A Study on the Resin Finishing of Silk Fabric -Silicone Resin Finishing-

견직물의 수지가공에 관한 연구

The structural and useful characteristics of silk habutae treated with silicone resin by emulsion finishing method were studied. The results were obtained through crease recovery test, water repellency test, scanning micrograph observation, amino acid analysis, X-Ray diffraction analysis, and Fourier Transform Infrared Spectroscopy. The results are summarized as follows; 1) The improvement in crease recovery of silk habutae finished with silicone resin, was observed b soaping treatment and curing conditions. 2) The higher water repellency and stiffness in silk fabrics finished with silicone resin was found by the fabric inspection and the scanning electron microscopic observation. It is suggested that silicone resin impregnated into the void of silk fibroin. 3) The polar side chains of amino acid composition were decreased, when the silicone resin was treated on silk fibroin. 4) Through Amino acid analysis of silicone resin finished fibroin, the different amounts of amino acid composition was indicated due to silk fibroin silicone polymer reaction and the structural difference of its fibroin were also proved by X-ray diffractograms. 5) The functionality of the siloxane compound may be deduced from the silicone finished silk habutae by Fourier Transform Spectroscopy. It was concluded from the above results that the useful characteristics of silk fabric can be improved by silicone resin finishing.

견직물의 실용성능(방추도, 세탁성)을 개선할 목적으로 실크하브다이(silk habutae)에 실리콘수지를 유화 가공법으로 처리하였다. 실리콘가공 하브다이의 방추도, 발수도, 유연도, 강신도, 수분율 등은 직물검사 방법에 따라서 검사하였고 가공 후 견피브로인의 구조적인 변화를 구명하기 위하여 주사전자현미경, 아미노산분석, X-선 회절강도, FT-IR 흡수분석에 의하여 검토한 결과 아래와 같은 결과를 얻었다. 1) 견하브다이 직물의 방추도는 soaping 처리오 큐어링 조건에 의하여 현저히 개선되었다. 2) 실리콘 수지 가공에 의하여 견하브다이의 발수도와 유연도가 향상되었고, 가공 후 silk fibroin을 주사전자현미경으로 관찰한 결과 견섬유 특유의 불규칙한 섬유표면은 평활하게 관찰되었다. 3) 실리콘 수지와 silk fibroin의 반응에 따라서 피브로인 조성 아미노산 중 극성기를 가지고 있는 아미노산의 감소비율이 현저하였다. 4) 실리콘 수지가공 silk habutae는 soaping에 의하여 X-선 회절강도가 높아지는 경향이었다. 5) 가공 후 견하브다이의 FT-IR 흡수곡선에 실록산등의 peak가 검출된 것으로 미루어 fibroin의 개질이 가능하다고 생각된다.