• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.641-649
• /
• 2002

The redox properties of a homogeneously-precipitated $TiO_2$ rutile powder with a BET surface area of ~$200 m^2$/g, consisting of an acicular primary particle, were characterized using photocatalytic reaction in aqueous 4-chlorophenol, Cu-EDTA and Pb-EDTA solutions under ultraviolet irradiation, compared to those of commercial P-25 X$200 m_2$ powder with a spherical primary particle as well as home-made anatase $TiO_2$ powder with ~$200 m^2$/g BET surface area. Here, the anatase powder also includes mainly the primary particles very similar to the acicular shapes of the rutile $TiO_2$ powder. The rutile powder showed the fastest decomposition rate and the largest amount in the photoredor, compared with the anatase or P-25 powder, while the anatase powder unexpectedly showed the slowest rate and the smallest amount in the same experiments regardless of almost the same surface area. From results, the excellent photoredox abilities of this rutile powder appears to be due to specific powder preparation method, like a homogeneous precipitation leading to direct crystallization from the solution, regardless of their crystalline structures even when having the similar particle shape and surface area.

• Journal of the Mineralogical Society of Korea
• /
• v.30 no.3
• /
• pp.127-136
• /
• 2017

High pressure has been applied to check the pressure effect on the powdered $TiO_2$-complex, which was synthesized for ultra-violet rays cutoff and antimicrobial applications. $TiO_2$-complex consists of anatase, rutile and silver chloride. Grain size was determined to be ~34 nm. Both anatase and rutile begin structural phase transitions to $ZrO_2$ (baddeleyite)-type crystal structures at 14~16 GPa, then sustain their phases up to 22.7 GPa. Under decompression to 0.0001 GPa (ambient pressure), rutile transforms to another phase with ${\alpha}-PbO_2$ structure, while anatase retains its high pressure structure upon complete decompression. Silver chloride peaks disappear at the low pressures.

• Journal of Powder Materials
• /
• v.10 no.6
• /
• pp.448-455
• /
• 2003

$TiO_2$ nanopowder has been synthesized by means of the flame method using a precursor of titanium tetraisopropoxide (TTIP, Ti$(OC_3H_7)_4)$. In order to clarify the effect of cooling rate of hot flame on the formation of $TiO_2$ crystalline phases, the flame was controlled by varying the mixing ratio and the flow rate of gases. Anatase phase was predominantly synthesized under the condition having the steep cooling gradient in flame, while a slow cooling gradient enabled to form almost rutile $TiO_2$ nanopowder of above 95%.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.148-152
• /
• 2012

Anatase and anatase/rutile $TiO_2$ samples were prepared at $HNO_3$/TTIP molar ratio of 0.1, 0.5, 1.0, and 1.5 to study the effects of the physical properties of $TiO_2$ on photocatalytic decomposition of methylene blue. The physical properties of the samples were measured with XRD, SEM, TEM, BET, FT-IR, and UV-vis spectroscopy. Anatase phase was observed at $HNO_3$/TTIP of 0.1 and anatase/rutile phases were observed at $HNO_3$/TTIP of 0.5~1.5. Rutile crystal phase, mesopore size between $TiO_2$ nanoparticles, and surface OH group on $TiO_2$ sample were gradually increased with increasing the molar ratio of $HNO_3$/TTIP and the residual methylene blue concentration before UV irradiation decreased from 78.0 to 53.3%. After UV irradiation, the residual methylene blue concentrations of the samples prepared at $HNO_3$/TTIP of 0.1, 0.5, 1.0, and 1.5 were 20, 14, 11, and 23%, respectively, and the sample prepared at $HNO_3$/TTIP of 1.0 showed the best photocatalytic ability.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.2
• /
• pp.91-95
• /
• 2002

$TiO_2$ nanopowder was successfully prepared using a titanium tetra-isopropoxide. Subsequently, the effect of pH on the characteristics of the prepared $TiO_2$ nanopowder was evaluated depending on the amounts of the catalysts such as HCI and NH40H. The morphology and phase transformation of $TiO_2$ powder prepared by hydrolysis of titanium tetraisopropoxide were strongly influenced by the presence of the catalysts. In the case of using $NH_4$OH, the morphology of the $TiO_2$ powder exhibited powder form. For the HCI catalyst, it showed bulk or granule form. The phase transformations of amorphous $Ti(OH)_4$ to anatase $TiO_2$ and the anatase to rutile was significantly influenced by the kind and amount of the catalysts.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.4
• /
• pp.165-168
• /
• 2008

