• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.245-248
• /
• 1991

Recently, oxide semiconductor gas sensors consisted of n-type semiconductor materials such as $SnO_2$, ZnO and $Fe_2O_3$ have been widely used to detect reducing gases. In this paper, we made the thick-film ZnO gas sensors with $PdCl_2$ as a catalyst and investigated the sensitivity to CO gas. In the thick-film Zno sensor, the highest sensitivity was shown in the sensor with 1wt.% of $PdCl_2$ which was sintered for 1 hour at $700^{\circ}C$ and operated at $300^{\circ}C$.

• Journal of Environmental Science International
• /
• v.8 no.6
• /
• pp.685-690
• /
• 1999

The pollution characteristics of groundwaters in Taegu City and correlation coefficients(r) between water pollution indicators were investigated for two years from January 1996 to December 1997. Volatile organic compounds such as TCE(tri-chloroethylene), PCE(tetrachloroethylene), l,l,l-trichloroethane, THM(trihalo-methane), dichloromethane, pesticides such as diazinon, parathion, malathion, and toxic inoganic matters such as As, Hg, Se, Pb, Cd, $Cr_6^+,$ CN were not detected in the groundwaters. Mean values of groundwater pollution indicators were below drinking-water standards, but hardness, $KMnO_4-C(potassium$ permanganate consumption), evaporate residues, $SO_4^{-2},\;Fe,\;NO_3^{-}-N,$ color and turbidity exceeded a little in some samples. As groundwater became deeper, hardness and evaporate residues remarkably increased, but $KMnO_4-C,\;NO_3^{-}-N,\;Cl-,$ color, turbity and bacteria decreased. $KMnO_4-C,$ evaporate residues, $Cl^-\;and\;SO_4^{-2}$ were very high at industrial and commercial areas, and $NO_3^--N$ and $NH_4^+-N$ were very high at agricultural and forest areas. It showed high positive significances in the relationships between hardness and each of evaporate residues, $SO_4^{-2}$, Zn and Mn, $KMnO_4-C$ and each of color, turbidity and Zn, color and each of turbidity, Cu, Zn and Mn, turbidity and each of Fe, Cu, Zn and Mn, and evaporate residues and each of $Cl^-,\;SO_4^{-2}$ and Zn.

• Journal of the Korean Magnetics Society
• /
• v.13 no.3
• /
• pp.121-126
• /
• 2003

The electromagnetic properties and microstructures of the basic composition of (N $i_{0.2}$C $u_{0.2}$Z $n_{0.6}$)$_{1.085}$(F $e_2$ $O_3$)$_{0.915}$ were invested by changing of the additive Sn $O_2$, CaO amounts and ferrite processes. There is no variation of grain size by changing additive amount. It can reduce the total loss when (N $i_{0.2}$C $u_{0.2}$Z $n_{0.6}$)$_{1.085}$(F $e_2$ $O_3$)$_{0.915}$ composition sintered at 1150 $^{\circ}C$ better than 130$0^{\circ}C$. Additive CaO confirmed of useful addition for the reduce total loss, because it increasing sintering density. Decreasing total loss were observed by adding both Sn $O_2$ 0.06 wt％ and CaO 0.4 wt％.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.3
• /
• pp.177-182
• /
• 2013

Transparent thin film transistors (TTFT) were fabricated on $N^+$ Si wafers. $SiO_2$, $Si_3N_4/SiO_2$ and $Al_2O_3/SiO_2$ grown on the wafers were used as gate insulators. The rf magnetron sputtered zinc tin oxide (ZTO) films were adopted as active layers. $N^+$ Si wafers were wet-oxidized to grow $SiO_2$. $Si_3N_4$ and $Al_2O_3$ films were deposited on the $SiO_2$ by plasma enhanced chemical vapor deposition (PECVD) and atomic layer deposition (ALD), respectively. The mobility, $I_{on}/I_{off}$ and subthreshold swing (SS) were obtained from the transfer characteristics of TTFTs. The properties of gate insulators were analyzed by comparing the characteristics of TTFTs. The property variation of the ZTO TTFTs with time were observed.

