• 한국표면공학회지
• /
• 제39권3호
• /
• pp.98-104
• /
• 2006

Al-doped ZnO (AZO) films were deposited on the plastic substrate by inductively coupled plasma (ICP) assisted DC magnetron sputtering. The AZO films were produced by sputtering a metallic target (Zn/Al) in a mixture of argon and oxygen gases. AZO films with an electrical resistivity of ${\sim}10^3\;{\Omega}cm$ and an optical transmittance of 80% were obtained even at a low deposition temperature. In-situ process control methods were used to obtain stable deposition conditions in the transition region without any hysteresis effect. The target voltage was controlled either at a constant DC power. It was found that the ratio of the zinc to oxygen emission intensity, I (O 777)/I (Zn 481) decreased with increasing the target voltage in the transition region. The $Ar/O_2$ plasma treatment improve the adhesion strength between the polycarbonate substrate and AZO films.

• 대한금속재료학회지
• /
• 제49권3호
• /
• pp.250-255
• /
• 2011

The basic properties and electrical characteristics of sputtering films deposited with a commercial cast target and Spark Plasma Sintering (SPS) were compared and analyzed. From the results, the Cu film prepared heating $60^{\circ}C/min$ (SPS process) showed a similar specific resistance compared to the commercial cast Cu film. Also, auording to the results of XRD, SIMS, and TEM. There was not much difference in the crystal structure and impurities between the two films. Consequently, the SPS Cu target was found to have quite similar properties with the commercial one and it is expected to be applied in futare research to the metal wiring material for semiconductor/display devices.

• 한국재료학회지
• /
• 제1권4호
• /
• pp.191-197
• /
• 1991

Composite $TiSi_{2.6}$ target으로 부터 Ti-silicide를 형성시 단결정 Si기판과 다결정 Si내의 dopant의 확산 거동, 그리고 Ti-silicide 박막의 표면 거칠기를 secondary ion mass spectrometry (SIMS), 4-point probe, X-선 회절 분석, 표면 거칠기 측정을 통해 조사하였다. X-선 회절 분석결과 중착된 직후의 중착막은 비정질이었고, 단결정 Si기판에 증착된 막은 $800^{\circ}C$에서 20초간 급속 열처리 시 orthorhombic $TiSi_2$(C54 구조)로 결정화가 이루어졌다. 단결정 Si 기판과 다결정 Si에서 Ti-silicide 충으로의 dopant의내부 확산은 거의 발생하지 않았으며, 주입된 불순물들은 Ti-silicide/Si 계면 근처의 단결정 Si이나 다결정 Si 내부에 존재하고 있었다. 또한 형성된 Ti-silicide 박막의 표면 거칠기는 16-22nm이었다.

• 한국산업보건학회지
• /
• 제25권3호
• /
• pp.254-284
• /
• 2015

Objectives: There is a requirement to select target materials for mutagenicity(Genotoxicity) testing, so we determined to set the test priorities of them by searching the related database. Methods and Results: We searched a number of databases to find information on mutagenicity tests with chemicals under the Occupational Safety and Health Act(OSH Act), such as KOSHANET, National Toxicology Program(NTP), European Chemicals Agency(ECHA), US National Library of Medicine(NLM), and Genetic Toxicology Data Bank(GENE-TOX), as well as ChemIDplus webpage, and presented the information. Also we anticipated their hazards with ACToR sites to confirm the 58 mutagenicity(Genotoxicity) tests we will perform. Conclusions: We presented target materials for mutagenicity testing with specific GLP tests consisting of reverse mutation(Ames), chromosomal aberration and micronucleus test.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.444-445
• /
• 2007

IZO/Al multilayer anode films for flexible top emitting organic light emitting diodes (TOLEDs) were grown on PEN (polyethylen-enaphthelate) substrate using twin target sputter (TTS) system. To investigate electrical and optical properties of IZO/Al multilayer films, 4-point probe method and UV/Vis spectrometer were used, respectively. From a IZO/Al multilayer films with 100nm-thick Al, sheet resistance of $1.4{\Omega}/{\square}$ and reflectance of above 62% at a range of 500~550nm wavelength could be obtained, In addition, structural and surface properties of IZO/Al multilayer films were analyzed by XRD (X-ray diffraction) and FESEM (field emission scanning electron microscopy) and AES (auger electron spectroscope), respectively. Moreover, flexibility of IZO/Al multilayer anode films were examined by bending test method.

