product that can be alkali-activated to yield adhesive and cementitious materials, whose production is less energy-intensive and emits less $CO_2$ than ordinary Portland cement manufacture. A laboratory investigation was carried out to evaluate the effect of alkali-activating conditions on compressive strength of fly ash/slag cement and the acid corrosion resistance of this cement. Two alkali activator solution, NaOH and waterglass + NaOH solutions, were used. Waterglass concentration was the factor that gave the highest compressive strength in all tests. The next significant factor was the NaOH concentration, followed by curing temperature. Acid corrosion resistance of FC(fly ash cement) and FSC(fly ash/slag cement), such as sulfuric$(H_2SO_4)$ and hydrochloric acid(HCl), was for better than Portland cement(PC).

• Journal of KIISE:Software and Applications
• /
• v.37 no.4
• /
• pp.311-316
• /
• 2010

Esterel is an imperative synchronous language that is used to develop memories, cache controllers, bus interfaces, and so on. An Esterel statement is called schizophrenic if it is executed more than once in an instant. A schizophrenic statement may cause problems when it is translated to hardware circuits; a circuit performs more than one reaction in a clock. Previous works claim that only local signal declarations and parallel statements may cause schizophrenic problems. However, control signals produced by a trap statement or data signals used by emit statements can cause schizophrenia. They are new schizophrenic patterns. Especially, schizophrenic problems caused by emit statements cannot be solved by a loop unrolling technique that is the key idea of previous curing techniques for schizophrenic problems. In this paper, we introduce and define the two schizophrenic problems.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.2
• /
• pp.123-135
• /
• 2005

Reaction intermediates PCP/BZA (PBI) and tetramethylene bis(orthophosphate)(TBOP) were synthesized from polycaprolactone (PCP) and benzoic acid (BZA) and from pyrophosphoric acid and 1,4-butanediol, respectively. Benzoic acid modified polyesters containing phosphorus (APTB-S, -10, -15) were synthesized by polycondensation of the prepared PBI (containing 5, 10, 15wt% of benzoic acid), TBOP, adipic acid, and 1,4-butanediol. Network structured PU flame-retardant coatings (APHD) were prepared by curing the synthesized benzoic acid modified polyesters containing phosphorus (APT B - 5 , -10, -15) with hexamethylene diisocyanate (HDI)-timer. From the TGA analysis of APTBs, it was found that the afterglow decreased with the amount of BZA content at the high temperatures. With the introduction of BZA, the film viscosity and film hardness of APHD decreased. With the introduction of caprolactone group, the flexibility, impact resistance, accelerated weathering resistance of APTBs increased. Flame retardancy of the coatings was tested. In a vertical burning method, APHD shows 210$^{\sim}$313 seconds, which indicates that the coatings are good flame-retardant coatings. Moreover, the amount of afterglow and flame retardancy of the coatings are decreased with increasing BZA content.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.474-478
• /
• 2007

Polymer substrate materials with low dielectric loss were obtained by fabricating the composite using dicyclopentadienyl bisphenol cyanate ester oligomer and polyphenylene ether (PPE). From the analysis of the curing reaction of oligomer and catalyst, it was observed that the optimum amount of catalyst was 0.02 phr of Zn content. It was applied to the fabrication of polymer composite. By changing oligomer/PPE weight ratio, the peel strength and the gel content of the fabricated composites were measured, and then, the dielectric constant and the dissipation factor were measured in the GHz frequency range. The amount of PPE affected the peel strength and the dielectric properties of composites. However, the amount of catalyst did not affect them at all. Resulting from all experiments, we obtained polymer composite laminates haying the peel strength of above 1 kN/m and the low dissipation factor of 0.004 at 1 GHz.

• Corrosion Science and Technology
• /
• v.8 no.3
• /
• pp.110-115
• /
• 2009

At the onset of corrosion of steel in concrete, hydrogen ions usually evolve in the process of electrochemical reaction, thereby decreasing the pH of the pore solution, which can be buffered by cement hydration products, as being representatively illustrated by calcium hydroxide. Hence, a fall in the pH is dependent on properties of cement hydration (i.e. hydration products and degree of hydration). The present study tested acid neutralization capacity (ANC) of cementitious binders of OPC(Ordinary Portland Cement), 30% PFA(Pulverized Fuel Ash), 60% GGBS(Ground Granulated Blast Furnace Slag), 10% SF(Silica Fume) to quantify the resistance of cement matrix to a pH fall. Cement pastes were cast at 0.4 of a free W/C ratio with 1.5% chlorides by weight of binder in cast. Powder samples obtained crushed and ground specimen after 200 days of curing were diluted in still water combined with different levels of 1M nitric acid solution, ranging from 0.5 to 20 mol/kg. Then, the pH of diluted solution was monitored until any further change in the pH did not take place. It was seen that the pH of the diluted solution gradually decreased as the molar amount of nitric acid increased. At some particular values of the pH, however, a decrease in the pH was marginal, which can be expressed in the peak resistances to a pH fall in the ANC curve. The peaks occurred at the variations in the pH, depending on binder type, but commonly at about 12.5 in the pH, indicate a resistance of precipitated calcium hydroxide. The measurement of water soluble chloride at the end of test showed that the amount of free chloride was significantly increased at the pH corresponding to the peaks in the ANC curve, which may reflect the adsorption of hydration products to chlorides.