To investigate the effects of swelling treatment by ammonia on characteristics of carboxymethy1cellulose(CMC) and CMC solution, the domestic kraft pulp pretreated with 5%, 10%, 15% and 20% $NH_4OH$ solution, was carboxymethylated by the standard method, and then the CMC prepared was tested. The physical properties of CMC and CMC solution, such as degree of substitution, transparency. viscosity, weight increase and solubility, were measured, and the comparison with commercial domestic CMC used as a food additive was done. The results obtained were as follows; 1. In CMC manufactured by standard solvent method, hardwood bleached kraft pulp(LBKP) was more substituted than safwood bleached kraft pulp(NBKP), and viscosity of NBKP was higher than that of LBKP. 2. When ammonia swelling treatment was done, degree of substitution gradually decreased with increasing concentration of $NH_4OH$, and degree of substitution of LBKP decreased with a larger range than that of NBKP. 3. When ammonia swelling treatment was done. transparency of CMC solution from LBKP was hardly effected, but in case of NBKP gradually increased with increasing concentration of $NH_4OH$. 4. When ammonia swelling treatment was done, viscosity of CMC solution was higher than that of CMC solution without ammonia swelling treatment. Especially, CMC of high viscosity could be manufactured in 5%, 10% concentration levels of $NH_4OH$. 5. In CMC manufactured from domestic NBKP, CMC at the range of 0.40 to 0.50 in DS was dispersed easily and quickly dissolved, and CMC at more than 0.50 in DS was dispersed slowly in water solution. 6. In comparison with commercial domestic CMC used as a food additive, CMC manufactured from domestic NBKP was higher in DS, and was lower in viscosity and transparency.