• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.63 no.11
• /
• pp.1533-1537
• /
• 2014

$WO_3/Ag/WO_3$ multilayer was researched by using RF magnetron sputtering with transparent electrode. Process gas flow ratio with $Ar/O_2$ were selected the optimum conditions at 70sccm/2sccm and $WO_3$ thin film at its conditions was appeared at transmittance about 80% in the visible light region to the average. $WO_3/Ag/WO_3$ multilayer thin films were fabricated from the same process condition which was the same gas flow ratio of Ar and $O_2$ $WO_3/Ag/WO_3$ thin films were appeared transmittance about 93% and sheet resistance about $6.41{\Omega}/{\square}$. From the SEM images, each thin films were appeared when $WO_3$ is 40nm and $O_2$ is 10nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.2
• /
• pp.118-123
• /
• 2007

The purpose of this work was to investigate the design and fabrication process effects on electrical properties in high capacitance multilayer ceramic capacitor (MLCC) with nickel electrode. Dielectric breakdown voltage and insulation resistance value were decreased with increasing stack layer number, but dielectric constant and capacitance were increased. With increasing green sheet thickness, dielectric breakdown voltage, C-V and I-V properties were also increased. The major reasons of the effects were thought to be the defects generated extrinsically during fabrication process and interfacial reactions formed between nickel electrode and dielectric layer. These investigations clearly showed the influence of both green sheet thick ness and stack layer number on the electrical properties in fabricating the MLCC.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.114-114
• /
• 1999

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.12
• /
• pp.1118-1123
• /
• 2008

High voltage multilayer ceramic capacitors (MLCCs) are classified into two classes-those for temperature compensation (class I) and high dielectric constant materials (class II). We manufactured high voltage MLCC with temperature coefficient characteristics of C0G and X7R and studied the characteristics of electric properties. Also we studied the characteristics of dielectric breakdown voltage (V) as the variation of thickness in the green sheet and how to pattern the internal electrodes. The dielectric breakdown by electric field was caused by defects in the dielectric materials and dielectric/electrode interface, so the dielectric thickness increased, the withstanding voltage per unit (E) thickness decreased. To overcome this problem, we selected the special design like as floating electrode and this design affected the increasing breakdown voltage(V) and realized the constant withstanding voltage per unit thickness(E). From these results, high voltage application of MLCCs can be expanded and the rated voltage can also be develop.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.4
• /
• pp.107-113
• /
• 2022

At present, it is possible to manufacture electrodes down to several micrometers (~ ㎛) using inkjet printing technology owing to the development of precision ejection heads. Inkjet printing technology is also used in the manufacturing of bio-sensors, electronic sensors, and flexible displays. To reduce the difference between the electrode design/simulation performance and actual printing pattern performance, it is necessary to analyze and optimize the processable area of the ink material, which is a fluid. In this study, process optimization was conducted to manufacture an IDE pattern and fabricate an impedance sensor. A total of 25 IDE patterns were produced, with five for each lamination process. Electrode line width and height changes were measured by stacking the designed IDE pattern with a nanoparticle-based conductive ink multilayer. Furthermore, the optimal process area for securing a performance close to the design result was analyzed through impedance and capacitance. It was observed that the increase in the height of stack layer 4 was the lowest at 4.106%, and the increase in capacitance was measured to be the highest at 44.08%. The proposed stacking process pattern, which is optimized in terms of uniformity, reproducibility, and performance, can be efficiently applied to bio-applications such as biomaterial sensing with an impedance sensor.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.394.2-394.2
• /
• 2014

We fabricated highly transparent and flexible Ti doped In2O3 (TIO)/Ag nanowire(NW)/TIO (TAT) multilayer electrodes by linear facing target sputtering (LFTS) and brush-painting for used as flexible for anode organic solar cells(FOSCs). The characteristics of TAT transparent anode as a function of number of brush-painting cycles was also investigated. At optimized conditions we achieved highly flexible TAT multilayer electrodes with a low sheet resistance of $9.01{\Omega}/square$ and a high diffusive transmittance more than 80% in visible region as well as superior mechanical stability. The effective embedment of the Ag NW network between top and bottom TIO films led to a metallic conductivity, high transparency. Based on FE-SEM HRTEM, and XRD analysis, we can find that the Ag NW network was effectively embedded between top and bottom TIO layers due to good flexibility of Ag NW, the TAT multilayer showed superior flexibility than single TIO layer. Successful operation of FOSCs with high power conversion efficiency of 3.01% indicates that TAT hybrid electrode is a promising alternative to conventional ITO electrode for high performance FOSCs.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.1
• /
• pp.37-43
• /
• 2022

