PP-PHE blends were prepared by mechanical blending using relatively high moecular weight polyhydrozyether(PHE) and popypropylene polymers. PP-PHE blends were prepared and characterized for the purpose of obtaining a dycable PP fibers with the composition of less than 10 wt.% of PHE. 1)yeable PP fibers were acquired through the melt spinning of the PP-PHE blend of comprising less than 10 wt.% of PHE. The resultant fibers had tensile strength of 2~3 g/d, elongation of 330~600%, initial modulus of 22~46 g/d and yield stress of 1.0 g/d, and exhibited markedly improved dyeing ability such as higher absorbance, higher dye adsorption and deeper shade than those of pure PP fiber.

PP-EVOH(poly(vinyl alchol-co-ethylene)) blends were prepared by the mixing of polypropylene and poly(vinyl alcohol-co-ethylene) containing 38mol% of ethylene units (EVOH38) at melt state above PP melting temperature. The materials were characterized by using dynamic mechanical thermal analysis (DMTA), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and contact angle measurement to detemine the glass transition, meltin, decomposition temperatures, and wettability respectively. From the results, PP-EVOH(poly(vinyl alcohol-co-ethylene)) blends exgibits partial miscibility.

단백질 섬유의 일종인 견섬유를 저온 플라즈마로 전처리한 후 효소처리하여 미처리시의 시료와 플라즈마처리 시료 및 효소처리한 시료에 대하여 역학특성, 염색성 및 태평가에 대해 비교, 고찰해 보았다. 인장강도, 인열강도 시험을 통해서 역학특성을 조사하였고, 산성 염료로 염색한 후 염색성의 변화를 알아보고, 염색견뢰도를 시험하였다. 플라즈마 전처리가 태평가에 미치는 영향을 알아보기 위해 Handle-O-Meter를 사용하여 태를 평가하였으며, SEM으로 시료의 표면을 관찰했다. 실험결과 플라즈마 전처리가 효소처리에 잇어서 섬유의 표면 특성 변화에 영향을 미친다고 생각된다.

Microfibers of Poly(ethylene terephthalate)(PET)/Nylon 6 (P/N) was heat set at 170C in a fixed state and then treated with hydrazine at 30C for 5, 10, 15, 20, 30 and 40 h. Weight loss from the hydrazine treatment increased according to the hydrazine concentration(Fig.1). In order to investigate in detail the effect of the electrostatic attraction between the dye anion and hydrazide groups in cooperated by hydrazinolysis, -potential of P/N fiber was measured by streaming potential method. The surface charge density, o, of the fiber was evaluated from the -potential.

The relationship between the chemical structure and properties of UV-cured polyurethane acrylate films has been investigated. Studies have been made on the effects of the molecular weight of polyol, the types of polyol and diluents on the properties such as tensile properties and thermal properties. The glass transition temperature decreased with increasing the molecular weight of polyol. However storage modulus increased by using the diluent containing rigid structure and multifunctional acrylate monomers.