• 한국재료학회지
• /
• 제31권12호
• /
• pp.690-696
• /
• 2021

The purpose of this study is to develop a zirconium-based alloy with low modulus and magnetic susceptibility to prevent the stress-shielding effect and the generation of artifacts. Zr-7Cu-xSn (x = 1, 5, 10, 15 mass%) alloys are prepared by an arc melting process. Microstructure characterization is performed by microscopy and X-ray diffraction. Mechanical properties are evaluated using micro Vickers hardness and compression test. The magnetic susceptibility is evaluated using a SQUID-VSM. The average magnetic susceptibility value of the Zr-7Cu-xSn alloy is 1.176 × 10^-8 cm³g^-1. Corrosion tests of zirconium-based alloys are conducted through polarization test. The average Icorr value of the Zr-7Cu-xSn alloy is 0.1912 ㎂/cm². The elastic modulus value of 14 ~ 18 GPa of the zirconium-based alloy is very similar to the elastic modulus value of 15 ~ 30 GPa of the human bone. Consequently, the Sn added zirconium alloy, Zr-7Cu-xSn, is very interesting and attractive as a biomaterial that reduces the stress-shielding effect caused by differences of elastic modulus between human bone and metallic implants. In addition, this material has the potential to be used in metallic dental implants to effectively eliminate artifacts in MRI images due to low magnetic susceptibility.

• Journal of Welding and Joining
• /
• 제7권3호
• /
• pp.36-43
• /
• 1989

The furnace brazing in a Ar of copper to martensitic stainless steel(13.5Cr) using Cu-(5~8%)P-(0~8%)Sn powders was investigated. Shear strength, wettability, reacted layer, defect ratio at the stainless steel interface was evaluated. As Sn was added to the Cu-P powders, defect ratio and P content at the stainless steel interface decreased. And also as Sn was added, defect form at the stainless steel interface changed from the continuous layer to the discrete type, and shear strength of the brazed joint increased.

• 마이크로전자및패키징학회지
• /
• 제18권2호
• /
• pp.49-55
• /
• 2011

전자기기에서의 고장 중 대부분은 작동 중 발생하는 열과 충격에 기인한다. 이 열과 충격은 PCB(Printed Board) 부품의 접합부 계면에 균열을 야기 시키고, 이 균열은 금속간 화합물(Intermetallic Compound: IMC)의 형성과 밀접한 관계를 가진다. 본 연구에서는 Sn-Ag-Cu계의 Ag함량을 변화한 Sn-1.0Ag-0.5Cu와 Sn-1.2Ag-0.5Cu 및 Sn-3.0Ag-0.5Cu의 3가지 조성의 솔더로 접합한 소재를 대상으로 1000시간 까지 등온시효(Isothermal Aging) 하였다. 등온시효 동 안 솔더(Solder)의 계면에 발생하는 IMC(Intermetallic Compound) 성장이 관찰되었으며, solder 접합부의 기계적 특성은 굽힘충격 시험법을 이용하여 평가되었다. 그 결과 시효처리 전에는 Ag 함량이 낮은 solder의 굽힘충격 특성이 우수하게 나타났으나, 시효처리 후에는 반대의 결과를 나타내었다. 이 결과는 IMC layer 주변에 생성된 미세한 $Ag_3Sn$ 및 조대한 $Cu_6Sn_5$와 관련되어, 미세한 $Ag_3Sn$이 충격을 완화한 것으로 나타나 이에 따라 굽힘충격 특성에 차이가 나타남을 알 수 있었다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.85.2-85.2
• /
• 2010

$Cu_2ZnSnSe_4$ (CZTSe) is one of candidate to alternate $Cu(In,Ga)Se_2$ as solar absorber material for solar cell. The expensive elements of In and Ga are replaced by Zn and Sn, respectively to lower the material cost. In this study we fabricated CZTSe thin film by selenization of single precursor layer consisted metallic constituent. Precursor compositions ratio were selected to have Cu-poor and Zn-rich content and prepared by RF magnetron sputtering. Thermal processing was applied to introduce selenium into as-deposited films at temperatures ranging from 350 to 500 for time up to 120 minutes. Single precursor films showed amorphous structure and consist of individual elements of Cu, Zn, and Sn. It was confirmed by XRD analysis that synthesis of CZTSe compound is occurred from lower temperature process, although concurrently additional phases such as binary cooper selenides are also existed. The quality of CZTSe crystal was improved as temperature increased. We also investigated the optical and electrical properties of as-selenized CZTSe as well.

• 한국분말재료학회지
• /
• 제30권4호
• /
• pp.339-345
• /
• 2023

This study investigates the melting point and brazing properties of the aluminum (Al)-copper (Cu)-silicon (Si)-tin (Sn) alloy fabricated for low-temperature brazing based on the alloy design. Specifically, the Al-20Cu-10Si-Sn alloy is examined and confirmed to possess a melting point of approximately 520℃. Analysis of the melting point of the alloy based on composition reveals that the melting temperature tends to decrease with increasing Cu and Si content, along with a corresponding decrease as the Sn content rises. This study verifies that the Al-20Cu-10Si-5Sn alloy exhibits high liquidity and favorable mechanical properties for brazing through the joint gap filling test and Vickers hardness measurements. Additionally, a powder fabricated using the Al-20Cu-10Si-5Sn alloy demonstrates a melting point of around 515℃ following melting point analysis. Consequently, it is deemed highly suitable for use as a low-temperature Al brazing material.