In this study, we investigated the optical, electrical and exothermic characteristics of ITO/Ag/ITO multilayer structures prepared with various Ag thicknesses on quartz and PI substrates. The transparent conducting properties of the ITO/Ag/ITO multilayer films depended on the thickness of the mid-layer metal film. The ITO/Ag (14 nm)/ITO showed the highest Haccke's figure of merit (FOM) of approximately 19.3×10^-3 Ω^-1. In addition, the exothermic property depended on the substrate. For an applied voltage of 3.7 V, the ITO/Ag (14 nm)/ITO multilayers on quartz and PI substrates were heated up to 110℃ and 200℃, respectively. The bending tests demonstrated a comparable flexibility of the ITO/Ag/IT multilayer to other transparent electrodes, indicating the potential of ITO/Ag/ITO multilayer as a flexible transparent conducting heater.

• Korean Journal of Materials Research
• /
• v.30 no.6
• /
• pp.285-291
• /
• 2020

Recent advances in technology using ultra-thin noble metal film in oxide/metal/oxide structures have attracted attention because this material is a promising alternative to meet the needs of transparent conduction electrodes (TCE). AZO/Ag/AZO multilayer films are prepared by magnetron sputtering for Cu₂ZnSn(S,Se)₄ (CZTSSe) of kesterite solar cells. It is shown that the electrical and optical properties of the AZO/Ag/AZO multilayer films can be improved by the very low resistivity and surface plasmon effects due to the deposition of different thicknesses of Ag layer between oxide layers fixed at AZO 30 nm. The AZO/Ag/AZO multilayer films of Ag 15 nm show high mobility of 26.4 ㎠/Vs and low resistivity and sheet resistance of 3.58^⁎10^-5 Ωcm and 5.0 Ω/sq. Also, the AZO/Ag (15 nm)/AZO multilayer film shows relatively high transmittance of more than 65 % in the visible region. Through this, we fabricated CZTSSe thin film solar cells with 7.51 % efficiency by improving the short-circuit current density and fill factor to 27.7 mV/㎠ and 62 %, respectively.

• Journal of the Korean Chemical Society
• /
• v.63 no.1
• /
• pp.37-44
• /
• 2019

N,N'-bis(ethyldihydrogen phosphate)-1,4,5,8-naphthalene bis(dicarboximide) (EPNI) and N,N'-bis(ethyldihydrogen phosphate)-3,4,9,10-perylene bis(dicarboximide) (EPPI) and their zirconium bisphosphate multilayers (Zr-EPNI and Zr-EPPI), that had been briefly reported by us, were further investigated in terms of their electrochemical properties. EPNI in aqueous solution showed typical two reversible reductions at ITO electrode but the reductions were strongly dependent on solution pH while EPPI showed only an irreversible reduction. The single and mixed multilayers of Zr-EPNI and Zr-EPPI were well constructed on ITO electrode by the alternate adsorptions of zirconium ion and the bisimides. While Zr-EPNI multilayer on ITO electrode showed single broad reversible reduction with $E_{1/2}=-0.68V$, Zr-EPPI gave two separated reductions at $E_{1/2}=-0.54$ and -0.81 V vs SCE, quite differently from the solution properties. The average layer densities of the multilayers were estimated as $1.5{\times}10^{-10}$ and $2.3{\times}10^{-10}mol/cm^2$ for Zr-EPNI and Zr-EPPI, respectively. Both the monolayers of Zr-EPNI and Zr-EPPI could not completely block the electron transfer between $Fe(CN){_6}^{3-}$ in solution and ITO electrode but 3-5 layers of Zr-EPNI and Zr-EPPI could block it completely and mediated the one-way electron transfer at the potential shifted to their reduction potentials. When the monolayer of zirconium 1,10-decanediylbisphosphonate (Zr-DBP) was used as a sublayer of Zr-EPNI and Zr-EPPI layers, the mediated electron transfer became prominent without any direct electron transfer.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.680-683
• /
• 1997

In this paper, the multilayer actuator is investigated by using the finite element method. The material is taken to be piezoelectric. The capacitor and interdigital wlfloating type actuator are compared to the stress field distribution under the uniform electric field. As the length of the floating electrode in the interdigital wlfloating actuator changes, the stress field around the edge of electrode is studied.