Experimental external collector type solar lumber dryer of $1m^3$ of maximum capacity with $1.6m^3$ of collector area was designed and constructed. The seasonal performance of solar dryer, including air-conditions, energy efficiency, and drying characteristics of 3cm-thick red pine and douglas-fir lumber was investigated. Also, the economic analysis was carried out. Annual average solar drying rate was about 2 times faster than air-drying rate with no significant difference in the amount of drying defects. But in initial drying stage air-drying rate in winter was much faster and those in spring and autumn were slightly slower than solar drying rate in each season. Annual average energy efficiency of solar-dryer and-collector was 25% and 57%, respectively. Fuel savings were over 50% at 15% of energy inflation rate and the payback period was estimated as 6.10 years at 30% of energy inflation rate.

This study was performed to investigate the corrosion of metal fasteners in waterborne preservative-treated wood. Of all the metal tested, steel exhibited the greatest amount of corrosion across all preservatives and exposure conditions whereas stainless steel was totally inert. Galvanized steel corroded at a much lower rate compared to steel and the corrosion of brass was negligible. Among the preservatives, CCA-Type B was the most corrosive system tested. The sequence for the average corrosivity across all metals was: CCA-type B>CCA-Type C${\geq}$ACC${\geq}$CCA-Type A. Across all metals and retentions the salt formulations were more corrosive than the oxide and the corrosion was increased with the increse in the amount of preservative loadings. The amount of corrosion was also increased with the increase in exposure relative humidity (RH) across all metals and presevatives However, at the 60% RH exposure condition, the corrosion of metals was very negligible. Consequently, it can be concluded that across all metals oxide-type preservatives should be used to prevent the corrosion problem of metal fasteners in contact with treated wood and the use of steel nail preservative-treated wood should be avoided without distinction of end-use location, i.e., exterior or interior, and the use of stainless steel or at least brass nail in damp exterior condition was strongly recommended.

81.9% of the cellulose delignified by acetosolv process was hydrolyzed in HCl-$AlCl_3$ hydrolysis system when $AlCl_3$ was used as catalyst in breaking down of glycosidic bond of cellulose. It was well compared that the HCl hydrolysis system without $AlCl_3$ as catalyst showed only 60~61% of the hydrolyzed yield. Also monosaccharide yield including glucose clearly increased when $AlCl_3$ was use. When concentration of HCl and $AlCl_3$ was increased, the hydrolyzed monosaccharide was increased within certain range. The monosaccharid yield out of the hydrolyzed reached 55.4% at optimum conditions which were identified as 20% of Hel solution, 0.03 Mol of $AlCl_3$, $120^{\circ}C$ of reaction temperature and 7 hours of reaction time employed in this study.

Fine structures of some Korean woods were investigated by X-ray diffraction methods. Relative crystallinity measured by the Segal's method and by the area method was $53{\pm}6%$ and $43{\pm}8%$ in softwoods, and $54{\pm}5%$ and $45{\pm}5%$ in hardwoods, respectively. The crystallite dimension in width was $3.11{\pm}0.45nm$ in softwoods and $3.22{\pm}0.25nm$ in hardwoods. In the longitudinal direction, the dimension was $12.79{\pm}0.89nm$ in softwoods and $12.60{\pm}0.72nm$ in hardwoods. The d-spacings of (200) in equatorial and (004) in meridional layers were about 0. 397 run and about. 0.260 nm, respectively. As a result, relative crystallinity, crystallite dimensions and d-spacings of (200) did not show any differences between the softwoods and hardwoods. The ratio of integrated intensities of (002) and (004), however, showed some differences between the softwoods and hardwoods. Namely, it was $0.101{\pm}0.027$ in softwoods and $0.138{\pm}0.037$ in hardwoods.

Fine and alkali-swollen structures of native cellulose fibers were investigated by x-ray diffraction methods. The results of fine structures are shown in Table 1. In meridional x-ray diffractograms, the relative intensity ratio R of (002) to (004) for cellulose I was ca. 0.05 and for regenerated cellulose it was ca. 0.45. It was considered that the transformation from cellulose I to cellulose II resulted from the packing or conformational change of cellulose chain. Finally. although cellulose I was not detected in the alkali-swollen celluloses treated for 1 hr to 24 hrs, washing and drying them resulted in the generation of considerable amounts of cellulose I and the amount decreased with increasing alkali duration.