• Journal of the Korean Magnetics Society
• /
• v.21 no.3
• /
• pp.88-92
• /
• 2011

We grew $Zn_{0.4}Fe_{2.6}O_4$ thin films using Pulsed Laser Deposition and studied their crystal structure and magnetical characteristics as a function of growth temperature ($T_g$). For the film with $T_g=300^{\circ}C$, X-ray reflections from ${\alpha}-Fe_2O_3$ and ZnO were observed. However, when $T_g$ was increased from 300 to $500^{\circ}C$, crystal structure of inverse spinel was stabilized with the crystal orientation of $Zn_{0.4}Fe_{2.6}O_4(111)/Al_2O_3(0001)$ without any detection of ${\alpha}-Fe_2O_3$ and ZnO phases. The surface morphology shows flattening behavior with increasing $T_g$ from 300 to $500^{\circ}C$. These observations indicate that Zn is substituted into tetrahedron A-site of the inverse-spinel $Fe_3O_4$. M-H curves exhibit clear ferromagnetism for the sample with $T_g=500^{\circ}C$ whereas no ferromagnetism is observed for the film with $T_g=300^{\circ}C$.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.9
• /
• pp.2503-2508
• /
• 2010

ZnO thin films were grown on Si or $SiO_2$/Si substrates, at growth temperatures ranging from 150 to $400^{\circ}C$, by atomic layer deposition (ALD) using diethylzinc and water. Despite the large band gap of 3.3 eV, the ALD ZnO films show high n-type conductivity, i.e. low resistivity in the order of $10^{-3}\;{\Omega}cm$. In order to understand the high conductivity of ALD ZnO films, the films were characterized with X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, elastic recoil detection, Rutherford backscattering, Photoluminescence, and Raman spectroscopy. In addition, the various analytical data of the ZnO films were compared with those of ZnO single crystal. According to our analytical data, metallic zinc plays an important role for the high conductivity in ALD ZnO films. Therefore when the metallic zinc was additionally oxidized with ozone by a modified ALD sequence, the resistivity of ZnO films could be adjusted in a range of $3.8{\times}10^{-3}\;{\sim}\;19.0\;{\Omega}cm$ depending on the exposure time of ozone.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.8
• /
• pp.1738-1742
• /
• 2009

Nanocrystalline Zn$Fe_2O_4$ oxide-semiconductor with spinel structure was synthesized by the polymerized complex (PC) method and investigated for its photocatalytic and photoelectric properties. The observation of a highly pure phase and a lower crystallization temperature in Zn$Fe_2O_4$ made by PC method is in total contrast to that was observed in Zn$Fe_2O_4$ prepared by the conventional solid-state reaction (SSR) method. The band gap of the nanocrystalline Zn$Fe_2O_4$ determined by UV-DRS was 1.90 eV (653 nm). The photocatalytic activity of Zn$Fe_2O_4$ prepared by PC method as investigated by the photo-decomposition of isopropyl alcohol (IPA) under visible light (${\geq}$ 420 nm) was much higher than that of the Zn$Fe_2O_4$ prepared by SSR as well as Ti$O_{2-x}N_x$. High photocatalytic activity of Zn$Fe_2O_4$ prepared by PC method was mainly due to its surface area, crystallinity and the dispersity of platinum metal over Zn$Fe_2O_4$.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.9
• /
• pp.121-127
• /
• 1994

The capability for application of rf magnetron sputterred and post annealed BaTiO$_{3}$ thin films in dielectrics AC drived TFELD(thin film electroluminescent device) was investigated. The dielectric constant of the thin films slightly increased up to about 25 with increase fothe post annealing temperature in the range of 210$^{\circ}C$-480$^{\circ}C$. The dielectric loss was about 0.005-0.01 except for the high frequency range above 100kHz and nearly independent on post annealing temperature. The BaTiO$_{3}$ thin film used for TFELD was annealed at 480.deg. C and Si$_{3}$N$_{4}$ thin film was inserted between BaTiO$_{3}$, lower dielecrics and ZnS:Mn, phosphor layer for stable driving of the device and for fear of interdiffusion. Regardless of the frequency of the applied sine wave voltage, the threshold voltage of the prepared TFELD was 65volt and saturated brightness was about 3000cd/m$^{2}$ at 130volt(2kHz sine wave), 65volt above V$_{TH}$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.330-332
• /
• 2013