Ta-doped thin films were deposited on quartz and indium-tin oxide glass substrates using a co-sputtering method. The Ta-doped films formed a solid solution that induced structural changes from rutile to anatase phase. The anodic photocurrents of the Ta-doped $TiO_2$ electrodes were observed not only in UV but also in the visible light range. The photocurrent response in visible light on Ta-doped $TiO_2$ films are due to bandgap reduction.

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.618-624
• /
• 2018

We developed a mass production method that simultaneously controls the phase transformation and crystal size of $TiO_2$ coatings on multiwalled carbon nanotubes (MWCNTs). Initially, MWCNTs were successfully coated with amorphous 15-20-nm-thick $TiO_2$ by an in-situ sol-gel method. As the calcination temperature increased in both air and argon atmospheres, the amorphous $TiO_2$ was gradually transformed into the fully anatase phase at approximately $600^{\circ}C$, a mixture of the anatase and rutile phases at approximately $700^{\circ}C$, and the fully rutile phase above approximately $800^{\circ}C$. The crystal size increased with increasing calcination temperature. Moreover, above $600^{\circ}C$, the size of crystals formed in air was approximately twice that of crystals formed in argon. The reason is thought to be that MWCNTs, which continuously supported the stresses associated with the reconstructive phase transformation, disappeared owing to complete oxidation in air at these high temperatures.

• Journal of Powder Materials
• /
• v.9 no.2
• /
• pp.110-115
• /
• 2002

In order to obtain the nano size $10wt%Cu-TiO_2$composite powders by mechanical alloying method for useful composite catalysis, the effects of mechanical alloying time on the formationof $10wt%Cu-TiO_2$ composite powders were analyzed. The phase transformation behaviors were experimented as the heat treating temperature increased. Homogeneous 10wt% Cu-rutile type $TiO_2$composite powders were synthesized in 40 hours by mechanical alloying. After 60 hours mechanical alloying 50 nm size $TiO_2$powders were obtained. Both the phase of mechanically alloyed 10 wt% $Cu-TiO_2$ and pure $TiO_2$ powders were not transformed to anatase after annealing at the temperature range between 350 to 500 $^{\circ}C$. The intermetallic compound of $Cu_2Ti_4$O was formed after 10 hours mechanical alloying, however it could be considered that this intemetallic phase dose not prevent the transformation of rutile $TiO_2$ to the anatase phase after heat treatment at the temperature between 350 and $550^{\circ}C$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.315-323
• /
• 1998

$TiO_2$films of rutile and anatase phase have been prepared on silica glass substrates by the sol-gel method using $Ti(i-OC_3H_7)_4$. The effect of additives on the polymorph of $TiO_2$film has been examined in view of degree of crystallization. Third-order nonlinear optical properties of the both film have been investigated by the third harmonic generation method. The measured 3rd order nonlinear optical susceptibility of rutile and anatase thin films were about $1.4{\times}10^{-12}$ and $9.7{\times}10^{-13}$ esu, respectively.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.178-182
• /
• 2011

The Rutile - type brown pigments doped with chromium were synthesized. Samples of $Ti_{1-x}Cr_xO_2$ ($0.02{\leq}X{\leq}0.08$) were synthesized by the solid state method. Solid solution limit of Cr contents to the rutile structure and its coloration were studied. Optimum composition was investigated accordingly. The characteristics of synthesized pigments were analyzed by XRD, SEM, Raman spectroscopy and UV. As a result, single phase of Rutile was observed from $1000^{\circ}C$ by XRD. The maximum limit of solid solution was 0.06 mole $Cr_2O_3$. The glazed sample showed brown color, and the value of CIE $L^*a^*b^*$ was $L^*$ 33.27, $a^*$ 10.64, $b^*$ 20.84.