본 연구는 잣나무 간벌재를 이용한 plywood gusset plate 접합과 toothed metal plate 접합에 대하여 인장력을 가해 조사하였다. plywood gusset plate 접합에 있어서는 합판과 부재 사이를 상온 경화제(초산 비닐 수지)로 접착한 후 6d 못으로 접합한 형태와 단지 합판만을 사용한 형태의 plywood gusset plate 접합 사이의 기계적 특성 차이를 조사했다. toothed metal plate 접합은 plywood gusset plate 접합보다 인장력에서 좋은 behavior를 보였다. 또한 접착제를 가한 plywood gusset plate 접합은 접합제를 가하지 않은 형태보다 큰 하중 지지력을 보였다.

The acetylation of papermaking pulp fiber(SwBKP, SwUKP, HwBKP and HwBCTMF) is carried out to modify the characteristics of pulp and paper. The effects of the addition of acetylated pulp on the filler retention and paper properties were investigated. The acetylation depended upon pulp type and the content of short fiber and fines. The addition of acetylated SwBKP did not deteriorate the retention of clay, talc and calcium carbonate, while the retention of titanium dioxide was increased with the addition of 20% and above. The brightness opacity, air permeability and tear strength were improved, but water resistance, burst strength and folding endurance were decreased by the addition of acetylated SwBKP and SwUKP. The tensile strength of SwBKP was increased until 20% of acetylated pulp is added, and then decreased. The tensile strength of SwUKP, however, was not changed until the acetylated pulp of 25% is added. The dimensional stability was improved by the addition of acetylated pulp and showed the different response to SwBKP and SwUKP.

To investigate the delignification behaviour in solvolysis pulping process, Populus alba ${\times}$ glandulosa H. and Pinus Kuraiensis S. et Z. were cooked with p-cresol and vater solvent(2:8, 5:5, 8:2 v/v) at $175^{\circ}C$ for 9 cooking time levels(20, 40, 60, 80, 100, 120, 140, 160, 180, min). Pulp yield, residual lignin content, de lignification rate, decarborhydration rate were determined. Delignification behaviours were analyzed by TEM. 1. The p-cresol-water solvent cooking of P. alba ${\times}$ glandulosa showed good delignification at the solvent system which the mixture ratio of p-cresol and water were 2:8(v/v), while the cooking of P. koraiensis with the p-cresol and water mixture ratio of 5:5 was no good. 2. P. alba ${\times}$ glandulosa showed three step-delignification phenomena at the solvent system which the mixture ratio of p-cresol and water were 2:8(v/v) anti 5:5(v/v). But P. koraiensis showed a first order delignification reaction at the same mixture ratio of p-cresol and water solvent system. 3. In TEM micrograph obtained for the solvent system which the mixture ratio of p-cresol and water was 5:5(v/v), the partial delignification of the cell corner of P. alba ${\times}$ glandulosa and P. koraiensis were observed at 60min. of cooking time. Complete delignification at the cell corner of P. alba ${\times}$ glandulosa was observed at 160min. and that of P. koraiensis was observed of 180min. of cooking time. 4. In optical microscopic observation, fiber separation of P. alba ${\times}$ glandulosa occured at 120min. and that of P. koraiensis began at 140min. of cooking time. 5. At the solvent system which the mixture ratio of p-cresol and water was 5:5(v/v), middle layer on secondary wall($S_2$) and cell corner of P. alba ${\times}$ glandulosa were more selectively delignified than primary wall(P) and outer layer on secondary wall($S_1$). However P. koraiensis did not showed any difference in delignification between cell wall layers and cell corner.

지진과 관련있는 하중 속도에서 damping을 측정하기 위하여 합판과 목재 사이에 한개의 못을 사용한 접합에 대하여 조사 했다. 조사된 하중은 sine function 의 15Hz와 ASTM하중 속도 사이에서 행했다. Damping 율은 4Hz까지의 하중 속도에서는 증가를 보였으며 그후 15Hz 까지는 점진적으로 감소하였다. 강성은 높은 하중 범위에서 slip moduli가 지속적으로 증가 하였다. 낮은 하중 범위에서 2.5Hz까지 증가 하였으며 그후는 감소 하였다. Damping 율과 slip modulus는 하중 속도와 상관 관계가 낮은 반면 work capacity와 dissipated energy는 높은 상관 관계를 보았다.

아까시나무로부터 두종류의 flavanone인 7, 3', 4' - trihydroxy flavanone과 3, 7, 3', 4', 5' - pentahydroxy flavanonol이 단리되어 $^{13}C$ NMR에 의해 구조가 규명되었다. flavanone은 resorcinol A-ring과 Catechol B-ring으로, flavanonol은 resorcinol A-ring 및 pyrogallol B-ring으로 구성되고 있다.