We have successfully fabricated a Metal-Ferroelectric-Insulator-Semiconductor (MFIS) structure using Bi$\sub$4-x/La$\sub$x/Ti$_3$O$\sub$12/ (BLT) ferroelectric thin film and SiO$_2$/Nitride/SiO$_2$ (ONO) stacked buffer layers for single transistor type ferroelectric nonvolatile memory applications. BLT films were deposited on 15 nm-thick ONO buffer layer by sol-gel spin-coating. The dielectric constant and the leakage current density of prepared ONO film were measured to be 5.6 and 1.0 x 10$\^$-8/ A/$\textrm{cm}^2$ at 2MV/cm, respectively, It was interesting to note that the crystallographic orientations of BLT thin films were strongly effected by pre-bake temperatures. X-ray diffraction patterns showed that (117) crystallites were mainly detected in the BLT film if pre-baked below 400$^{\circ}C$. Whereas, for the films pre-baked above 500$^{\circ}C$, the crystallites with preferred c-axis orientation were mainly detected. From the C-V measurement of the MFIS capacitor with c-axis oriented BLT films, the memory window of 0.6 V was obtained at a voltage sweep of ${\pm}$8 V, which evidently reflects the ferroelectric memory effect of a BLT/ONO/Si structure.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.7
• /
• pp.662-666
• /
• 2005

Silicon nitride $(SiN_x)$ film is a promising material for anti-reflection coating and passivation of multicrystalline silicon (me-Si) solar cells. In this work, a plasma-enhanced chemical vapor deposition (PECVD) system with batch-type reactor tube was used to prepare highly robust $SiN_x$ films for screen-printed mc-Si solar cells. The Gas flow ratio, $R=[SiH_4]/[NH_3]$, in a mixture of silane and ammonia was varied in the range of 0.0910.235 while maintaining the total flow rate of the process gases to 4,200 sccm. The refractive index of the $SiN_x$ film deposited with a gas flow ratio of 0.091 was measured to be 2.03 and increased to 2.37 as the gas flow ratio increased to 0.235. The highest efficiency of the cell was $14.99\%$ when the flow rate of $SiH_4$ was 350 sccm (R=0.091). Generally, we observed that the efficiency of the mc-Si solar cell decreased with increasing R. From the analysis of the reflectance and the quantum efficiency of the cell, the decrease in the efficiency was shown to originate mainly from an increase in the surface reflectance for a high flow rate of $SiH_4$ during the deposition of $SiN_x$ films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.18-22
• /
• 2006

Epitaxial aluminum nitride films on 6H-SiC (0001) were fabricated using reactive RF magnetron sputtering and post-deposition rapid thermal annealing. The electrical properties of AIN films depending on film thickness and measurement temperature have been observed. Full width at half maximum of AIN (0002) was $0.1204^{\circ}$ (about 430 arcsec) X-ray rocking curve results. The equivalent oxide thickness (EOT) of AIN film was estimated as about 10 nm and the leakage current density was within the order of $10^{-8} 4/cm^2$. The dielectric constant of AIN film estimated from the accumulation region of C-V curve measured at $300^{\circ}C$ was 8.3. The dynamic dielectric constant was obtained as 5.1 from J vs. 1/T plots at the temperature ranging from R.T. to $300^{\circ}C$ From above, estimation temperature dependance of the electrical properties of Al/AIN/SiC MIS devices was affirmed and useful data compilation for the reliabilities of SiC MIS is expected.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.10
• /
• pp.831-837
• /
• 2002

Scaled SONOS transistors have been fabricated by 0.35$\mu\textrm{m}$ CMOS standard logic process. The thickness of stacked ONO(blocking oxide, memory nitride, tunnel oxide) gate insulators measured by TEM are 2.5 nm, 4.0 nm and 2.4 nm, respectively. The SONOS memories have shown low programming voltages of ${\pm}$8.5 V and long-term retention of 10-year Even after 2 ${\times}$ 10$\^$5/ program/erase cycles, the leakage current of unselected transistor in the erased state was low enough that there was no error in read operation and we could distinguish the programmed state from the erased states precisely The tight distribution of the threshold voltages in the programmed and the erased states could remove complex verifying process caused by over-erase in floating gate flash memory, which is one of the main advantages of the charge-trap type devices. A single power supply operation of 3 V and a high endurance of 1${\times}$10$\^$6/ cycles can be realized by the programming method for a flash-erased type EEPROM.

• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1375-1377
• /
• 2001

This paper describes the fabrication and characteristics of CrN thin-film type pessure sensors, in which the sensing elements were deposited on SUS. 630 diaphragm by DC reactive magnetron sputtering in an argon-nitride atmosphere(Ar-(10%) $N_2$). The optimized condition of CrN thin-film sensing elements was thickness range of 3500$\AA$ and annealing condition($300^{\circ}C$, 3 hr) in Ar-10 %$N_2$ deposition atmosphere. Under optimum conditions, the CrN thin-films for strain gauges is obtained a high resistivity, $\rho$=1147.65 ${\mu}{\Omega}$cm, a low temperature coefficient of resistance, TCR=-186 ppm/$^{\circ}C$ and a high temporal stability with a good longitudinal, 11.17. The output sensitivity of fabricated CrN thin-film type pressure sensors is 2.36 mV/V, 4$\sim$20 mA and the maximum non-linearity is 0.4 %FS and hysteresis is less than 0.2 %FS..