• 마이크로전자및패키징학회지
• /
• 제12권1호
• /
• pp.47-52
• /
• 2005

전세계 전자패키지 산업에서 납(Pb) 사용에 대한 환경규제 움직임이 본격화되고 있어 새로운 무연솔더의 개발이 활발히 이루어지고 있다. 게다가 무연솔더의 신뢰성에 대한정보가 아직까지 많이 부족한 실정이다 무연솔더의 신뢰성에 영향을 줄수 있는 것 중의 하나가 Sn pest라고 알려진 동소체 변태이다. Sn pest가 형성될 때 동반되는 부피의 증가는 솔더 조인트의 신뢰성을 저하시킨다. 이미 보고된 바에 따르면, Sn 고용도가 있는 원소(Pb, Bi, Sb)들을 첨가시킬 경우 Sn pest가 효과적으로 억제된다. 그러나 Sn pest를 억제하는 합금에 대한 기계적인 특성에 연구가 거의 이루어지지 않았다. 본 연구에서는 Sn과 Sn-0.7Cu를 기반으로 하여 Bi, Sb을 첨가한 솔더 합금을 사용하여 lap shear크리프 실험을 하였다. 본 연구에서 사용한 합금들의 변형율은 전체적으로 Sn-3.5Ag를 기반으로 하는 합금들보다 높았다. 파괴까지 이르는 변형량은 Sn-0.5Bi가 가장 크고 Sn-0.7Cu-0.5Sb 합금이 가장 작았는데 이러한 경향은 Sn-0.5Bi 합금의 파단면에 Sn globules이 길게 늘어나 있고 Sn-0.7Cu-0.5Sb 합금에서는 더 짧은 Sn globules 이 관찰되는 결과와 일치하였다.

• 마이크로전자및패키징학회지
• /
• 제20권4호
• /
• pp.17-23
• /
• 2013

신축성 전자패키징 기술개발을 위한 기초연구로서 Cu/Sn 범프에 CNT-Ag 복합패드를 형성한 칩을 이방성 전도접착제를 사용하여 플립칩 본딩한 후, CNT-Ag 복합패드의 유무 및 본딩압력에 따른 플립칩 접속부의 접속저항을 측정하였다. CNT-Ag 복합패드가 형성된 Cu/Sn 칩 범프를 25MPa과 50MPa의 본딩압력으로 플립칩 본딩한 시편들은 접속저항이 너무 높아 측정이 안되었으며, 100MPa의 본딩압력으로 플립칩 본딩한 시편은 $213m{\Omega}$의 평균 접속저항을 나타내었다. 이에 비해 CNT-Ag 복합패드가 없는 Cu/Sn 칩 범프를 사용하여 25MPa, 50 MPa 및 100 MPa의 본딩압력으로 플립칩 본딩한 시편은 각기 $1370m{\Omega}$, $372m{\Omega}$ 및 $112m{\Omega}$의 평균 접속저항을 나타내었다.

• 마이크로전자및패키징학회지
• /
• 제6권3호
• /
• pp.9-18
• /
• 1999

본 연구에서는 융점 이상에서의 유지시간에 따른 Sn-3.5Ag 및 Sn-37Pb 공정솔더볼과 Au/Ni/Cu 기판 사이의 야금학적 특성을 고찰하였다. 현재 상용되는 리플로 솔더링 장비를 사용하여, 최고 솔더링 온도와 Conveyor 속도를 변화시킴으로써 융점이상에서의 유지시간을 측정하였다. 결과로서 접합부 계면에서 스캘럽 형태의 $Ni_3Sn_4$금속간화합물이 형성되었고, Cu-Sn계 화합물은 관찰되지 않았다. Ni층이 Cu의 확산 장벽으로 작용하였다. 최고 솔더링 온도가 증가함에 따라 금속간화합물 층의 두께가 최고 2.2$\mu\textrm{m}$까지 성장하였다. 스캘럽의 형상은 반구형에서 지름이 더 작은 볼록한 형상으로 변하게 된다. 접합부의 미세경도값은 Sn-3.5Ag와 Sn-37Pb의 공정조직이 성장함에 따라 감소하였다.

• 마이크로전자및패키징학회지
• /
• 제28권2호
• /
• pp.95-103
• /
• 2021

대표적인 저온솔더인 Sn-58Bi에 Ru nanoparticles을 첨가하여 Sn-58Bi-xRu 복합솔더를 제작하고 Cu/OSP 및 ENIG 표면처리된 PCB 기판과 반응시켜 계면반응 및 솔더조인트 신뢰성을 분석하였다. Cu/OSP와의 반응에서 형성된 Cu₆Sn₅ IMC는 Ru 함량에 따른 두께 변화가 거의 없고 100hr aging 후에도 큰 변화없이 고속 전단시험시 솔더 내부로 연성파괴가 발생하였다. ENIG 와의 반응시에는 Ru 함량이 증가함에 따라서 Ni₃Sn₄ IMC 두께가 감소하는 경향을 보였으며 일부 시편에서 ENIG 특유의 취성파괴 현상이 발견되었다. Ru 원소는 계면 부근에서 발견되지 않아서 계면반응에 크게 관여하지 않는 것으로 판단되며 주로 Bi phase와 함께 존재하는 것으로 분석되고 있는데 어떠한 형태로 두 원소가 공존하고 있는지에 대해서는 추가적인 연구가 필요하다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 추계학술발표강연 및 논문개요집
• /
• pp.102-102
• /
• 2002