• 한국표면공학회지
• /
• 제50권3호
• /
• pp.192-197
• /
• 2017

A 6-way-cross consisting of a 2.75-inch CF flange was used as a main chamber on a PFEIFFER VACUUM TMP station based on a 67 l / sec turbo molecular pump and a diaphragm pump to produce a magnet array with a volume ratio of 5.5: 1.A 1-inch diameter copper target and graphite target were fabricated using MDX-1.5K from Advanced Energy Industries, Inc as a DC power supply. Ion current density of copper target and graphite target was measured by unbalanced magnetron sputtering. The basic pressure condition was $6.3{\times}10^{-7}mbar$ and the process pressure was Ar 50 sccm at $1.0{\times}10^{-2}mbar$ (7.5 mTorr) in the Ar atmosphere. Therefore, the relative density of copper ions reaching the substrate with the measured ion current density was derived.

• Journal of Information Display
• /
• 제8권3호
• /
• pp.5-10
• /
• 2007

Twin target sputtering (TTS) system with a configuration of vertically parallel facing Al targets and a substrate holder perpendicular to the Al target plane has been designed to realize a direct Al cathode sputtering on organic light emitting diodes (OLEDs). The TTS system has a linear twin target gun with ladder type magnet array for effective and uniform confinement of high density plasma. It is shown that OLEDs with Al cathode deposited by the TTS show a relatvely lower leakage current density $({\sim}1{\times}10^{-5}mA/cm^2)$ at reverse bias of -6V, compared to that ($1{\times}10^{-2}{\sim}10^{-3}$ $mA/cm^2$ at -6V) of OLEDs with Al cathodes grown by conventional DC magnetron sputtering. In addition, it was found that Al cathode films prepared by TTS were amorphous structure with nanocrystallines due to low substrate temperature. This demonstrates that there is no plasma damage caused by the bombardment of energetic particles. This indicates that the TTS system with ladder type magnet array could be useful plasma damage free deposition technique for direct Al cathode sputtering on OLEDs or flexible OLEDs.

• 한국재료학회지
• /
• 제24권7호
• /
• pp.344-350
• /
• 2014

Metal films (i.e., Ti, Al and SUH310S) were prepared in a magnetron sputtering apparatus, and their cross-sectional structures were investigated using scanning electron microscopy. The apparatus used consisted of a cylindrical metal target which was electrically grounded, and two anode rings attached to the top and to the bottom of the target. A wire was placed along the center-line of the cylindrical target to provide a substrate. When the electrical potential of the substrate was varied, the metal-film formation rate depended on both the discharge voltage and the electrical potential of the substrate. As we made the magnetic field stronger, the plasma which appeared near the target collected on the plasma wall surface and thereby decreased the bias current. The bias current on the conducting wire was different from that for cation collection. The bias current decreased because the collection of cations decreased when we increased the magnetic-coil current. When the substrate was electrically isolated, the films deposited showed a slightly coarse columnar structure with thin voids between adjacent columns. In contrast, in the case of the grounded substrate, the deposited film did not show any clear columns but instead, showed a densely-packed granular structure. No peeling region was observed between the film and substrate, indicating good adhesion.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권1호
• /
• pp.655-658
• /
• 2007

Characteristics of Al cathode films deposited by using specially designed twin target sputter (TTS) system were investigated. It was found that Al cathode films prepared by TTS were amorphous structure with nanocrystallines due to low substrate temperature and OLEDs fabricated using TTS system have low leakage current density at reverse bias because of effective confinement of energetic particles during sputtering process.

• 한국재료학회지
• /
• 제20권1호
• /
• pp.47-50
• /
• 2010

Various thicknesses of Al-doped ZnO (AZO) films were deposited on glass substrate using pulsed dc magnetron sputtering with a cylindrical target designed for large-area high-speed deposition. The structural, electrical, and optical properties of the films of various thicknesses were characterized. All deposited AZO films have (0002) preferred orientation with the c-axis perpendicular to the substrate. Crystal quality and surface morphology of the films changed according to the film thickness. The samples with higher surface roughness exhibited lower Hall mobility. Analysis of the measured data of the optical band gap and the carrier concentration revealed that there were no changes for all the film thicknesses. The optical transmittances were more than 85% regardless of film thickness within the visible wavelength region. The lowest resistivity, $4.13\times10^{-4}\Omega{\cdot}cm^{-1}$ was found in 750 nm films with an electron mobility $(\mu)$ of $10.6 cm^2V^{-1} s^{-1}$ and a carrier concentration (n) of $1.42\times10^{21} cm^{-3}$.