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.7
• /
• pp.564-569
• /
• 2002

Heteroepitaxial GaN films were grown on sapphire substrates in order to study the effects of the buffer layer's surface roughness and thermal treatment on the epitaxial layer's quality. For this, GaN buffer layers were grown at $550^{\circ}C$ with various TMGa flow rates and durations of growth, and annealed at $1010^{\circ}C$ for 3 min after the temperature was raised by 23 ~ $92^{\circ}C/min$, and then GaN epitaxial layers were grown at $1000^{\circ}C$. It has been found that the buffer layer's surface roughness and the thermal treatment condition are critical factors on the quality of the epitaxial layer. When a buffer layer was frown with a TMGa flow rate of $24\mu mole/min$ for 30 sec, the surface roughness of the buffer lather was minimum and when the thermal ramping rate was $30.6^{\circ}C/min$ on this layer, the successively grown epitaxial layer's crystalline and optical qualities were optimized with a specular morphology. The minimum full width at half maximum(FWHM) of GaN(0002) x-ray diffraction peak and that of near-band-edge(NBE) peak from a room temperature photoluminescence (PL) were 5 arcmin and 9 nm, respectively.

• Electrical & Electronic Materials
• /
• v.8 no.1
• /
• pp.90-94
• /
• 1995

Reactive Ion Etching(RIE) of Si$_{3}$N$_{4}$ in a CF$_{4}$/O$_{2}$ gas plasma exhibits such good anisotropic etching properties that it is widely employed in current VLSI technology. However, the RIE process can cause serious damage to the silicon surface under the Si$_{3}$N$_{4}$ layer. When an atmospheric pressure chemical vapor deposited(APCVD) SiO$_{2}$ layer is used as a etch-stop material for Si$_{3}$N$_{4}$, it seems inevitable to get a good etch selectivity of Si$_{3}$N$_{4}$ with respect to SiO$_{2}$. Therefore, we have undertaken thorough study of the dependence of the etch rate of Si$_{3}$N$_{4}$ plasmas on $O_{2}$ dilution, RF power, and chamber pressure. The etch selectivity of Si$_{3}$N$_{4}$ with respect to SiO$_{2}$ has been obtained its value of 2.13 at the RF power of 150 W and the pressure of 110 mTorr in CF$_{4}$ gas plasma diluted with 25% $O_{2}$ by flow rate.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.455-460
• /
• 2005

Deposition of TiN$_{x}$ film was conducted with a DC sputtering technique. The effect of the processing parameters such as substrate temperature, deposition time, working pressure, bias power, and volumetric flowing rate ratio of Ar to N$_{2}$ gas on the resistivity of TiN$_{x}$ film was systematically investigated. Three kinds of substrates, soda-lime glass, (100) Si wafer, and 111m thermally grown (111) SiO$_{2}$ wafer were used to explore the effect of substrate. The phase of TiN$_{x}$ film was analyzed by XRD peak pattern and deposition rate was determined by measuring the thickness of TiNx film through SEM cross-sectional view. Resistance was obtained by 4 point probe method as a function of processing parameters and types of substrates. Finally, optimum condition for synthesizing TiN$_{x}$ film having lowest resistivity was discussed.

• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.317-323
• /
• 1999

Si3N4-TiC composites have been known as electrically conductive ceramics. $Si_3N_4-TiC$ composites with 2 wt% $Al_2O_3$ and 4 wt% $Y_2O_3$ were hot pressed in $N_2$ environment. The mechanical properties including hardness, fracture toughness, and flexural strength and tribological properties were investigated as a function of TiC content. $Si_3N_4-40$ vol% TiC composite was hot pressed at $1,750^{\circ}C$, $1,800^{\circ}C$, and $1,850^{\circ}C$ for 1, 3 and 5 hours in $N_2$ gas. Mechanical and tribolgical properties depended on microstructures, which were controlled by hte TiC content, hot press temperature, and hot press holding time. However, mechanical properties and tribological behaviors were degraded by the chemical reaction between TiC and N. The chemically reacted products such as TiCN, SiC, and $SiO_2$ were detered by the X-ray diffraction analysis.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.443-448
• /
• 1997

Titanium carbonitride (Ti(CxN1-x)) ceramics were prepared by hot pressing of the mixture of TiN and graphite. Hot pressing was performed in a graphite mold at 198$0^{\circ}C$ for 40 min under 44 MPa in N2 atmosphere. The effect of graphite addition on sinterability and the mechanical properties of titanium carbonitride were investigated. In this study, the solubility limit of graphite in Ti(CxN1-x) was slightly below 10 wt% based on the results of XRD analysis. Within the solubility limit, graphite dissolved completely into titanium nitride and formed the single phase Ti(CxN1-x) solid solution. Peak relative density of 99% and hardness of 16 GPa were observed for Ti(CxN1-x) ceramics with 7 wt% graphite while maximum flexural strength of 500 MPa and fracture toughness of 4.0 MPa.m1/2 were observed for Ti(CxN1-x) ceramics with 10 wt% graphite. The electrical resistivities of the ceramics with 7 wt% and 10 wt% graphite were observed 40 {{{{ mu OMEGA }}cm and 50 {{{{ mu OMEGA }}cm respectively.