소 분위기에서 플라즈마 표면 처리의 경우 기판 표면에 존재하는 수소와 탄소 유기물들이 산소와 반응하여 $H_2O$와 $CO_2$ 등으로 제거되며 표면에 오존 결합을 유도하여 표면 에너지를 증가시키는 것으로 알려져 있다. ZnO 나노구조물을 성장시키는 방법으로는 MOCVD (Metal-Organic Chemical Vapor Deposited), PLD (Pulsed Laser Deposition), VLS (Vapor-Liquid-Solid), Sputtering, 습식화학합성법(Wet Chemical Method) 방법 등이 있다. 그중에서도 습식화학합성법은 쉽게 구성요소를 제어할 수 있고, 저비용 공정과 낮은 온도에서 성장 가능하며 플렉서블 소자에도 적용이 가능하다. 그러므로 본 연구에서는 플라즈마 표면처리에 따라 표면에너지를 변화하여 습식화학합성법으로 성장시킨 ZnO nanorods의 밀도를 제어하고 photolithography 공정 없이 패터닝 가능성을 유 무를 판단하는 연구를 진행하였다. 기판은 Si wafer (100)를 사용하였으며 세척 후 표면에너지 증가를 위한 플라즈마 표면처리를 실시하였다. 분위기 가스는 Ar/$O_2$를 사용하였으며 입력전압 400 W에서 0, 5, 10, 15, 60초 동안 각각 실시하였다. ZnO nanorods의 seed layer를 도포하기 위하여 Zinc acetate dehydrate [Zn $(CH_3COO)_2{\cdot}2H_2O$, 0.03 M]를 ethanol 50 ml에 용해시킨 후 스핀코팅기를 이용하여 850 RPM, 15초로 5회 실시하였으며 $80^{\circ}C$에서 5분간 건조하였다. ZnO rods의 성장은 Zinc nitrate hexahydrate [$Zn(NO_3)_2{\cdot}6H_2O$, 0.025M], HMT [$C6H_{12}N_4$, 0.025M]를 deionized water 250 ml에 용해시켜 hotplate에 올리고 $300^{\circ}C$에서 녹인 후 $200^{\circ}C$에서 3시간 성장시켰다. ZnO nanorods의 성장 공정은(Fig. 1)과 같다. 먼저 플라즈마 처리한 시편의 표면에너지 측정을 위해 접촉각 측정 장치[KRUSS, DSA100]를 이용하였다. 그 결과 0, 5, 10, 15, 60 초로 플라즈마 표면 처리했던 시편이 각각 Fig. l, 2와 같이 $79^{\circ}$, $43^{\circ}$, $11^{\circ}$, $6^{\circ}$, $7.8^{\circ}$로 측정되었으며 이것을 각각 습식화학합성법으로 ZnO nanorods를 성장 시켰을 때 Fig. 3과 같이 밀도 차이를 확인할 수 있었다. 이러한 결과를 바탕으로 기판의 표면에너지를 제어하여 Fig. 4와 같이 나타나며 photolithography 공정없이 ZnO nanorods를 패터닝을 할 수 있었다. 본 연구에서는 플라즈마 표면 처리를 통하여 표면에너지의 변화를 제어함으로써 ZnO nanorods 성장의 밀도 차이를 나타냈었다. 이러한 저비용, 저온 공정으로 $O_2$, CO, $H_2$, $H_2O$와 같은 다양한 화학종에 반응하는 ZnO를 이용한 플렉시블 화학센서에 응용 및 사용될 수 있고, 플렉시블 디스플레이 및 3D 디스플레이 소자에 활용 가능하다.

• Korean Journal of Materials Research
• /
• v.22 no.4
• /
• pp.180-184
• /
• 2012

Nanostructures of ZnO, such as nanowires, nanorods, nanorings, and nanobelts have been actively studied and applied in electronic or optical devices owing to the increased surface to volume ratio and quantum confinement that they provide. ZnO seed layer (about 40 nm thick) was deposited on Si(100) substrate by RF magnetron sputtering with power of 60 W for 5 min. ZnO nanorods were grown on ZnO seed layer/Si(100) substrate at $95^{\circ}C$ for 5 hr by hydrothermal method with concentrations of $Zn(NO_3)_2{\cdot}6H_2O$ [ZNH] and $(CH_2)_6N_4$ [HMT] precursors ranging from 0.02M to 0.1M. We observed the microstructure, crystal structure, and photoluminescence of the nanorods. The ZnO nanorods grew with hexahedron shape to the c-axis at (002), and increased their diameter and length with the increase of precursor concentration. In 0.06 M and 0.08 M precursors, the mean aspect ratio values of ZnO nanorods were 6.8 and 6.5; also, ZnO nanorods had good crystal quality. Near band edge emission (NBE) and a deep level emission (DLE) were observed in all ZnO nanorod samples. The highest peak of NBE and the lower DLE appeared in 0.06 M precursor; however, the highest peak of DLE and the lower peak of NBE appeared in the 0.02 M precursor. It is possible to explain these phenomena as results of the better crystal quality and homogeneous shape of the nanorods in the precursor solution of 0.06 M, and as resulting from the bed crystal quality and the formation of Zn vacancies in the nanorods due to the lack of $Zn^{++}$ in the 0.02 M precursor.