• 동력기계공학회지
• /
• 제19권6호
• /
• pp.12-18
• /
• 2015

Austenitic stainless steels generally experience the occurrence of chromium-depleted zones at the boundaries, known as sensitization, caused by the carbide precipitation that takes place due to a welding process or heat treatment. Normally, the depleted zones become the focus of the intense corrosion. In this study, the Cr-free organic/inorganic hybrid solution was developed, and the artificially degraded STS316S and STS347H with the solution-coating investigated the corrosion resistance by salt spray test. Both the OIBD-1 and OIBD-2 solutions improved the corrosion resistance of STS310S and STS347H. The corrosion resistance with the OIBD-1 solution was better than that of OIBD-2 solution. Additionally, Both solutions have been proven excellence in adhesion ability, boiling water resistance and flexibility. However, a problem of rubbing after the boiling was found out to be overcome.

• Transactions on Electrical and Electronic Materials
• /
• 제16권4호
• /
• pp.190-193
• /
• 2015

Insulation breakdown characteristics of an inverter surge resistant enameled wire were investigated in a twisted pair prepared with organic/inorganic hybrid nanocomposite. Organic polymer was polyesterimide-polyamideimide (EI/AI) and inorganic material was a nano-sized silica. The enamel thickness was 50 μm and the diameters of enameled copper wires were 0.75, 1.024, and 1.09 mm, respectively. There were many air gaps in a twisted pair. Therefore, when the voltage was applied to the twisted pair, enamel erosion took place in the air gap area because of partial discharge according to Paschen’s law. The insulation lifetime of the hybrid wire (HW) was 41,750 sec, which was 515.4 times more than the 81 sec of EI/AIW. In addition, the shape parameter of HW was 2.58, which was 3.4 times higher than 0.75 of EI/AIW.

• 동력기계공학회지
• /
• 제20권5호
• /
• pp.20-28
• /
• 2016

This study has developed an organic/inorganic hybrid solution by addition of $SiO_2$ polysilicate and Melamine to the urethane. The three types of cold rolled steel were evaluated a corrosion resistance properties by using these solutions. The urethane solution(U) and the urethane solution with $SiO_2$ polysilicate($US_7$) were generate a lot of corrosion. The urethane solution with $SiO_2$ polysilicate and melamine($US_7M_3$) was excellent in corrosion resistance, regardless of the steel type. In addition, corrosion resistance has been shown to depend on the tensile strength. The appearance of coating by U and $US_7$ solution is bumpy surface, and were a lot of fine defects. $US_7M_3$ solution is made a sophisticated molecular cross-linking structure inside the coating, it was a slick surface. Other characteristics are exhibited the excellent property for all solutions.

• Korean Chemical Engineering Research
• /
• 제46권1호
• /
• pp.112-117
• /
• 2008

1:1로 몰 비가 조절된 glycidoxypropyl trimethoxysilane(GPTMS)과 methyl triethoxysilane(MTES)을 출발물질로 하여 sol-gel법에 의해 유-무기 혼성 용액을 제조하였다. 이 용액에 spiropyran계 광 변색 염료를 ethylacetate(EA)에 용해시킨 용액을 혼합하여 광 변색 코팅 용액을 제조하였다. 그 후 기재인 polycarbonate 시트에 스핀 코팅 시키고 $100^{\circ}C$에서 2 h 동안 열 경화 시켜 광 변색 코팅 막을 제조하였다. 코팅 막은 UV 광을 조사함에 의해 가역적인 색변화를 보여주었다. 이때 코팅 막의 소색속도는 코팅 용액 중의 EA의 첨가량이 증가됨에 따라 증가하였다.

• 한국산학기술학회논문지
• /
• 제7권6호
• /
• pp.1296-1301
• /
• 2006

눈은 자외선과 가시광선에 노출되어 있다. 눈은 자외선 노출에 해로우므로 모든 자외선으로부터 눈을 보호해야 한다. 본 연구에서는 자외선 차단을 위해 투명 플라스틱에 유-무기 하이브리드 재료와 자외선 흡수제의 배합에 의한 자외선 차단 코팅하였고, PMMA, CR 39 및 PC기재에 적용하여 자외선 차단 효과를 조사하였다. 자외선 흡수제의 양이 증가할수록 자외선의 투과도는 낮았다. PMMA의 경우 자외선 투과도를 현저히 감소시켰으며 CR 39에서도 자외선 차단 효과가 있는 것으로 나타났다. 한편, PC자체에서는 자외선 차단효과가 있는 것으로 평가되었다. CR 39 렌즈의 부착력, 내약품성, 내온수성은 우수하였고, 연필 경도의 경우 4H였으며 내마모성은 좋지 않았다.

• 마이크로전자및패키징학회지
• /
• 제25권4호
• /
• pp.1-7
• /
• 2018

As the performance and density of IC (integrated circuit) devices increase, power and signal integrities in the global interconnects of advanced packaging technologies are becoming more difficult. Thus, the global interconnect technologies should be designed to accommodate increased input/output (I/O) counts, improved power grid network integrity, reduced RC delay, and improved electrical crosstalk stability. This requirement resulted in the fine-pitch interconnects with a low-k dielectric in 3D packaging or wafer level packaging structure. This paper reviews an organic-inorganic hybrid material as a potential dielectric candidate for the global interconnects. An organic-inorganic hybrid material called polysiloxane can provide spin process without high temperature curing, an excellent dielectric constant, and good mechanical properties.

• 한국세라믹학회지
• /
• 제41권5호
• /
• pp.349-352
• /
• 2004

Organic-inorganic hybrid sol based on ZrO$_2$-SiO$_2$ system was prepared by sol-gel process. Firstly, ZrO$_2$ non-aqueous precursor sol was synthesized and then organosilane compounds which include epoxy silane (GPTS; 3-g1ycidoxypropyl tri-methoxysilane) and acryl silane (ACS; (3-(tri-methoxysilyl)propylmethacrylate)) were added to ZrO$_2$precursor sol for hybridization. Finally, com-mercial silica sol was added to improve the mechanical properties. Synthesized organic-inorganic Zr-hybrid sol was coated on polycarbonate substrate for enhancing it’s mechanical properties, especially hardness. Vicker’s hardness of polycarbonate sub strate was increased from 13.6 to 17.8 MPa and its pencil hardness was increased from 2 to 7 H, respectively, after coating and drying at 10$0^{\circ}C$ for 30 min.

• The Korean Journal of Ceramics
• /
• 제7권1호
• /
• pp.1-5
• /
• 2001

Inorganic-organic hybrid Li$^+$ ion conductors were prepared by the sol-gel process. Tetramethyl orthosilicate (TMOS), polyethylene glycol 200 (PEG$_200$) and lithium bis (trifluoro-methylsulfony) imide were used as raw materials and $H_2O$ was used as a solvent. Hybrid Li$^+$ ion conductor prepared by the sol-gel process showed very high ion conductivities of log${\sigma}_R.T$(S/cm)=-3.73, log${\sigma}_60$(S/cm)=-3.00 at room temperature and $60^{\circ}C$, respectivery. Decomposition voltage was 3.1 V.

• 폴리머
• /
• 제34권5호
• /
• pp.405-409
• /
• 2010

내부식성이 우수한 기능기를 함유하는 새로운 졸-젤 전구체를 합성하고 이를 함유하는 유무기 하이브리드 코팅 조성물을 제조하였다. 코팅 조성물에는 통상의 졸-젤 전구체로 tetraethoxysilane을 사용하였고 비스페놀 A 타입의 에폭시를 실란화합물로 개질하였으며, 졸-젤 반응을 위하여 물과 HCl을 촉매로 사용하였다. 각 조성물은 졸-젤 전구체의 종류, 함량 등을 변화하여 다양한 코팅 조성물을 제조하였고 iron 기판위에 딥코팅하여 열경화하였다. 코팅된 iron 기판의 내부식성을 평가하기 위하여 염수분무시험과 전기화학적 임피던스 분광법을 사용하였는데, 내부식성 기능기를 함유한 유무기 하이브리드 코팅재가 일반적인 하이브리드 코팅재에 비해 매우 향상된 내부식성을 나타냄을 확인할 수 있었다. 내부식성 기능기를 함유한 코팅재의 경우, 0.1 M NaCl에서 500시간 이상 초기의 임피던스를 유지하는 반면, 일반적인 코팅재는 24시간 이후에 임피던스가 감소하는 것을 관찰할 수 있었다.

• 공업화학
• /
• 제23권1호
• /
• pp.53-58
• /
• 2012

투명한 플라스틱 필름의 표면경도를 향상시키기 위하여 유-무기 하이브리드 코팅 용액을 졸-겔 공정을 이용하여 합성하였다. 무기성분으로 콜로이드 실리카와 유기성분으로 PMMA, 유-무기 성분 간의 결합력을 향상시켜 하이브리드 코팅 층의 특성을 더욱 향상시키기 위하여 실란커플링제로서 vinyl trimethoxy silane (VTMS)과 [3-(metha cryloyloxy)] propyl trimethoxy silane (MAPTMS)를 이용하였고, 알콕시 실란의 종류, 콜로이드 실리카/PMMA의 함량비 등의 반응조건에 따라 콜로이드 실리카/PMMA 졸을 합성하였다. 이러한 졸을 PET 필름에 바코팅시키고, 열경화 시켜 하드코팅막을 제조하여 물리적 화학적 특성을 조사하였다. PMMA에 비해서 하이브리드 형태에서 코팅 막의 연필경도와 기재와의 부착력이 우수하였다.